Preparation method of degradable amino molding plastic
An amino molding compound, a disposable technology, applied in the field of degradable amino molding compound and its preparation, can solve the problems of large number of workers in the production line, difficulty in controlling quality stability, and large dust in the operating environment
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] The injection molding grade plant fiber reinforced amino molding compound (sample 1) was prepared according to the following formula composition and process. The formula is:
[0014] Table 1 Formula composition of sample 1
[0015] name Dosage (number of servings) formaldehyde solution 28 urea 15 Hardener 2.0 Emulsifier, release agent, pigment 2.0 filler 60
[0016] Preparation:
[0017] (1) Put formaldehyde, urea and auxiliary materials into the vertical polymerization kettle in sequence according to the proportion of the above formula, control the temperature at 50°C to 60°C, and mix and stir the reaction time for 100 minutes to prepare the original slurry of urea-formaldehyde resin.
[0018] (2) Pour the resin stock solution into another mixing and drying reactor through the pipeline, set the stirring speed to 80rpm, add fillers, curing agents, mold release agents, emulsifiers, etc. in sequence according to the ratio in ...
Embodiment 2
[0021] The injection molding grade plant fiber reinforced amino molding compound (sample 2) was prepared according to the following formula composition and process. The formula is:
[0022] Table 2 Formula composition of sample 2
[0023] name Dosage (number of servings) formaldehyde 34 urea 12 Hardener 1.5 Emulsifier, release agent, pigment 1.8 filler 78
[0024] Preparation:
[0025] (1) The preparation method of urea-formaldehyde resin stock solution is the same as in Example 1.
[0026] (2) Pour the resin stock solution into another mixing and drying reactor through the pipeline, set the stirring speed at 80rpm, add filler, curing agent, mold release agent, emulsifier, etc. in sequence according to the ratio in the formula, and mix and stir evenly for 9 minutes; Raise the temperature, control the temperature at 60°C, increase the speed to 120rpm, and last for about 65 minutes; turn on the vacuum pump, continue to heat up, con...
Embodiment 3
[0029] The injection molding grade plant fiber reinforced amino molding compound (sample 3) was prepared according to the following formula composition and process. The formula is:
[0030] Table 3 Formula composition of sample 3
[0031] name Dosage (number of servings) formaldehyde 35 urea 10 Hardener 1.6 Emulsifier, release agent, pigment 1.8 filler 78
[0032] Preparation:
[0033] (1) The preparation method of urea-formaldehyde resin stock solution is the same as in Example 1.
[0034] (2) Pour the resin stock solution into another mixing and drying reactor through the pipeline, set the stirring speed at 80rpm, add filler, curing agent, mold release agent, emulsifier, etc. in sequence according to the ratio in the formula, and mix and stir evenly for 9 minutes; Raise the temperature, control the temperature at 60°C, increase the speed to 95pm, and continue for about 70 minutes; turn on the vacuum pump, continue to heat up, c...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com