Non-fired antique green brick based on construction waste tailings and its preparation method and application

A technology for construction waste and antique blue bricks, applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve problems such as environmental pollution, achieve broad market prospects, promote harmless and efficient use, and excellent water resistance Sexual and anti-aging effects

Active Publication Date: 2022-04-15
蒋品
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the embodiment of the present invention is to provide a non-fired antique green brick based on construction waste tailings, to solve the problem that most of the construction waste tailings are disposed of in landfills in the prior art proposed in the above background technology, which is easy to cause environmental damage. pollution problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-fired antique green brick based on construction waste tailings and its preparation method and application
  • Non-fired antique green brick based on construction waste tailings and its preparation method and application
  • Non-fired antique green brick based on construction waste tailings and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] Another purpose of the embodiments of the present invention is to provide a method for preparing non-fired antique green bricks based on construction waste tailings (that is, a method for making unfired antique green bricks using construction waste tailings). The preparation method of the non-fired antique blue brick based on construction waste tailings comprises the following steps:

[0039] Weigh the inorganic solvent (preferably deionized water), sodium alginate, phenolic resin, liquid silicon dioxide, etc. according to the proportion, heat, stir and mix them uniformly in the reaction kettle to prepare the curing agent;

[0040] Weigh water according to the proportion and add it to the curing agent to mix evenly to obtain a diluent;

[0041] Weigh the tailings of construction waste, cement and colorant according to the proportion and mix them evenly, and then mix them evenly with the diluent (by spraying) to obtain the mixture;

[0042] The mixed material is hydraul...

Embodiment 1

[0058] A kind of non-fired archaized blue brick based on construction waste tailings, the specific preparation method is as follows (refer to figure 1 shown):

[0059] 1) Preparation of curing agent (curing admixture): Inject 440kg of deionized water into a reaction kettle with a heating system, heat it to 70°C, add 10kg of sodium alginate, stir for 20min, and heat at the same time to make the temperature in the reaction kettle Raise to 80°C, keep warm for 1h; cool down to 40°C; add 250kg of sulfonated phenolic resin and stir for 1h until it is completely dissolved, then naturally cool to 20°C; add 300kg of liquid silica for full stirring; measure the density at 1.26g / mL, filter, obtain the curing agent of the present embodiment formula, for subsequent use;

[0060] 2) Stirring the mixture: Weigh 900kg of construction waste tailings, 90kg of cement, and 10kg of coloring agent and carry out uniform mixing for 2-3min to obtain a dry mixture; simultaneously take 0.3kg of the ab...

Embodiment 2

[0064] A kind of non-fired archaized blue brick based on construction waste tailings, the specific preparation method is as follows (refer to figure 1 shown):

[0065] 1) Preparation of curing agent (curing admixture): Inject 438kg of deionized water into a reaction kettle with a heating system, heat it to 70°C, add 12kg of sodium alginate, stir for 20min, and heat at the same time to make the temperature in the reaction kettle Raise to 80°C, keep warm for 1h; cool down to 40°C; add 250kg of sulfonated phenolic resin and stir for 1h until completely dissolved, then naturally cool to 20°C; add 300kg of liquid silica and stir thoroughly; measure the density at 1.27g / mL left and right, filter, obtain the solidifying agent of this embodiment formula, for subsequent use;

[0066] 2) Stirring the mixture: Weigh 900kg of construction waste tailings, 90kg of cement, and 10kg of coloring agent and carry out uniform mixing for 2-3min to obtain a dry mixture; simultaneously take 0.3kg ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of environmental protection building materials, and specifically discloses a non-burning antique green brick based on construction waste tailings and its preparation method and application. As well as water as raw materials, the unfired antique green bricks prepared by chemical modification have high strength, excellent water resistance and aging resistance, and the high-density hydraulic forming method greatly improves the density of building materials, which can Promote the harmless and efficient utilization of construction waste tailings. The preparation method provided by the invention is simple, and the prepared building materials have the advantages of low production cost, high block strength, good physical waterproof effect, long service life, etc. At the same time, it solves the problem that most of the tailings of construction waste are disposed of through landfill in the prior art, which is easy to cause pollution to the environment, and has a broad market prospect.

Description

technical field [0001] The invention relates to the field of environmentally friendly building materials, in particular to an unfired antique green brick based on construction waste tailings, a preparation method and application thereof. Background technique [0002] At present, my country produces at least 2-3 billion tons of construction waste every year, of which plastics, wood, metals, etc. produced in the early stage can be basically recycled, and the primary aggregate, secondary aggregate, and fine aggregate produced after the building is broken Conventional disposal methods can also be directly sold to obtain profits. The most difficult to deal with is construction waste tailings, such as engineering dregs and crushed tailings powder. Due to factors such as large soil content, complex components, and fine particles, domestic existing Some technologies are difficult to reuse as resources. [0003] For the tailings of construction waste, there is currently a lack of effe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B18/16C04B111/54
CPCC04B28/04C04B18/16C04B2201/50C04B2111/547C04B2201/20C04B24/302C04B24/38C04B22/06C04B2103/54Y02W30/91
Inventor 蒋品
Owner 蒋品
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap