Buffer composite packaging paper and preparation method thereof

A composite packaging and high molecular polymer technology, applied in the field of cushioning composite packaging paper and its preparation, can solve the problems of lack of moisture-proof and waterproof, poor cushioning and shock-absorbing effect of packaging paper, etc., achieve better waterproof effect, ensure cushioning reduction Shock effect, a wide range of effects

Inactive Publication Date: 2021-04-09
马鞍山高思贸易有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cushioning composite wrapping paper and its preparation method in the above-mentioned patents have the following disadvantages: the cushioning and shock absorption effect of the wrapping paper is not good when used, and it does not have the function of moisture-proof and waterproof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Buffer composite packaging paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] According to 25 parts of tapioca starch, 15 parts of styrene propylene, 13 parts of crotonate, 5 parts of paraffin, 2 parts of sodium dodecylbenzenesulfonate, and the parts by weight of 1 part of silicon dioxide are prepared by weighing and preparing the moisture-proof agent for subsequent use;

[0024] The calcium carbonate and the titanate coupling agent were fully mixed and reacted for 6 hours according to the weight ratio of 3:1 to prepare a modified foaming agent for use;

[0025] Weigh the wrapping paper raw material according to the following parts by weight: 6 parts by weight of brucite fiber, 3 parts by weight of modified foaming agent, 60 parts by weight of talcum powder, 10 parts by weight of high molecular polymer, 5 parts by weight of Dispersant, the moistureproof agent of 10 parts by weight;

[0026] Soak the brucite fiber in the modified foaming liquid for 24 hours, and the soaking temperature is 50°C, then filter and dry to obtain the fibrous foaming age...

Embodiment 2

[0028] According to 27 parts of tapioca starch, 17 parts of styrene propylene, 15 parts of crotonate, 7 parts of paraffin, 4 parts of sodium dodecylbenzene sulfonate, and the parts by weight of 3 parts of silicon dioxide are prepared by weighing and preparing the moisture-proof agent for subsequent use;

[0029] Calcium carbonate and titanate coupling agent were fully mixed and reacted for 6 hours according to the weight ratio of 3:1.5 to prepare a modified foaming agent for use;

[0030] Weigh the wrapping paper raw material according to the following parts by weight: 12 parts by weight of brucite fiber, 6 parts by weight of modified foaming agent, 75 parts by weight of talcum powder, 12 parts by weight of high molecular polymer, 7 parts by weight of Dispersant, the moistureproof agent of 15 parts by weight;

[0031] Soak the brucite fiber in the modified foaming liquid for 24 hours, and the soaking temperature is 55°C, then filter and dry to obtain the fibrous foaming agent;...

Embodiment 3

[0033] According to 30 parts of tapioca starch, 17 parts of styrene propylene, 15 parts of crotonate, 6 parts of paraffin, 3 parts of sodium dodecylbenzenesulfonate, and 3 parts of silicon dioxide, the moistureproof agent is prepared by weighing and preparing for subsequent use;

[0034] The calcium carbonate and the titanate coupling agent were fully mixed and reacted for 6 hours according to the weight ratio of 3:2 to prepare a modified foaming agent for use;

[0035] Weigh the wrapping paper raw material according to the following parts by weight: 18 parts by weight of brucite fiber, 9 parts by weight of modified foaming agent, 90 parts by weight of talcum powder, 15 parts by weight of high molecular polymer, 10 parts by weight of Dispersant, the moistureproof agent of 20 parts by weight;

[0036] Soak the brucite fiber in the modified foaming solution for 24 hours, and the soaking temperature is 60°C, then filter and dry to obtain a fibrous foaming agent; mix the fibrous f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses buffer composite packaging paper and a preparation method thereof. The buffer composite packaging paper is prepared from, by weight, 6-18 parts of mineral fiber, 3-9 parts of a modified foaming agent, 60-90 parts of talcum powder, 10-15 parts of a high molecular polymer, 5-10 parts of a dispersing agent and 10-20 parts of a moisture-proof agent.. The modified foaming agent coats the mineral short fibers, the modified foaming agent prepared from carbonate modified by the titanate coupling agent has a better foaming effect in use, initiated bubbles are smaller and denser, and the buffering and damping effects of the packaging paper are guaranteed.

Description

technical field [0001] The invention relates to the technical field of wrapping paper, in particular to a cushioning composite wrapping paper and a preparation method thereof. Background technique [0002] With the extensive application of paper in packaging and other fields, the demand is increasing. In particular, the application of white cardboard in the packaging field includes a large number of white cardboard applications in food packaging such as medicines, health care products, cosmetics, electronic products, handbags, and clothing boxes, resulting in a sharp increase in demand for white cardboard. At present, the rapid development of e-commerce and logistics has further promoted the surge in demand for packaging paper products such as cartons and cartons. [0003] After retrieval, the Chinese Patent Publication No. CN105482222B discloses a cushioning composite wrapping paper and a preparation method thereof, in which short fibers carry a foaming agent so that the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H13/46D21H17/68D21H17/20D21H17/28D21H17/19D21H17/09D21H17/69D21H27/10
CPCD21H13/46D21H17/68D21H17/20D21H17/28D21H17/19D21H17/09D21H17/69D21H27/10
Inventor 王玉芹
Owner 马鞍山高思贸易有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com