A method for preparing porous lithium battery silicon carbon negative electrode by screw extruder

A technology of screw extrusion and lithium battery, which is applied to battery electrodes, negative electrodes, secondary batteries, etc., and can solve problems such as effective control of difficult porous structures

Active Publication Date: 2021-09-28
孙斌
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] Aiming at the problem that it is difficult to effectively control the porous structure in the preparation process of the existing porous silicon carbon negative electrode materials, the present invention proposes a method for preparing porous lithium battery silicon carbon negative electrodes with a screw extruder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing porous lithium battery silicon carbon negative electrode by screw extruder
  • A method for preparing porous lithium battery silicon carbon negative electrode by screw extruder
  • A method for preparing porous lithium battery silicon carbon negative electrode by screw extruder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of screw extruder prepares the preparation of silicon carbon negative electrode of porous lithium battery:

[0034] (1). Ultrasonic dispersion of 40 parts by weight of styrene, 50 parts by weight of methyl methacrylate and 40 parts by weight of nano silicon powder in a mixed solvent of 100 parts by weight of tetrahydrofuran and 100 parts by weight of cyclohexane is configured as a suspension, and added 10 parts by weight of n-butyllithium initiator, react under protection of argon, form PS-b-PMMA block polymer coating nano-silicon particle, with described PS-b-PMMA block polymer coating nano-silicon particle After filtering and drying, add deionized water, and slowly add 38%wt acetic acid solution dropwise under ultraviolet light irradiation to obtain porous PS membrane-coated nano-silicon particles;

[0035] (2). The inorganic filler sodium chloride was added into deionized water to form a saturated solution, and 200 parts by weight of the porous PS membrane-coa...

Embodiment 2

[0039] A kind of screw extruder prepares the preparation of silicon carbon negative electrode of porous lithium battery:

[0040] (1). Ultrasonic dispersion of 40 parts by weight of styrene, 50 parts by weight of methyl methacrylate and 50 parts by weight of nano silicon powder in a mixed solvent of 100 parts by weight of tetrahydrofuran and 100 parts by weight of cyclohexane is configured as a suspension, and added 10 parts by weight of n-butyllithium initiator, react under protection of argon, form PS-b-PMMA block polymer coating nano-silicon particle, with described PS-b-PMMA block polymer coating nano-silicon particle After filtering and drying, add deionized water, and slowly add 38%wt acetic acid solution dropwise under ultraviolet light irradiation to obtain porous PS membrane-coated nano-silicon particles;

[0041] (2). Add the water-soluble inorganic filler sodium chloride into deionized water to configure a saturated solution, and disperse 200 parts by weight of the ...

Embodiment 3

[0046] A kind of screw extruder prepares the preparation of silicon carbon negative electrode of porous lithium battery:

[0047] (1). Ultrasonic dispersion of 40 parts by weight of styrene, 50 parts by weight of methyl methacrylate and 40 parts by weight of nano silicon powder in a mixed solvent of 100 parts by weight of tetrahydrofuran and 100 parts by weight of cyclohexane is configured as a suspension, and added 10 parts by weight of n-butyllithium initiator, react under protection of argon, form PS-b-PMMA block polymer coating nano-silicon particle, with described PS-b-PMMA block polymer coating nano-silicon particle After filtering and drying, add deionized water, and slowly add 38%wt acetic acid solution dropwise under ultraviolet light irradiation to obtain porous PS membrane-coated nano-silicon particles;

[0048] (2). Add the water-soluble inorganic filler sodium chloride into deionized water to configure a saturated solution, and disperse 200 parts by weight of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of lithium battery negative electrode preparation, and in particular relates to a method for preparing a porous lithium battery silicon carbon negative electrode with a screw extruder. The method comprises: ultrasonically dispersing styrene, methyl methacrylate and nano-silicon powder in a mixed solvent of tetrahydrofuran and cyclohexane, adding an n-butyllithium initiator, and reacting under the protection of argon to form coated nano-silicon particles, After filtering and drying, add deionized water, and add acetic acid solution under ultraviolet light irradiation to obtain porous PS membrane-coated nano-silicon particles; add water-soluble inorganic fillers to deionized water to form a saturated solution, and coat porous PS membranes with nano-silicon particles Dispersed in a saturated solution, evaporated to remove water, crystallize the inorganic filler in the nanopores; carbonize the product obtained after evaporation. The carbonized product is mixed with carbon powder, binder and paraffin wax lubricant and then added to the screw extruder. After repeated extrusion, the extruded powder is soaked in deionized water and dried to obtain a silicon-carbon composite material with a porous structure. .

Description

technical field [0001] The invention belongs to the technical field of lithium battery negative electrode preparation, and in particular relates to a method for preparing a porous lithium battery silicon carbon negative electrode with a screw extruder. Background technique [0002] At present, the development of new energy is in full swing. In the field of mobile power, lithium-ion batteries have gradually replaced lead-acid batteries and nickel-metal hydride batteries, becoming the leader of the next generation of mobile power. However, lithium-ion batteries also have some unresolved "pain points", such as low capacity, long charge and discharge time, and poor cycle life. The optimization of negative electrode materials is one of the keys to solving these problems. At present, the anode materials of commercial lithium-ion batteries are mainly artificial graphite and natural graphite, but their theoretical specific capacity is relatively low, which is difficult to meet the m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/1395H01M4/04H01M4/38H01M4/62H01M10/0525B82Y40/00
CPCB82Y40/00H01M4/0411H01M4/1395H01M4/386H01M4/625H01M4/628H01M10/0525H01M2004/021H01M2004/027Y02E60/10
Inventor 陈庆廖健淞司文彬李钧
Owner 孙斌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com