Crystal non-slip mat and preparation method thereof

A non-slip mat and crystal technology, applied in the field of yoga mats, can solve the problems of single surface pattern, expensive PU, poor wear resistance and scratch resistance, etc., and achieve high aesthetic requirements, easy sales and promotion, and good ornamental effects

Pending Publication Date: 2021-02-05
广东远华新材料股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional PVC yoga mat has a single surface pattern and poor wear and scratch resistance.
In order to improve the wear-resistant, scratch-resistant and anti-slip effects, a layer of PU is usually compounded on the surface of PVC, but PU is expensive, which increases the cost
In addition, the existing PVC yoga mat is made of opaque material, which is not beautiful enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crystal non-slip mat and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A crystal anti-slip mat, the crystal anti-slip mat comprises a foam layer and a crystal layer, the crystal layer is arranged on the surface of the foam layer, and the thickness of the crystal anti-slip mat is 6.5mm. The inside of the foam layer contains a base cloth layer, and the foam layer is a PVC foam material, which includes in parts by weight: polyvinyl chloride paste resin powder E67ST: 100 parts, dioctyl terephthalate 75 parts , 80 parts of filler, 13 parts of azodicarbonamide, 1.6 parts of potassium zinc heat stabilizer, 1.0 part of tackifier; the crystal layer includes by weight parts: 100 parts of polyvinyl chloride paste resin P70, p-phenylene 85 parts of dioctyl diformate, 2.5 parts of potassium zinc heat stabilizer, 16 parts of vinyl chloride copolymer resin.

[0037] The preparation method of above-mentioned crystal anti-skid mat specifically comprises the following steps:

[0038] Step S1. Preparation of foam layer slurry: Take the ingredients in the fo...

Embodiment 2

[0044] A crystal anti-slip mat, the crystal anti-slip mat comprises a foam layer and a crystal layer, the crystal layer is arranged on the surface of the foam layer, and the thickness of the crystal anti-slip mat is 6mm. The inside of the foam layer contains a base cloth layer, and the foam layer is a PVC foam material, which includes in parts by weight: polyvinyl chloride paste resin powder E67ST: 50 parts, dioctyl phthalate 60 parts , 50 parts of filler, 9 parts of azodicarbonamide, 1.2 parts of potassium-zinc heat stabilizer, 0.4 part of tackifier; the crystal layer includes by weight parts: 50 parts of polyvinyl chloride paste resin P70, o-phthalic 60 parts of dioctyl diformate, 1.5 parts of calcium zinc stabilizer, and 8 parts of vinyl chloride copolymer resin.

[0045] The preparation method of above-mentioned crystal anti-skid mat, described method is identical with embodiment 1, difference is:

[0046] (1) In step S1, the viscosity of the foam layer slurry is 15000mPa...

Embodiment 3

[0050] A crystal anti-slip mat, the crystal anti-slip mat comprises a foam layer and a crystal layer, the crystal layer is arranged on the surface of the foam layer, and the thickness of the crystal anti-slip mat is 8mm. The inside of the foam layer contains a base cloth layer, and the foam layer is a PVC foam material, which includes in parts by weight: polyvinyl chloride paste resin powder E67ST: 120 parts, 90 parts of chlorinated fatty acid methyl ester, filled 100 parts of agent, 15 parts of azodicarbonamide, 2.0 parts of potassium zinc heat stabilizer, 2.0 parts of tackifier; the crystal layer includes by weight: 120 parts of polyvinyl chloride paste resin P70, chlorinated fatty acid methyl 90 parts of ester, 3.0 parts of potassium zinc heat stabilizer, 18 parts of vinyl chloride copolymer resin.

[0051] The preparation method of above-mentioned crystal anti-skid mat, described method is identical with embodiment 1, difference is:

[0052] (4) In step S1, the viscosity ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a crystal non-slip mat and a preparation method thereof. The crystal non-slip mat comprises a foaming layer and a crystal layer, a base cloth layer is arranged in the foaming layer, the foaming layer and the crystal layer are compounded into a whole through a foaming process, and the crystal layer is prepared from the materials in pass by weight: 50-120 parts of polyvinyl chloride paste resin, 60-90 parts of a plasticizer, 1.5-3.0 parts of a heat stabilizer and 8-18 parts of vinyl chloride-vinyl acetate copolymer resin. The preparation method comprises the steps of preparation of foaming layer slurry, preparation of crystal layer slurry, slurry coating, foaming and cooling shaping. According to the crystal non-slip mat and the preparation method thereof, the crystalnon-slip mat is transparent in surface, good in ornamental value, convenient to sell and popularize and excellent in anti-slip and wear-resisting performance, provides good protection for yoga sporters, and meets the requirements of the public.

Description

technical field [0001] The invention relates to the technical field of yoga mats, in particular to a crystal anti-slip mat and a preparation method thereof. Background technique [0002] Yoga exercise is a fashionable exercise in today's society. Yoga mat is an essential equipment for yoga exercise, which can improve the protection for yoga exercisers. Existing yoga mats are usually common cloth, EVA foam mats, PVC yoga mats and the like. Among them, PVC yoga mats are used in the largest amount and have the highest cost performance. However, the traditional PVC yoga mat has a relatively single surface pattern and poor wear and scratch resistance. In order to improve the wear-resistant, scratch-resistant and anti-skid effects, a layer of PU is usually compounded on the surface of PVC, but PU is expensive, which increases the cost. In addition, the existing PVC yoga mat is made of opaque material, which is not attractive enough. Therefore urgently need a kind of wear-resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/18D06N3/06D06N3/00A63B6/00
CPCD06N3/183D06N3/065D06N3/0043D06N3/0088D06N3/0077A63B6/00
Inventor 陶玮夏冠明
Owner 广东远华新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com