Concrete waterproof anti-cracking agent and preparation method thereof

An anti-crack agent and concrete technology, which is applied in the field of building materials, can solve the problems such as the need to further improve the waterproof and impermeable performance and mechanical strength of concrete, poor synergy, and poor environmental protection performance, and achieve the effect of waterproof and anti-crack. Significantly improve the impermeability and waterproof effect, and the preparation method is simple and easy to implement.

Inactive Publication Date: 2021-03-16
杨井英
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the sodium β-sulfonate formaldehyde condensate is used therein, which makes the environmental protection performance not good; due to the poor synergy between the components, the amount of it is large, which affects the waterproof and anti-seepage performance and the mechanical strength of the concrete. The promotion effect needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete waterproof anti-cracking agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A concrete waterproof anti-cracking agent is characterized in that it is made of the following components in parts by weight: 3 parts of porous β-cyclodextrin crosslinked polymer nanofibers, 10 parts of bauxite powder, sulfonic acid 4 parts of base fiber material, 20 parts of alum stone, 8 parts of blast furnace slag, 2 parts of rosin-based hyperbranched polyester, 5 parts of sulfonate modified 2-aminoadenosine, 3 parts of nano boron fiber, surface hydrophilic Sexual pig hair fiber 2 parts.

[0028] The particle diameter of the bauxite powder is 1000 mesh; the particle diameter of the alunite is 900 mesh; the particle diameter of the blast furnace slag is 1000 mesh; the diameter of the nano boron fiber is 200nm, and the aspect ratio is 10 :1.

[0029] The preparation method of the sulfonate modified 2-aminoadenosine comprises the following steps: adding 2-aminoadenine and 3-chloro-2-hydroxypropanesulfonic acid into an organic solvent, stirring at 55°C React for 3 hour...

Embodiment 2

[0032] A concrete waterproof anti-cracking agent is characterized in that it is made of the following components in parts by weight: 4 parts of porous β-cyclodextrin crosslinked polymer nanofibers, 12 parts of bauxite powder, sulfonic acid-containing 5 parts of base fiber material, 22 parts of alum stone, 9 parts of blast furnace slag, 2.5 parts of rosin-based hyperbranched polyester, 6 parts of sulfonate modified 2-aminoadenosine, 3.5 parts of nano boron fiber, surface hydrophilic 3 parts of pig hair fiber.

[0033] The particle diameter of the bauxite powder is 1100 mesh; the particle diameter of the alunite is 1000 mesh; the particle diameter of the blast furnace slag is 1050 mesh; the diameter of the nano boron fiber is 300nm, and the aspect ratio is 12 :1.

[0034] The preparation method of the sulfonate modified 2-aminoadenosine comprises the following steps: adding 2-aminoadenine and 3-chloro-2-hydroxypropanesulfonic acid into an organic solvent, stirring at 60°C Afte...

Embodiment 3

[0038] A concrete waterproof anti-cracking agent is characterized in that it is made of the following components in parts by weight: 4.5 parts of porous β-cyclodextrin crosslinked polymer nanofibers, 13 parts of bauxite powder, sulfonic acid 5.5 parts of base fiber material, 25 parts of alum stone, 10 parts of blast furnace slag, 3 parts of rosin-based hyperbranched polyester, 7.5 parts of sulfonate modified 2-aminoadenosine, 4 parts of nano-boron fiber, surface hydrophilic Sexual pig hair fiber 3.5 parts.

[0039] The particle diameter of the bauxite powder is 1150 mesh; the particle diameter of the alunite is 1100 mesh; the particle diameter of the blast furnace slag is 1100 mesh; the diameter of the nano boron fiber is 350nm, and the aspect ratio is 13 :1.

[0040] The preparation method of the sulfonate modified 2-aminoadenosine comprises the following steps: adding 2-aminoadenine and 3-chloro-2-hydroxypropanesulfonic acid into an organic solvent, stirring at 67°C After ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a concrete waterproof anti-cracking agent which is characterized in that the concrete waterproof anti-cracking agent is prepared from the following components in parts by weight: 3-6 parts of porous beta-cyclodextrin crosslinked polymer nano-fibers, 10-15 parts of bauxite powder, 4-7 parts of a sulfonic acid group-containing fiber material, 20-30 parts of alunite, 8-12 parts of blast furnace slag, 2-4 parts of rosin-based hyperbranched polyester, 5-10 parts of sulfonate modified 2-amino adenine nucleoside, 3-5 parts of nano-boron fibers, and 2-5 parts of surface hydrophilic pig hair fibers. The invention also provides a preparation method of the concrete waterproof anti-cracking agent. The concrete waterproof anti-cracking agent disclosed by the invention is remarkable in waterproof anti-cracking effect, small in mixing amount, capable of effectively improving the comprehensive performance of concrete and good in environmental protection property.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a concrete waterproof and anti-cracking agent and a preparation method thereof. Background technique [0002] With the rapid development of the economy, my country's construction industry is also developing rapidly, and the use of concrete has also greatly increased. Concrete is referred to as "concrete" for short, which refers to the collective name of engineering composite materials that aggregate aggregates into a whole by cementitious materials. Concrete is one of the most important civil engineering materials in the contemporary era. It has the characteristics of abundant raw materials, low price and simple production process. At the same time, the hardened concrete has the characteristics of high compressive strength, good durability and wide range of strength grades. It is widely used in construction projects. [0003] Concrete is a hydraulic material. During ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/34C04B16/06C04B14/30C04B18/14C04B24/10C04B18/18C04B14/38C04B103/65
CPCC04B40/0039C04B2103/65C04B16/0675C04B14/303C04B18/142C04B24/34C04B24/10C04B18/18C04B14/38Y02W30/91
Inventor 杨井英
Owner 杨井英
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com