Ultrathin flexible cement decorative plate and preparation method thereof

A decorative board and cement technology, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., can solve the problem that the cement decorative board is easily damaged during handling or installation, and the ultra-thin cement decorative board is hard and brittle and lacks flexibility and other problems, to achieve the effect of improving anti-pan-alkali performance, improving bending toughness and waterproof performance, and good compactness

Active Publication Date: 2021-06-25
漳州市贝丘工艺品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the ultra-thin cement decorative board made by the above technology is too hard and brittle, lacks flexibility, and there is a problem that the cement decorative board is easily damaged during the handling or installation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrathin flexible cement decorative plate and preparation method thereof
  • Ultrathin flexible cement decorative plate and preparation method thereof
  • Ultrathin flexible cement decorative plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A preparation method of an ultra-thin flexible cement decorative board, comprising the following steps:

[0061] S1, the preparation of mixing agent:

[0062] S11, 5Kg magnesium chloride is added in the mixing tank, while adding water, measure solution salinity by Baume meter, when the salinity of solution reaches 22 ° Be after, stop adding water;

[0063] S12, add 0.05Kg of color paste, and after stirring evenly, add 22.5Kg of polyvinyl alcohol, stir evenly, and make the mixed water agent;

[0064] S2, preparation of mortar:

[0065] 10Kg cement, 20Kg magnesia, 20Kg fine sand, 0.5Kg water reducer, 10Kg fly ash, 0.3Kg short fiber are premixed in proportion in turn, and after stirring for 15 minutes, the mortar is prepared;

[0066] S3. Mix the mixing water agent and the mortar according to the mass ratio of 3:8, and stir for 5-8 minutes to obtain a composite slurry;

[0067] S4. Spray a layer of composite slurry in the first mold, spread a layer of non-alkali mesh cl...

Embodiment 2

[0070] A preparation method of an ultra-thin flexible cement decorative board, comprising the following steps:

[0071] S1, the preparation of mixing agent:

[0072] S11, 1Kg magnesium chloride is added in the mixing tank, while adding water, measure solution salinity by Baume meter, after the salinity of solution reaches 25 ° of Be, stop adding water;

[0073] S12, add 0.07Kg of color paste, and after stirring evenly, add 4.5Kg of polyvinyl alcohol, stir evenly, and make mixing water;

[0074] S2, preparation of mortar:

[0075] 5Kg cement, 10Kg magnesia, 10Kg fine sand, 0.1Kg superplasticizer, 5Kg fly ash, 0.1Kg short fiber were premixed in proportion in turn, and after stirring for 15 minutes, the mortar was prepared;

[0076] S3. Mix the mixing water agent and the mortar according to the mass ratio of 3:6, and stir for 5 minutes to obtain a composite slurry;

[0077] S4. Spray a layer of composite slurry in the first mold, spread a layer of non-alkali mesh cloth on the ...

Embodiment 3

[0080] A preparation method of an ultra-thin flexible cement decorative board, comprising the following steps:

[0081] S1, the preparation of mixing agent:

[0082] S11, 3Kg magnesium chloride is added in the mixing tank, while adding water, measure solution salinity by Baume meter, when the salinity of solution reaches 22 ° Be, stop adding water;

[0083] S12, add 0.1Kg of color paste, and after stirring evenly, add 13.5Kg of polyvinyl alcohol, stir evenly, and make the mixed water agent;

[0084] S2, preparation of mortar:

[0085] 7.5Kg of cement, 15Kg of magnesium oxide, 15Kg of fine sand, 0.3Kg of water reducer, 7.5Kg of fly ash, and 0.2Kg of short fibers were premixed in proportion in sequence, and after stirring for 20 minutes, the mortar was prepared;

[0086] S3. Mix the mixing water agent and the mortar according to the mass ratio of 3:7, and stir for 5 minutes to obtain a composite slurry;

[0087] S4. Spray a layer of composite slurry in the first mold, spread ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of building materials, and particularly discloses an ultrathin flexible cement decorative plate and a preparation method thereof. The ultrathin flexible cement decorative plate comprises a plate body and a plurality of pieces of alkali-free gridding cloth, the upper surface of the plate body is in texture color, a single piece of alkali-free gridding cloth is horizontally embedded in the plate body, and the plurality of pieces of alkali-free gridding cloth are distributed in the height direction of the plate body; The plate body comprises the following raw materials in parts by weight: 5-10 parts of cement; 10-20 parts of fine sand; 0.1-0.3 part of short fiber; 0.2-0.5 part of a filler; 10-20 parts of magnesium oxide; 1-5 parts of magnesium chloride; 4.5-22.5 parts of polyvinyl alcohol; 5-10 parts of fly ash; And 0.1-0.5 part of a water reducing agent. The ultrathin flexible cement decorative plate has the advantages of being good in flexibility and good in waterproof effect.

Description

technical field [0001] The application relates to the technical field of building materials, more specifically, it relates to an ultra-thin flexible cement decorative board and a preparation method thereof. Background technique [0002] The imitation wood production process has been greatly improved through people's hard work and research. It has overcome technical problems such as long-term corrosion, oxidation and vulnerability, and can develop, design, and manufacture a variety of materials and sketches for decoration applications. It is an excellent substitute for wood. Nowadays, when my country's wood resources are extremely scarce, imitation wood has become the mainstream of decoration and decoration. [0003] Among them, the ultra-thin flexible cement decorative board is a relatively common decoration. The cement decorative board, also known as the draped board, is a fiber cement board with decorative high temperature and high pressure steaming treatment. The main co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32C04B24/26C04B18/14
CPCC04B28/32C04B24/2623C04B18/146C04B7/02C04B14/06C04B20/0048C04B18/26C04B18/248C04B18/08C04B2103/302Y02W30/91
Inventor 江卫平