Fireproof tent fabric and preparation method thereof

A tent fabric, fire-resistant technology, applied in the field of fabrics, can solve the problems of shortening the service life of tent fabrics, property loss, personal injury, etc.

Pending Publication Date: 2021-06-18
李金赛
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, with the improvement of living standards, people have generally begun to make changes to their leisure time, so going out camping has become the first choice for most people. Tents are an indispensable portable rest tool in camping, and their fabric performance has been greatly improved. Attention should be paid to it. The performance of most tent fabrics is concentrated on lightness, breathability and wind and sand resistance. Some polyester fabric tents are better than other conventional fabrics in terms of warmth retention, and tensile breaking strength and tear resistance are also major advantages, but It is inevitable to encounter some accidents outdoors, such as accidental fire, most of the tents will be burned, resulting in a shorter service life of the tent fabric, and even causing injury to personnel and loss of property, making people's camping Pleasure is greatly reduced, therefore, it is necessary to design a fire-resistant tent fabric with flame retardancy and moisture resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The invention provides a technical solution: a fire-resistant tent fabric and a preparation method thereof, comprising the following raw materials in parts by weight:

[0025] 50-80 parts of epoxy resin, 50-80 parts of cured flame-retardant epoxy resin, 50-80 parts of porous layer epoxy resin, and 70-100 parts of fabric.

[0026] Preferably, the flame-retardant epoxy resin cured product contains butyl titanate, starch-coated mesoporous calcium carbonate, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide .

[0027] Preferably, the starch-coated mesoporous calcium carbonate is prepared by mixing and stirring mesoporous calcium carbonate and starch at a mass ratio of 1:2 to 1:3, drying and grinding, and the mesoporous calcium carbonate is made of calcium carbonate , calcium chloride and sodium lauryl sulfate in a mass ratio of 2:2:1 to 4:4:1, mixed and dried, and washed with alcohol.

[0028] Preferably, the porous layer epoxy resin is mixed with epoxy resin and emulsifie...

Embodiment 1

[0039] Embodiment 1: A kind of refractory tent fabric one

[0040] A fire-resistant tent fabric, comprising the following raw materials in parts by weight:

[0041] 50 parts of epoxy resin, 50 parts of flame retardant epoxy resin cured product, 50 parts of porous layer epoxy resin, 70 parts of fabric.

[0042] A fire-resistant tent fabric and a preparation method thereof, comprising the following specific steps:

[0043] (1) Preparation of starch-coated mesoporous calcium carbonate: calcium carbonate and surfactant are obtained by a series of operations in a mass ratio of 4:1, and then mesoporous calcium carbonate and starch are mixed in a mass ratio of 1: 2 mixed and prepared through a series of operations;

[0044] (2) Preparation of flame-retardant epoxy resin cured product: Add 0.2 times the butyl titanate of epoxy resin to the epoxy resin to react, and remove the 9,10-dihydro-9-oxa-10- Phosphaphenanthrene-10-oxide and starch-coated mesoporous calcium carbonate are mixe...

Embodiment 2

[0051] Example 2: A fire-resistant tent fabric 2

[0052] A fire-resistant tent fabric, comprising the following raw materials in parts by weight:

[0053] 80 parts of epoxy resin, 80 parts of flame retardant epoxy resin cured product, 80 parts of porous layer epoxy resin, and 100 parts of fabric.

[0054] A fire-resistant tent fabric and a preparation method thereof, comprising the following specific steps:

[0055] (1) Preparation of starch-coated mesoporous calcium carbonate: calcium carbonate and surfactant are obtained by a series of operations at a mass ratio of 2:1, and then mesoporous calcium carbonate and starch are obtained at a mass ratio of 1: 3 mixed and prepared through a series of operations;

[0056] (2) Preparation of flame-retardant epoxy resin cured product: Add 0.5 times the butyl titanate of epoxy resin to the epoxy resin to react, and remove the 9,10-dihydro-9-oxa-10- Phosphaphenanthrene-10-oxide and starch-coated mesoporous calcium carbonate are mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Gram weightaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fireproof tent fabric and a preparation method thereof, and relates to the field of fabrics. The preparation method comprises the following steps: firstly, coating polyester fibers of the tent fabric with a layer of epoxy resin, standing for a period of time, then coating the polyester fibers coated with the epoxy resin with a layer of flame-retardant epoxy resin cured material which is modified with butyl titanate, starch-coated mesoporous calcium carbonate and 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide again, standing for a period of time, finally coating the polyester fibers of the tent fabric with a layer of porous epoxy resin which is obtained by curing sorbitan monolauric acid and silicon dioxide, so as to obtain the fireproof tent fabric. The fireproof tent fabric has better flame retardant property, moisture resistance and thermal stability.

Description

technical field [0001] The invention relates to the field of fabrics, in particular to a fire-resistant tent fabric and a preparation method thereof. Background technique [0002] In recent years, with the improvement of living standards, people have generally begun to make changes to their leisure time, so going out camping has become the first choice for most people. Tents are an indispensable portable rest tool in camping, and their fabric performance has been greatly improved. Attention should be paid to it. The performance of most tent fabrics is concentrated on lightness, breathability and wind and sand resistance. The warmth retention of some polyester fabric tents will be better than other conventional fabrics, and the tensile breaking strength and tearing strength are also a major advantage, but It is inevitable to encounter some accidents outdoors, such as accidental fire, most of the tents will be burned, resulting in a shorter service life of the tent fabric, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/12D06N3/00
CPCD06N3/12D06N3/0063D06N3/0061D06N3/0036D06N2211/125D06N2209/067
Inventor 李金赛
Owner 李金赛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com