Tin brass welding wire and preparation method thereof

A technology of tin brass welding wire and range, applied in welding equipment, welding medium, manufacturing tools, etc., can solve the problems of tin brass welding wire processing technology is immature, processing technology is not complete, can not meet production needs, etc., to achieve processing effect Good, complete processing technology, high tensile strength effect

Pending Publication Date: 2021-02-26
铜陵新鑫焊材有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the processing technology of tin brass welding wire on the market is still immature, the processing technology is not complete, the processing effect is poor, and it is far from meeting the production demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tin brass welding wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] A method for preparing tin-brass welding wire, the process steps comprising:

[0048] Step S1, melting: (1) using raw materials; main materials: electrolytic copper, zinc ingots, tin, auxiliary materials: slag cleaning agent, silicon;

[0049] (2) Feeding sequence: copper, silicon, zinc, tin;

[0050] (3) When the added material is melted and kept warm, take a sample test and adjust the composition according to the data of the test sheet;

[0051] (4) Raise the temperature after the ingredients are adjusted;

[0052] (5) Add an appropriate amount of slag cleaning agent after the temperature rise is complete, and then start to remove the ash and remove the slag. During the ash removal process, the copper ash spoon is required to stay at the furnace mouth for about 20 seconds when the ash is removed from the copper water, so as to ensure that the copper in the ash All the water flows into the furnace;

[0053] (6) Measure the temperature in the furnace after the ash re...

Embodiment 1

[0062] The raw materials are batched according to the ratio, and the batching sequence is: copper, silicon, zinc, tin, and the materials are added for melting. When keeping warm, sampling and testing are carried out, and the ingredients are adjusted according to the data of the test sheet. After the ingredients are adjusted, the temperature is raised. , the method of judging the temperature increase without ash and slag removal is to look at the direction of the pointer of the furnace ammeter. When the pointer reverses violently, the temperature has reached the state of temperature increase. In the process of ash removal, the copper ash spoon is required to stay at the furnace mouth for about 20 seconds when the ash is removed from the copper water, so as to ensure that all the copper water in the ash flows into the furnace. When the ash removal is complete Measure the temperature in the furnace. If the temperature is not enough, you need to raise the temperature again. The met...

Embodiment 2

[0064]The raw materials are batched according to the ratio, and the batching sequence is: copper, silicon, zinc, tin, and the materials are added for melting. When keeping warm, sampling and testing are carried out, and the ingredients are adjusted according to the data of the test sheet. After the ingredients are adjusted, the temperature is raised. , the method of judging the temperature increase without ash and slag removal is to look at the direction of the pointer of the furnace ammeter. When the pointer reverses violently, the temperature has reached the state of temperature increase. In the process of ash removal, the copper ash spoon is required to stay at the furnace mouth for about 20 seconds when the ash is removed from the copper water, so as to ensure that all the copper water in the ash flows into the furnace. When the ash removal is complete Measure the temperature in the furnace. If the temperature is not enough, you need to raise the temperature again. The meth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a tin brass welding wire. The tin brass welding wire is prepared from the following components in percentage by weight: 59%-61% of copper, 0.8%-1.0% of tin, 0.15%-0.35% of silicon and the balance of zinc. According to the tin brass welding wire and a preparation method thereof, the defects in the prior art are overcome, the machining process is very complete, the machining effect is good, the production requirement can be met conveniently, and the tensile strength is high and is improved by 20%-30% compared with a welding wire machined through a common method; and the tin brass welding wire is high in hardness, can bear large pressure, can be widely applied to brazing, copper, steel, copper-nickel alloy, gray cast iron, inlaid hard alloy cutters and the like, and canalso be used as a surfacing material for low-pressure valve seal and light-load N-grinding surfaces, the performance of welding wire products can be improved through a reasonable proportion of Sn andSi in the tin brass welding tire, the fluidity, strength and corrosion resistance of the welding wire are improved through Sn, Si controls evaporation of zinc, and air holes are eliminated.

Description

technical field [0001] The invention relates to a welding wire, especially a tin-brass welding wire and a preparation method thereof. Background technique [0002] The production of tin brass wire has a history of more than 50 years in our country, and its production process is actually the processing and production process of tin brass wire. [0003] At present, the processing technology of tin-brass welding wire on the market is still immature, the processing technology is not complete, the processing effect is poor, and it is far from meeting the production demand. [0004] Therefore, it is necessary to provide a tin brass welding wire and a preparation method thereof to solve the above technical problems. Contents of the invention [0005] Purpose of the invention: Aiming at the problems in the prior art, the present invention provides a tin-brass welding wire and its preparation method. The processing technology is very complete, the processing effect is good, and it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/02B23K35/30B23K35/40C22C1/02
CPCB23K35/302B23K35/40C22C1/02C22C9/02
Inventor 王陵周四清赵双刚赵刚徐安吾吕斌韩昌龙施永波王静
Owner 铜陵新鑫焊材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com