Nickel electroplating process of electrode

An electrode and nickel-plating technology, applied in metal material coating process, liquid chemical plating, coating and other directions, can solve the problems of affecting the service life and safety of IGBT, fatal danger of automobile safety, and exposed side of electrodes, etc. The effect of electroplating surface quality, convenient plating adhesion, and improving roughness

Active Publication Date: 2021-04-20
ZHEJIANG HUAJING RECTIFIER
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional domestic electroplating method is to nickel-plate all the accessories, that is, to punch out the electrode pieces on the plate first, and then immerse all the electrode pieces in the electroplating solution for electroplating, so that all parts of the electrode pieces are plated with a nickel layer, which will cause The electrodes are weakly welded at the solder joints, or even fall off, which poses a fatal danger to the safety of the car
as attached figure 1 As shown, similar foreign products adopt electroplated plate punching process, which is to pre-plate nickel layer on both sides of the plate, and then punch out the electrode sheet with nickel on both sides. The major defect of this electrode is that the electrode side is exposed. , it is very easy to cause oxidation and rust, which affects the service life and safety of IGBT

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel electroplating process of electrode
  • Nickel electroplating process of electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The present invention will be further described below:

[0031] The electroplating nickel plating process of a kind of electrode in the present embodiment comprises the following specific steps:

[0032] (1) Carry out the following pretreatment to the electrode;

[0033] Degreasing and derusting: Put the polished electrode into the drum, which contains 1 / 2 volume of degreasing and derusting solution, which contains: Accelerator 2.5-3.5g / L, diffusing agent 1.5-2.5g / L, penetrating agent 2-3g / L and 20wt%-50wt% nitric acid. The reasonable proportion of accelerator, diffusing agent and penetrating agent can speed up the dissolution of oil stains on the electrode surface. Nitric acid can effectively remove rust stains and oxides on the electrode surface. Clean under rotation for 30-60 minutes to achieve the purpose of degreasing and rust removal, and improve the smoothness of the electrode surface;

[0034] Ultrasonic cleaning: The electrode after degreasing and rust remo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a nickel electroplating process of an electrode. The nickel electroplating process of the electrode comprises the following specific steps of (1) pre-treating the electrode in sequence; (2) coating a layer of anti-plating protective coating on the position, needing to be welded, of the electrode, and performing protection before plating; (3) hanging the electrode on a hanger made of a material with good conductivity, carrying out preheating, immersing the electrode in the electroplating liquid of a plating tank, connecting a cathode, placing anodes on two sides at a proper distance, and carrying out electrifying to deposit nickel ions on the surface of the electrode; (4) after nickel plating, removing the anti-plating protective coating at the position needing to be welded, and exposing the surface which is not plated with nickel; and (5) carrying out post-treatment on the electrode of which the protection is removed. The welding position of the electrode is protected before plating, nickel plating is conducted through a rack plating technology, protection is removed after plating, the bare copper surface is exposed so that welding can be firm, nickel plating is conducted on the surfaces of other parts so that rust prevention and electric conduction quality of the electrode can be guaranteed, and the selective local electroplating technology is an international advanced technology.

Description

technical field [0001] The invention relates to the technical field of electroplating, in particular to an electrode electroplating nickel plating process. Background technique [0002] At present, the electroplating process of power electrodes (hereinafter referred to as electrodes or electrode sheets) of IGBT power semiconductor accessories such as new energy vehicles directly affects the firmness of electrode welding. The traditional domestic electroplating method is to nickel-plate all the accessories, that is, to punch out the electrode pieces on the plate first, and then immerse all the electrode pieces in the electroplating solution for electroplating, so that all parts of the electrode pieces are plated with a nickel layer, which will cause The electrodes are weakly welded at the solder joints, or even fall off, which poses a fatal danger to the safety of the car. as attached figure 1 As shown, similar foreign products adopt electroplated plate punching process, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D5/02C25D5/34C25D5/48C25D3/12C23G1/02C23C18/42C09D175/04C09D167/08C09D5/25C09D7/63
Inventor 刘胜弟
Owner ZHEJIANG HUAJING RECTIFIER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products