A kind of preparation method of ultrafine denier nylon fiber, ultralight fabric and ultralight coat

A technology of nylon fiber and ultra-fine denier, which is applied in the preparation of ultra-light jackets, ultra-light fabrics, and ultra-fine denier nylon fibers. It can solve the problems of low yield and achieve high crystallinity, increase yield, and high purity. Effect

Active Publication Date: 2022-05-27
XIAMEN ANTA SPORTS GOODS CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, none of the existing technologies can rationally make nylon fibers into fine or ultrafine deniers, and the fineness of the obtained fibers is generally at least greater than 1dtex; or after making nylon fibers into fine or ultrafine deniers, the yield is low. This produces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of ultrafine denier nylon fiber, ultralight fabric and ultralight coat
  • A kind of preparation method of ultrafine denier nylon fiber, ultralight fabric and ultralight coat
  • A kind of preparation method of ultrafine denier nylon fiber, ultralight fabric and ultralight coat

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of ultra-fine denier nylon fiber, comprising the following steps:

[0031] Step 1: Weigh the following components by weight: 99 parts of nylon 66 slices, TiO 2 0.35 part of matting masterbatch, 0.05 part of phosphite antioxidant, 0.05 part of fatty alcohol phosphate, 0.05 part of polyethylene glycol antistatic agent and 0.4 part of nylon linear chain extender BRUGGOLEN M1251, the nylon 66 chip model is CM3006, The relative molecular weight is 25000-30000, and the viscosity is 2.9;

[0032] Step 2: The raw material weighed in Step 1 is prepared by melt spinning to obtain nylon fibers with a monofilament fineness of 0.4 dtex. During the melt spinning process, the melting temperature is 290°C, and the number of holes in the spinneret is 12. , the aperture is 0.15mm, the shape of the spinneret hole is circular, the winding speed is 500 m / min, and the winding temperature is 19°C.

[0033] Correspondingly, the present embodiment also provides a method f...

Embodiment 2

[0037] A preparation method of ultra-fine denier nylon fiber, comprising the following steps:

[0038] Step 1: Weigh the following components by weight: 96 parts of nylon 66 slices, TiO 2 1.5 parts of matting masterbatch, 1 part of phosphite antioxidant, 0.5 part of fatty alcohol phosphate, 0.5 part of polyethylene glycol antistatic agent and 0.5 part of nylon linear chain extender BRUGGOLENM1251, the nylon 66 slice model is CM3006, relatively The molecular weight is 25000-30000, and the viscosity is 2.8;

[0039] Step 2: The raw materials weighed in Step 1 are prepared by melt spinning to obtain nylon fibers with a monofilament fineness of 0.3 dtex. During the melt spinning process, the melting temperature is 280° C., and the number of holes in the spinneret is 10. , the aperture is 0.1mm, the shape of the spinneret hole is cross-shaped, the winding speed is 300 m / min, and the winding temperature is 18 °C.

[0040] Correspondingly, the present invention also provides a prepar...

Embodiment 3

[0043] A preparation method of ultra-fine denier nylon fiber, comprising the following steps:

[0044] Step 1: Weigh the following components by weight: 97 parts of nylon 66 slices, TiO 2 2 parts of matting masterbatch, 0.7 part of phosphite antioxidant, 0.45 part of fatty alcohol phosphate, 0.35 part of polyethylene glycol antistatic agent and 0.35 part of nylon linear chain extender BRUGGOLEN M1251, the nylon 66 chip model is CM3006, The relative molecular weight is 25000-30000, and the viscosity is 2.9;

[0045] Step 2: The raw materials weighed in Step 1 are prepared by melt spinning to obtain nylon fibers with a monofilament fineness of 0.3 dtex. During the melt spinning process, the melting temperature is 285°C, and the number of holes in the spinneret is 16. , the aperture is 0.12mm, the shape of the spinneret is circular, the winding speed is 450 m / min, and the winding temperature is 19°C to obtain nylon fibers with a monofilament fineness of 0.3dtex.

[0046] Corres...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of ultrafine denier nylon fiber, comprising the following steps: 1) Weighing the following components by weight: 96-99 parts of nylon 66 slices, TiO 2 0.35-2 parts of matting masterbatch, 0.05-1 part of phosphite antioxidant, 0.05-0.5 part of fatty alcohol phosphate and 0.05-0.5 part of polyethylene glycol antistatic agent, the model of nylon 66 slice is CM3006, and the relative molecular weight is 25000 ‑30000, the viscosity is 2.8‑2.9; 2) the raw material weighed in step 1 is prepared through the melt spinning method to obtain a nylon fiber with a monofilament fineness of 0.3‑0.5dtex, wherein in the melt spinning process, the melting temperature is 260‑ 290°C, the number of holes in the spinneret is 5-30, the hole diameter is 0.1-0.2mm, the winding speed is 300-500 m / min, the winding temperature is 18-19°C; the yield rate is over 92%. The invention also provides a preparation method of an ultra-light fabric and an ultra-light coat. The preparation method of the superfine-denier nylon fiber of the present invention can prepare the superfine-denier nylon fiber, and can ensure that the finished product rate is above 92%.

Description

technical field [0001] The invention relates to the field of textiles, in particular to a preparation method of an ultra-fine denier nylon fiber, an ultra-light fabric and an ultra-light jacket. Background technique [0002] Nylon fiber fabric has the characteristics of sweat absorption, light weight, good toughness, good resilience, acid and alkali resistance, etc., and is one of the main raw materials of clothing materials. The thickness of nylon fiber can be characterized by monofilament fineness. Generally, chemical fibers with a monofilament fineness of about 1 dtex are called fine denier fibers, and chemical fibers with a single fiber fineness of about 0.5 dtex are called ultra-fine denier fibers. Fine denier nylon fibers can give the fibers a silky luster, smooth and soft feel, and are very popular. For this reason, fine denier or ultra-fine denier nylon fibers are very important. However, none of the existing technologies can reasonably make nylon fibers fine or ult...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01D5/08D01D5/253D01F1/09D01F1/10D01F6/90D03D13/00D03D15/283A41D3/00A41D27/20A41D27/28A41D31/04
CPCD01D5/08D01D5/253D03D15/00D03D13/008D01F6/90D01F1/09D01F1/10A41D3/00A41D27/28A41D27/20A41D31/04A41D2300/322
Inventor 向贤贤叶介茂刘涛曾国坪劳作恬赵尚振
Owner XIAMEN ANTA SPORTS GOODS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap