Novel method for combining blue-and-white mud material and Nixing pottery

A technology of blue and white materials and Nixing pottery, applied in the field of Nixing pottery, can solve the problems of deformation and cracking of Nixing pottery, different firing temperatures, and increased production costs, and achieve high-temperature cracking prevention, strong flammability, and less powder ash Effect

Inactive Publication Date: 2021-06-11
QINZHOU CITY HUAXIA TAIJIQUAN NINGXING POTTERY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of novel blue-and-white material and Nixing pottery combination method, to solve the Nixing pottery pattern of the prior art on the market that the above-mentioned background technology proposes and can't fulfill people's demand, need to Nixing pottery Blue and white materials are used to describe the decorations, but the firing temperature of Nixing pottery is different from that of blue and white materials. If you want the blue and white materials to be completely consolidated on the glaze, there will be problems of deformation and cracking of Nixing pottery. Caused unnecessary losses and raised production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The present invention provides a technical solution: a novel method for combining blue and white materials with Nixing pottery. The raw materials include the following components: east mud, west mud, quartz, kaolin, hematite, water and blue and white materials, including the following steps in turn:

[0027] (1) Mud weathering and dissolution treatment: place the east mud and west mud in an open area, and after 4 months of wind, sun and rain until the mud is broken, it will be collected and stored after dissolving and oxidized, and wait for future use. The ratio of Xini is 45 parts of Dongni and 55 parts of Xini.

[0028] (2) Mud crushing treatment: put the weathered material in step (1) into a ball mill for grinding, collect and store it after grinding, and wait for standby. The model of the ball mill is MQ750×1800, and the ball mill is made of pebbles. The control is 40r / min, and the ball milling time is controlled at 8h.

[0029] (3) Grinding mud material sieving tr...

Embodiment 2

[0040] The present invention provides a technical solution: a novel method for combining blue and white materials with Nixing pottery. The raw materials include the following components: east mud, west mud, quartz, kaolin, hematite, water and blue and white materials, including the following steps in turn:

[0041] (1) Mud material weathering and dissolution treatment: place the east mud and west mud in an open area after being blown by wind, sun and rain for 5 months until the mud is broken up, collected and stored after dissolving and oxidizing, and waiting for backup. The ratio of Xini is 55 parts of Dongni and 45 parts of Xini.

[0042] (2) Mud crushing treatment: put the weathered material in step (1) into a ball mill for grinding, collect and store it after grinding, and wait for standby. The model of the ball mill is MQ750×1800, and the ball mill is made of pebbles. The control is 45r / min, and the ball milling time is controlled at 7h.

[0043] (3) Grinding mud materia...

Embodiment 3

[0054] The present invention provides a technical solution: a novel method for combining blue and white materials with Nixing pottery. The raw materials include the following components: east mud, west mud, quartz, kaolin, hematite, water and blue and white materials, including the following steps in turn:

[0055] (1) Mud weathering and dissolution treatment: place the east mud and west mud in an open area, and after 4 to 6 months of wind, sun and rain until the mud is broken up, it will be collected and stored after dissolution and oxidation, and wait for future use. The ratio of mud and western mud is 60 parts of eastern mud and 40 parts of western mud.

[0056] (2) Mud crushing treatment: put the weathered material in step (1) into a ball mill for grinding, collect and store it after grinding, and wait for standby. The model of the ball mill is MQ750×1800, and the ball mill is made of pebbles. The control is 49r / min, and the ball milling time is controlled at 6h.

[0057]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel blue-and-white mud material and Nixing pottery combination method. The method sequentially comprises the following steps: performing weathering and dissolving treatment on the mud; carrying out soil crushing treatment on the pug; screening and filtering the ground pug; pressing the pug and carrying out vacuum treatment; aging the pug; carrying out formability treatment; carrying out throwing forming treatment; carrying out finishing treatment; drying the pottery green body; treating the modified pottery green body; carrying out firing treatment on the pottery green body; and cooling and molding the pottery. According to the novel method for combining the blue-and-white material with the Nixing pottery, the kaolin, the quartz and the hematite powder are added into the pug, so that the blue-and-white material can be attached to the pottery, and the blue-and-white material is more stable during combination. In addition, the hematite powder is added, so that the toughness and rigidity of the pottery are more excellent when the pottery is fired; pine is selected as fuel, and the temperature in the kiln is more uniform due to the fact that flames generated by burning the pine are long, heat is high and ash is little. Most importantly, pine oil contained in the pine wood is very high in flammability, the function of enriching the glaze surface is achieved, and the pottery is more exquisite.

Description

technical field [0001] The invention relates to the technical field of Nixing pottery, in particular to a method for combining novel blue and white materials with Nixing pottery. Background technique [0002] Pottery is a utensil made of clay or clay that is kneaded and then fired. Pottery has a long history, and simple and rough pottery was first seen in the Neolithic Age. Pottery was used as a daily necessities in ancient times, and is now generally collected as handicrafts. The famous pottery varieties in my country include: Jiangsu Zisha pottery, Chongqing Rongchang pottery, Jingdezhen pottery, Yunnan Jianshui pottery and Guangxi Qinzhou Nixing pottery, among which Nixing pottery is in The "natural pottery color" produced by the kiln after the firing process is a highlight in the artistic style of Nixing pottery in Qinzhou, and the clay for making pottery is very plastic. Xingtao reveals a mellow and strong humanistic flavor in its simplicity and simplicity. It is an ele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/24C04B33/16C04B33/13C04B41/87C04B33/32
CPCC04B33/131C04B33/16C04B33/24C04B33/32C04B41/009C04B41/5072C04B41/87C04B2235/3272C04B2235/612C04B2235/6567
Inventor 黄涛默齐越李肖琼
Owner QINZHOU CITY HUAXIA TAIJIQUAN NINGXING POTTERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap