Thick and large aluminum alloy frame body type casting and casting method thereof

An aluminum alloy and casting technology, applied in the field of aluminum alloy casting, can solve the problems that the mechanical properties are difficult to meet the requirements of navigation marks, the ultrasonic flaw detection is unqualified, and the quality of castings is unstable, so as to improve the filling stability, reduce porosity defects, and optimize heat treatment. The effect of craftsmanship

Active Publication Date: 2021-06-11
NORTHWESTERN POLYTECHNICAL UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1) The cooling rate of the entire thick and large part is not enough, resulting in coarse grains, and the mechanical properties are difficult to meet the requirements of the navigation mark
[0005] 2) The alloy liquid finally solidifies at the suspension ring located at the water inlet, and there are hot spots, the mechanical properties are the worst, and there are potential safety hazards
[0006] 3) The quality of castings is unstable, sometimes the ultrasonic flaw detection is unqualified, and there are often air hole defects on the upper bottom surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thick and large aluminum alloy frame body type casting and casting method thereof
  • Thick and large aluminum alloy frame body type casting and casting method thereof
  • Thick and large aluminum alloy frame body type casting and casting method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] see figure 1 , is a structural schematic diagram of a thick aluminum alloy frame casting provided by an embodiment of the present invention, the casting includes: a frame body 10, two gate locations 12, a boss 13 and two lifting rings 14.

[0045] One end of the frame body 10 has a thick part 11; two gate parts 12 are respectively arranged on both sides of the thick part 11; the boss 13 is arranged on the upper side of the thick part 11; two lifting rings 14 are arranged in parallel on the boss 13 on one end.

[0046] Wherein, the side of the boss 13 away from the suspension ring 14 is provided with a first placement area 101, the two sides of the boss 13 are provided with a second placement area 102, and the side of the thick part 12 close to one of the gate parts 12 is provided with a second placement area. Three placement areas 103, a fourth placement area 104 is arranged between the 2 suspension rings 14, a fifth placement area 105 is provided on the side of the th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of aluminum alloy casting, in particular to a thick and large aluminum alloy frame body type casting and a casting method thereof. The method comprises the following steps that S1, a casting sand mold is manufactured, and shot blasting cleaning and drying are conducted on a chilling block, wherein sprues are formed in the two sides of the sand mold; S2, the dried chilling block is placed in the sand mold, a sand mold mold is obtained, and drawing is conducted after the sand mold mold is dried and hardened, wherein the thickness of the lower molded surface of the chilling block is greater than that of the upper molded surface of the chilling block ; S3, the sand mold is subjected to box closing pouring, and a casting crude product is obtained; S4, the casting crude product is subjected to heat preservation for 14 h at the temperature of 543+ / -2 DEG C, water quenching is conducted at the room temperature, the temperature is kept at 155+ / -2 DEG C for 5.5 hours, aging treatment is carried out, and cooling is conducted in the air till the room temperature is reached so as to obtain the product. According to the casting method, the ductility of a thick and large part can be greatly improved by modifying a mold of the thick and large part and combining with an optimized heat treatment process, so that the overall performance of the thick and large part completely meets the aviation industrial standard, and the qualification rate of products is greatly improved.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy casting, in particular to a thick aluminum alloy frame casting and a casting method thereof. Background technique [0002] Cast aluminum alloy has the advantages of high strength, low density, low hot cracking tendency, good weldability, corrosion resistance and low production cost, making it an irreplaceable important material in the fields of aviation, aerospace, navigation, automobile and other industries. The frame casting made of ZL114A alloy is an important part used in aerospace, but due to the complex structure and uneven wall thickness of the casting, the mechanical properties of some parts are low. Among them, the part connected with other workpieces is in the shape of a plate with a thickness of about 51mm. Because the grain structure of this part is coarser than other parts, the mechanical properties are low, especially the elongation is particularly low, and it is difficult to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22C9/02B22C9/22B22C9/08B22D15/00C22F1/04C21D1/18
CPCB22C9/02B22C9/22B22C9/082B22D15/00C22F1/002C22F1/04C21D1/18
Inventor 卢艳丽王一帆眭怀明吴晓鸣兰起洪
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products