Preparation method of DMF-free environment-friendly microfiber leather
An environmental protection and airflow control technology, applied in fiber treatment, improved handle fiber, textile material treatment, etc., can solve the problems of human body damage, harm to human health, easy to exceed the standard content, etc., to improve production efficiency and shorten immersion time , the effect of simple operation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0026] A preparation method of zero DMF environment-friendly ultra-fiber bass, comprising the following steps:
[0027] Step 1, slurry rolling: Pour the stirred slurry evenly on the base cloth, and then pass through two squeeze rollers to make the slurry on the base cloth penetrate into the base cloth, and then pass through the oven, at 100-140°C down drying;
[0028] Step 2, base fabric opening: soak the base fabric prepared in step 1 in a trough containing fiber opening lye for 6-8 minutes, control the liquid content of the base fabric at 80-90%, and send it into the softener. Control the airflow to slap and open the fibers of the base cloth, the wind force is controlled at 45-50Pa / m, the slapping time is controlled at 20-30min, and the airflow temperature is controlled at 30-80°C. Among them, the airflow slapping control is as follows:
[0029] In the first stage, the air temperature is raised from room temperature to 30°C, and the wind beats for 10-15 minutes;
[0030] I...
Embodiment 1
[0040] A preparation method of zero DMF environment-friendly ultra-fiber bass, comprising the following steps:
[0041] Step 1, slurry rolling: Pour the stirred slurry evenly on the base fabric, and then pass through two squeeze rollers to make the slurry on the base fabric penetrate into the base fabric, and then pass through an oven and dry at 100°C Dry;
[0042] Step 2, base fabric opening: Soak the base fabric prepared in step 1 in a trough containing fiber opening lye for 6 minutes, control the liquid content of the base fabric at 90%, send it into the softener, and control the airflow to the base fabric. The cloth is slapped to open the fiber, the wind force is controlled at 45Pa / m, the slapping time is controlled at 30min, and the airflow temperature is controlled at 30-80°C. Among them, the airflow slapping control is as follows:
[0043] In the first stage, the temperature of the airflow is raised from room temperature to 30°C, and the wind beats for 15 minutes;
[...
Embodiment 2
[0054] A preparation method of zero DMF environment-friendly ultra-fiber bass, comprising the following steps:
[0055] Step 1, slurry rolling: Pour the stirred slurry evenly on the base fabric, and then pass through two squeeze rollers to make the slurry on the base fabric penetrate into the base fabric, and then pass through an oven and dry at 140°C Dry;
[0056] Step 2, base fabric opening: Soak the base fabric prepared in step 1 in the trough containing fiber opening lye for 8 minutes, control the liquid content of the base fabric at 80%, send it into the softener, and control the airflow to the base fabric. The cloth is slapped to open the fiber, the wind force is controlled at 50Pa / m, the slapping time is controlled at 20min, and the air temperature is controlled at 30-80°C. Among them, the air slapping control is as follows:
[0057] In the first stage, the temperature of the airflow is raised from room temperature to 30°C, and the wind beats for 10 minutes;
[0058] ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com