Formula of brass colorful ceramic plate and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of colorful ceramic plates and brass, applied in the field of clay plate production, can solve problems such as difficult control in actual production
Inactive Publication Date: 2021-04-20
JIANGSU CN ECO MATERIALS CO LTD
View PDF9 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In addition, the Chinese patent with the publication number of 107902904 A introduces a preparation method of a kiln-transformed crystal golden flower glaze. The main body of the glaze presents a milky yellow tone, and the crystal flower is a golden microcrystal. The firing of the glaze requires a reducing atmosphere, and the actual production Not easy to control, suitable for small batch production
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] Embodiment 1: A kind of formula of brass-colored dazzling pottery plate, comprises bottom glaze and surface glaze, and bottom glaze comprises the raw material of following mass fraction: 71% feldspar, 4% quartz, 7.5% titanium dioxide, 13% Lithium carbonate, 2.5% ferric oxide, 2% nickel carbonate; the surface glaze includes the following raw materials in mass fractions: 71% feldspar, 4% quartz, 7.5% titanium dioxide, 13% lithium carbonate, 2% ferric oxide, 2.5% calcined zinc oxide.
Embodiment 2
[0027] Embodiment 2: A kind of formula of brass-colored dazzling pottery plate, comprises bottom glaze and surface glaze, and bottom glaze comprises the raw material of following mass fraction: 72% feldspar, 6% quartz, 7% titanium dioxide, 11% Lithium carbonate, 2.5% ferric oxide, 1.5% nickel carbonate; the surface glaze includes the following raw materials in mass fractions: 72% feldspar, 6% quartz, 7% titanium dioxide, 11% lithium carbonate, 1.5% ferric oxide, 2.5% calcined zinc oxide.
Embodiment 3
[0028] Embodiment 3: A kind of formula of brassy colorful pottery plate, comprises bottom glaze and surface glaze, and bottom glaze comprises the raw material of following mass fraction: 73% feldspar, 5% quartz, 7% titanium dioxide, 12% Lithium carbonate, 2% ferric oxide, 1% nickel carbonate; the surface glaze includes the following raw materials in mass fractions: 73% feldspar, 5% quartz, 7% titanium dioxide, 12% lithium carbonate, 1% ferric oxide, 2% calcined zinc oxide.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a formula of a brass colorful ceramic plate, the brass colorful ceramic plate comprises a ground coat and a surface coat, the ground coat comprises the following raw materials by mass fraction: 71-73% of feldspar, 4-6% of quartz, 7-9% of titanium dioxide, 11-13% of lithium carbonate, 2-4% of ferroferric oxide, and 1-2% of nickel carbonate; the surface coat is prepared from the following raw materials in percentage by mass: 71-73 percent of feldspar, 4-6 percent of quartz, 7-9 percent of titanium dioxide, 11-13 percent of lithium carbonate, 1-2 percent of ferroferric oxide and 2-4 percent of calcined zinc oxide. The invention further provides a preparation method of the brass colorful ceramic plate. According to the invention, a Li2O-Al2O3-SiO2 formula system is adopted, titanium dioxide is introduced, different metal oxides are respectively added through the ground coat, different planar effects can be obtained, and the pottery clay plate prepared from the glaze has colorful glaze color effects.
Description
technical field [0001] The invention relates to the field of making pottery clay plates, in particular to a formula and a preparation method of a brassy colorful pottery plate. Background technique [0002] Clay board is a kind of exterior wall building decoration material that uses clay raw materials to be wet-extruded and then fired at high temperature. Its internal hollow structure is also equipped with installation slots. It has the advantages of easy installation, high safety, sound insulation and noise reduction, and environmental protection. And many other advantages, in recent years, it has been adopted by more and more building facade designs. The surface shape of ordinary clay board material is natural surface, which is the color of clay after firing. As people become more and more personalized and differentiated Constantly exploring and pursuing, in recent years, glazed clay panels have become more and more favored by domestic and foreign architectural designers. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more