A kind of recycled asphalt concrete and its preparation method

A technology of recycled asphalt and concrete, applied in the field of recycled asphalt concrete, can solve the problems of poor aging resistance and durability of asphalt concrete pavement, poor adhesion, and unbearable potholes on asphalt concrete pavement.

Active Publication Date: 2021-08-20
宁波东兴沥青制品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Asphalt concrete has the advantage of reducing pavement cracking, but in the process of road paving, it is necessary to combine new asphalt concrete with old asphalt concrete. Due to the poor bonding between new and old asphalt concrete, the resistance of asphalt concrete pavement The aging and durability are poor, which leads to the phenomenon of potholes on the asphalt concrete pavement after not being used for a long time, which affects the continued use in the later period

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A recycled asphalt concrete, calculated in parts by weight, comprising the following components:

[0034] 60 parts of new asphalt, 40 parts of waste asphalt mixture, 15 parts of coarse aggregate, 10 parts of fine aggregate, 3 parts of regeneration agent, 2 parts of antioxidant and 1.5 parts of SBS modifier.

[0035] The coarse aggregate is steel slag powder with a particle size ranging from 3 to 10 mm; in the steel slag powder, the mass fraction of CaO is 50 to 70%, Al 2 o 3 The mass fraction is 4-8%.

[0036] The fine aggregate is natural sand with a particle size ranging from 0.5 to 3 mm; wherein, the natural sand includes sea sand and lake sand.

[0037] The antioxidant is antioxidant 1010.

[0038] The regeneration agent is calculated in parts by weight and consists of the following components: 12 parts of palm oil, 3 parts of cyclohexanedione, 6 parts of modified halloysite, 4 parts of coumarone resin and 4 parts of polyester resin.

[0039] The preparation pro...

Embodiment 2

[0054] A recycled asphalt concrete, calculated in parts by weight, comprising the following components:

[0055] 40 parts of new asphalt, 30 parts of waste asphalt mixture, 10 parts of coarse aggregate, 8 parts of fine aggregate, 2 parts of regeneration agent, 1 part of antioxidant and 1 part of SBS modifier.

[0056] The coarse aggregate is steel slag powder with a particle size ranging from 3 to 10 mm; in the steel slag powder, the mass fraction of CaO is 50 to 70%, Al 2 o 3 The mass fraction is 4-8%.

[0057] The fine aggregate is natural sand with a particle size ranging from 0.5 to 3 mm; wherein, the natural sand includes river sand and mountain sand.

[0058] The antioxidant is antioxidant 168.

[0059] The regeneration agent is calculated in parts by weight and consists of the following components: 10 parts of palm oil, 1 part of cyclohexanedione, 5 parts of modified halloysite, 3 parts of coumarone resin and 3 parts of polyester resin.

[0060] The preparation proc...

Embodiment 3

[0075] A recycled asphalt concrete, calculated in parts by weight, comprising the following components:

[0076] 70 parts of new asphalt, 50 parts of waste asphalt mixture, 20 parts of coarse aggregate, 12 parts of fine aggregate, 5 parts of regeneration agent, 3 parts of antioxidant and 2 parts of SBS modifier.

[0077] The coarse aggregate is steel slag powder with a particle size ranging from 3 to 10 mm; in the steel slag powder, the mass fraction of CaO is 50 to 70%, Al 2 o 3 The mass fraction is 4-8%.

[0078] The fine aggregate is natural sand with a particle size ranging from 0.5 to 3mm; wherein, the natural sand includes sea sand, lake sand, river sand and mountain sand.

[0079] The antioxidants are antioxidant 1010 and antioxidant 168.

[0080] The regeneration agent is calculated in parts by weight and consists of the following components: 15 parts of palm oil, 5 parts of cyclohexanedione, 8 parts of modified halloysite, 6 parts of coumarone resin and 5 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a recycled asphalt concrete and a preparation method thereof. The recycled asphalt concrete comprises the following components in parts by weight: 40-70 parts of new asphalt, 30-50 parts of waste and old asphalt mixture, 10-20 parts of coarse Aggregate, 8-12 parts of fine aggregate, 2-5 parts of regeneration agent, 1-3 parts of antioxidant and 1-2 parts of SBS modifier. The invention solves the problem that the aging resistance and durability of the existing asphalt concrete pavement are poor, which further leads to the phenomenon that the asphalt concrete pavement is full of potholes after a short period of use, which affects the continued use of the later stage. The recycled asphalt concrete prepared by the invention has excellent performance, can be closely bonded to the old asphalt concrete when splicing, meets the use requirements of high-grade road surfaces, and can provide important references for the development of asphalt concrete in my country.

Description

technical field [0001] The invention relates to the field of recycled asphalt concrete, in particular to a recycled asphalt concrete and a preparation method thereof. Background technique [0002] Asphalt concrete is obtained by mixing and compacting mineral mixture and asphalt binder. It is one of the main materials of modern road pavement structure. It is widely used in various road pavements, especially suitable for high-speed road pavement. Asphalt concrete pavement has good mechanical properties and road performance, smooth pavement without joints, low vibration and low noise, comfortable driving, high traffic safety, etc., and asphalt pavement can realize the regeneration of pavement materials, so it is widely used in highway construction Designers and builders of all ages. [0003] Asphalt concrete has the advantage of reducing pavement cracking, but in the process of road paving, it is necessary to combine new asphalt concrete with old asphalt concrete. Due to the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26C04B24/42C08F292/00C08F212/08C08F212/36C04B111/20
CPCC04B24/425C04B26/26C04B40/0039C04B2111/0075C04B2111/20C08F292/00C08F212/08C08F212/36C04B18/16C04B18/142C04B14/068C04B2103/608C04B2103/0068C04B24/08C04B24/008C04B24/283C04B24/2617
Inventor 王正韶夏静杰陈晓辉王利君
Owner 宁波东兴沥青制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com