Dry stone particles with simulation effect, rock plate and preparation method and application of rock plate

A technology of stone and dry granules, which is applied in the field of brick product coatings. It can solve the problems of high initial melting point and high temperature viscosity stone dry granules, insufficient three-dimensional effect, and no flash effect, etc., achieve high high temperature viscosity, low cost of raw materials, and reduce viscosity. Effect

Active Publication Date: 2021-01-15
FOSHAN TAOYING NEW MATERIAL CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When imitating this effect, rock slabs mainly use the following two methods: ① Adjust the gray level of the inkjet pattern on the penetrating part, and achieve the simulation effect in the way of visual illusion, but the three-dimensional effect of the "permeable part" in this way is not enough Strong; ② Add frit stone dry particles to the glaze surface of the slab. The three-dimensional effect of the slab obtained by this method is acceptable. The dry stone particles are either too transparent or too milky, and there is no flash effect and lack of layering.
[0003] Therefore, there is currently no stone dry granule on the market that can satisfy moderate transparency, clear layers, simulation effect and three-dimensional effect of real stone dry granules, and has a high initial melting point and a suitable high-temperature viscosity. problem to be solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dry stone particles with simulation effect, rock plate and preparation method and application of rock plate
  • Dry stone particles with simulation effect, rock plate and preparation method and application of rock plate
  • Dry stone particles with simulation effect, rock plate and preparation method and application of rock plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1 has the preparation of stone material dry granule and slate of simulation effect

[0031] The preparation steps of stone dry granules with simulation effect are as follows:

[0032] Take 50Kg of potassium feldspar, 10Kg of quartz, 6Kg of zinc oxide, 5Kg of calcite, 7Kg of dolomite, 12Kg of barium carbonate, 3Kg of boronite, 4Kg of cerium oxide and 3Kg of alumina. The obtained frit is pulverized by a jet mill to obtain granular dry stone granules with a particle size of 30-150 meshes, which is recorded as the finished product 1 of the embodiment of dry stone granules with simulation effect.

[0033] The steps to prepare the rock slabs are as follows: apply the finished product 1 of dry stone granules with simulation effect on the brick surface that has been glazed with a bell jar, and then fire at 1200°C for 55 minutes to obtain a rock slab. Example finished product 1.

Embodiment 2

[0034] Embodiment 2 has the preparation of stone material dry granule and slate of simulation effect

[0035] The preparation steps of stone dry granules with simulation effect are as follows:

[0036] Take 50Kg of potassium feldspar, 10Kg of quartz, 6Kg of zinc oxide, 4Kg of calcite, 6Kg of dolomite, 12Kg of barium carbonate, 3Kg of boronite, 5Kg of cerium oxide and 4Kg of alumina. The obtained frit is pulverized by a jet mill to obtain granular dry stone granules with a particle size of 30-150 meshes, which is recorded as the finished product 2 of the embodiment of dry stone granules with simulation effect.

[0037] The steps for preparing the slate are as follows: apply the finished product 2 of the stone dry granule example 2 with the simulation effect on the brick surface that has been glazed with a bell jar, and then fire it at 1200°C for 55 minutes to obtain a slate. Example finished product 2.

Embodiment 3

[0038] Embodiment 3 has the preparation of stone dry granule and slate with simulation effect

[0039] The preparation steps of stone dry granules with simulation effect are as follows:

[0040] Take 50Kg of potassium feldspar, 11Kg of quartz, 6Kg of zinc oxide, 6Kg of calcite, 7Kg of dolomite, 12Kg of barium carbonate, 3Kg of boronite, 3Kg of cerium oxide and 2Kg of aluminum oxide, mix well, and melt at 1450°C for 5.5 hours. The obtained frit was pulverized by a jet mill to obtain granular stone dry granules with a particle size of 30-150 meshes, which was recorded as Example 3 of dry stone granules with simulation effect.

[0041] The steps for preparing the slate are as follows: apply the finished product 3 of the stone dry granule example 3 with the simulation effect on the brick surface that has been glazed with a bell jar, and then fire it at 1200°C for 55 minutes to obtain a slate. Example finished product 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of brick product coatings, and discloses dry stone particles with a simulation effect, and a rock plate, and a preparation method and an application thereof, and the product ismainly prepared from a main flux, a high temperature raw material, a fluxing agent, a filler and cerium oxide. The main flux is potassium feldspar, the quartz is a filler and plays a role of a skeleton structure, and the addition of the cerium oxide not only enables the dry stone particles to have a colorful flashing effect, but also is helpful for reducing the high-temperature viscosity of the dry stone particles. In addition, the boehmite, the zinc oxide, the dolomite and the calcite are used as fluxing agents, so that the viscosity of the dry stone particles at high temperature is reduced, and the leveling effect is good; barium carbonate and aluminum oxide are used as high-temperature raw materials, so that the initial melting point of the stone dry particles is increased. The obtained dry stone particles can be used as one of preparation raw materials of the rock plate, are moderate in permeability and distinct in gradation, have the simulation effect and thethree-dimensional effect of real stone dry particles, have the performance requirements for a high initial melting point, proper high-temperature viscosity and the like, and are wide in application prospect.

Description

technical field [0001] The invention belongs to the technical field of coatings for brick products, and in particular relates to dry stone granules and rock slabs with simulation effects, a preparation method and application thereof. Background technique [0002] The currently popular rock slabs in the market are mainly imitation stone dry particles. Among them, stone dry granules have a very distinctive feature, that is, the effect of stone dry granules is difficult to imitate at present. Most of the real stone dry granules contain penetrating parts, which are mainly composed of quartz. The transparent effect and a little colorful flash highlight the layered and three-dimensional effect of the stone dry granules. When imitating this effect, rock slabs mainly use the following two methods: ① Adjust the gray level of the inkjet pattern on the penetrating part to achieve the simulation effect in the way of visual illusion, but the three-dimensional effect of the "permeable pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B32/00C04B41/50C04B111/54
CPCC04B32/005C04B41/5049C04B2111/542C04B2111/00482C04B14/045C04B14/26C04B14/303C04B14/36C04B14/30C04B14/28C04B14/06C04B41/5035C04B41/5024C04B41/5045C04B41/501C04B41/5006C04B41/5031C04B41/0072C04B41/4545
Inventor 全春辉司金凯
Owner FOSHAN TAOYING NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap