Preparation method of ultraviolet-curable nano aluminum phosphate and graphene oxide anticorrosive paint

A technology of aluminum phosphate and oxide stone, used in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of not too high pigment content, blocking ultraviolet light, affecting deep resin curing, etc., to enhance surface performance, improve The effect of anti-corrosion efficiency

Inactive Publication Date: 2021-03-26
HENAN UNIVERSITY OF TECHNOLOGY
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the content of pigments in UV-curable coatings should not be too high, otherwise it will block UV light and affect the curing of deeper resins

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Add 22g of phosphoric acid (85% purity) to the reaction vessel, then add 66g of distilled water, stir evenly and add 6g of aluminum hydroxide; heat up to 80°C, and continue to stir until a transparent viscous liquid is formed; stop heating, and add a concentration of 0.01 % graphene oxide aqueous solution 3000mL; after stirring evenly, adjust the pH value to 5 with ammonia water, then raise the temperature to 80°C, and keep the temperature constant for 3.5h; stop stirring, and cool down naturally to obtain a dispersion of nano-aluminum phosphate / graphene oxide composite pigment.

[0016] Add 100g of bis(7-oxabicyclo[4.1.0]3-heptylmethyl)adipate (CAS: 3130-19-6) to the dispersion, keep stirring until uniform, let stand to separate layers; remove water Layer, continue to add 1000mL distilled water to wash, repeat more than three times; then, vacuumize at 50°C to remove water to obtain color paste.

[0017] In another container, add 70g bis(7-oxabicyclo[4.1.0]3-heptylmethy...

Embodiment 2

[0019] Add 22g of phosphoric acid (85%) to the reaction vessel, then add 66g of distilled water, stir well and then add 5.7g of aluminum hydroxide; heat up to 90°C, keep stirring until a transparent viscous liquid is formed; stop heating, and add a concentration of 0.05% Graphene oxide aqueous solution 3300mL; after stirring evenly, adjust the pH value to 5 with ammonia water, then raise the temperature to 75°C, and keep the temperature constant for 4h; stop stirring, and cool down naturally to obtain a dispersion of nano-aluminum phosphate / graphene oxide composite pigment.

[0020] Add 100g of 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexyl carboxylate (CAS-2386-87-0) to the dispersion, keep stirring until uniform, let stand and separate; remove the water layer , continue to add 1000mL of distilled water to wash, repeat more than three times; then, vacuumize at 50°C to remove moisture to obtain color paste.

[0021] Add 150g 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexylcarboxyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of an ultraviolet-curable nano aluminum phosphate and graphene oxide anticorrosive paint. The ultraviolet-curable nano aluminum phosphate and graphene oxide anticorrosive paint is characterized by comprising a nano aluminum phosphate / graphene oxide composite pigment, epoxy resin, epoxy acrylate and a photoinitiator in a weight ratio of 1-20: 100: 1-30:1-10, the preparation method comprises the following steps: a, loading nano aluminum phosphate with graphene oxide; b, pre-dispersing the composite pigment into epoxy resin; and c, preparing the ultraviolet curable pain according to the formula.

Description

technical field [0001] The invention relates to an ultraviolet curing anti-corrosion coating, in particular to an ultraviolet curing anti-corrosion coating using graphene oxide loaded with aluminum phosphate nanoparticles as an anti-corrosion composite pigment and a preparation method thereof. [0002] technical background [0003] Metal corrosion is the process in which simple metals are oxidized into various metal oxides with different valence states. The loss caused by metal corrosion is very serious, and protection and anti-corrosion treatment must be carried out. Among the various anti-corrosion methods, coating a layer of anti-corrosion paint on the metal surface is a relatively common and effective protection method. Anti-corrosion coatings usually add anti-corrosion pigments to organic resins, and form a protective film on the metal surface to prevent corrosive media from contacting the metal surface to achieve anti-corrosion effects. However, traditional anti-corro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D163/10C09D5/08C09D7/62
CPCC08K2003/327C08K2201/011C08L2205/025C08L2205/035C09D5/084C09D163/00C09D7/62C08L63/00C08L63/10C08K9/12C08K3/32C08K3/042
Inventor 宋伟强冯雨朱青松刘箫华孙东泽
Owner HENAN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap