Light alloy vacuum high-pressure casting flexible loading casting-forging composite forming device and application method thereof

A flexible loading, high-pressure casting technology, applied in the field of light alloy vacuum casting and forging composite forming devices, can solve the problems of difficult control of casting defects at thick walls, achieve the effect of fine grain strengthening and macro mechanical properties, and reduce casting defects. The effect of gas residue

Active Publication Date: 2021-07-09
HARBIN INST OF TECH
View PDF13 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the technical problem of difficult control of casting defects at the thick wall of the current alloy vacuum die-casting technology, and provides a light alloy vacuum high-pressure casting flexible loading casting-forging composite forming device and its use method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light alloy vacuum high-pressure casting flexible loading casting-forging composite forming device and application method thereof
  • Light alloy vacuum high-pressure casting flexible loading casting-forging composite forming device and application method thereof
  • Light alloy vacuum high-pressure casting flexible loading casting-forging composite forming device and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0034] Specific implementation mode 1: This implementation mode is a light alloy vacuum high-pressure casting flexible loading casting and forging composite forming device, such as Figure 1-Figure 6 As shown, it is specifically composed of a movable mold bottom plate 1, a movable mold ejector rod 2, a return spring 3, a movable mold cushion block 4, a vacuum valve 5, a vacuum pump 6, a movable mold 7, a flexible loading cylinder fixing frame 8, and a flexible loading hydraulic cylinder 9 , flexible loading dowel 10, blanking hydraulic cylinder bracket 11, blanking hydraulic cylinder 12, blanking cutting tool 13, fixed mold bottom plate 14, injection cylinder 15, injection piston 16, fixed mold middle plate 17, flexible loading block 19. Composed of flexible loading limit plate 20, ejector rod 21, ejector rod fixing plate 22, ejector rod bottom plate 23 and guide rod 24;

[0035] The movable mold base plate 1 is fixedly connected with two movable mold cushion blocks 4 and the ...

specific Embodiment approach 2

[0040] Embodiment 2: This embodiment differs from Embodiment 1 in that: the flexible loading dowel 10 is a cylindrical structure. Others are the same as the first embodiment.

specific Embodiment approach 3

[0041] Embodiment 3: This embodiment differs from Embodiment 1 or Embodiment 2 in that: the guide rod 24 is a cylindrical structure. Others are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a light alloy vacuum high-pressure casting flexible loading casting-forging composite forming device and an application method thereof, and relates to a light alloy vacuum casting-forging composite forming device and an application method thereof. The invention aims to solve the technical problem that casting defects at a thick wall are difficult to regulate and control in the current alloy vacuum die-casting technology. According to the device, a vacuum pump is used for pumping out gas in a cavity before aluminum alloy or magnesium alloy melt enters the cavity of a die, so that gas residues in the cavity are greatly reduced, the gas entrapment degree of a die casting is obviously lowered, and the effect of improving the mechanical properties and compactness of the die casting is obvious; and a flexible loading system which is composed of a flexible loading hydraulic cylinder, a flexible loading dowel bar, a flexible loading limiting plate and a flexible loading block and mounted on a movable die is adopted to conduct local loading and forced feeding on the liquid-solid aluminum alloy or magnesium alloy melt, so that the casting defects at the thick wall are obviously reduced, which is beneficial for improving the compactness and macroscopic mechanical properties of the casting.

Description

technical field [0001] The invention relates to a light alloy vacuum casting and forging composite forming device and its application method. Background technique [0002] Light alloy metal materials including aluminum alloys and magnesium alloys are widely used in the fields of aviation, aerospace, weapons, automobiles, rail transit and 3C due to their light weight, high specific strength and specific stiffness, energy saving and emission reduction. be widely used. The national demand for energy saving, emission reduction, efficiency increase and consumption reduction is constantly increasing, which is very urgent for the lightweight of equipment, and the simple replacement of traditional steel with aluminum alloy or magnesium alloy can not meet the requirements of equipment use. Combined with forming manufacturing methods to achieve real lightweight, this can meet the needs of equipment use and ensure the safety and efficiency of its operation. Die-casting technology is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D17/14B22D17/20B22D17/10
CPCB22D17/14B22D17/2069B22D17/10
Inventor 姜巨福王迎李明星秦少华
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap