Shoe polish prepared from wool fat extract and preparation method of shoe polish

A technology of extract and lanolin, which is applied in the field of shoe polish prepared by lanolin extract and its preparation field, and achieves the effects of high shelf life, easy operation, excellent gloss and water resistance

Inactive Publication Date: 2021-07-09
浙江花园营养科技有限公司
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Lanolin extract is the paste-like waste of lanolin industrially purified, dark brown, oily, paste-like, and pure natural; its structure is still a complex mixture of various higher fatty acid higher fatty alcohol esters, which can be used as shoe polish preparation The main component, but the shoe polish with lanolin extract as the main raw material has not been reported yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A shoe polish prepared from lanolin extract comprises the following components by weight:

[0039] 60 parts of modified lanolin extract;

[0040] 25 parts of modified mixed wax;

[0041] 15 parts white oil;

[0042] 1 part of methyl silicone oil;

[0043] 1 part of vinyl tri(dimethylsiloxane) silane;

[0044] 1 part of glycerin;

[0045] 1 part of regulator;

[0046] 1 part emulsifier;

[0047] Wherein the modified lanolin extract comprises the following components by weight:

[0048] 50 parts of lanolin extract;

[0049] 5 parts modifier;

[0050] Described modifying agent is the mixture of sorbitan monooleate, fatty alcohol polyoxyethylene ether and (1-fluoro-2-phenylvinyl) (4-aminophenyl) sulfide, and its mass ratio is 2:2:1;

[0051] The moisture in the lanolin extract is less than 2.0%, the acid value is less than 10.0 mgKOH / g, the saponification value is 100 mgKOH / g, and the ash content is less than 0.30%;

[0052] The preparation method of the modified...

Embodiment 2

[0065] A shoe polish prepared from lanolin extract comprises the following components by weight:

[0066] 55 parts of modified lanolin extract;

[0067] 20 parts of modified mixed wax;

[0068] 12 parts white oil;

[0069] 2 parts of methyl silicone oil;

[0070] 1 part of vinyl tri(dimethylsiloxane) silane;

[0071] 1 part of glycerin;

[0072] Regulator 0.5 parts;

[0073] 0.5 parts of emulsifier;

[0074] The modified lanolin extract comprises the following components by weight:

[0075] 40 parts of lanolin extract;

[0076] Modifier 4 parts;

[0077] Described modifying agent is the mixture of sorbitan monooleate, fatty alcohol polyoxyethylene ether and (1-fluoro-2-phenylvinyl) (4-aminophenyl) sulfide, and its mass ratio is 2:2:1;

[0078] The moisture in the lanolin extract is less than 2.0%, the acid value is less than 10.0 mgKOH / g, the saponification value is 95 mgKOH / g, and the ash content is less than 0.30%;

[0079] The preparation method of the modified l...

Embodiment 3

[0093] A shoe polish prepared from lanolin extract comprises the following components by weight:

[0094] 65 parts of modified lanolin extract;

[0095] 30 parts of modified mixed wax;

[0096] 18 parts white oil;

[0097] 0.5 parts of methyl silicone oil;

[0098] 0.5 parts of vinyl tris (dimethylsiloxane) silane;

[0099] 1.8 parts of glycerin;

[0100] 1.5 parts of regulator;

[0101] 2 parts emulsifier;

[0102] The modified lanolin extract comprises the following components by weight:

[0103] 55 parts of lanolin extract;

[0104] 6 parts of modifier;

[0105] Described modifying agent is the mixture of sorbitan monooleate, fatty alcohol polyoxyethylene ether and (1-fluoro-2-phenylvinyl) (4-aminophenyl) sulfide, and its mass ratio is 2:2:1;

[0106] The moisture in the lanolin extract is less than 2.0%, the acid value is less than 10.0 mgKOH / g, the saponification value is 105 mgKOH / g, and the ash content is less than 0.30%;

[0107] The preparation method of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Acid valueaaaaaaaaaa
Saponification valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses shoe polish prepared from a wool fat extract and a preparation method of the shoe polish, and the shoe polish is prepared by taking the modified wool fat extract as a main raw material and simultaneously adding substances such as modified mixed wax, a regulator and an emulsifier. The modified wool fat extract is obtained by modifying a wool fat extract through a modifier, and the modifier is a mixture of sorbitan monooleate, fatty alcohol-polyoxyethylene ether and (1-fluoro-2-phenyl vinyl) (4-aminophenyl) thioether; and the modified mixture is prepared by taking liquid paraffin, microcrystalline wax and carnauba wax as raw materials and under the promotion action of an accelerant, and the accelerant is a mixture of 3, 4, 6-trihydroxy-5-oxo-5H-benzo [7] cyclopent-8-carboxylic acid propyl ester, bisphenol A glycerol dimethacrylate and 1, 2-epoxyhexyl-5-ene. The shoe polish prepared from the lanolin extract enables leather to have excellent glossiness and waterproofness, and meanwhile, the shoe polish has very high wiping resistance and durability and is wide in application range.

Description

technical field [0001] The invention belongs to the technical field of daily chemicals, in particular to a shoe polish prepared from lanolin extract and a preparation method thereof. Background technique [0002] Shoe polish is a daily chemical product used to polish and repair leather shoes, and enhance its waterproof, leather protection, surface gloss, cleaning and color-adding effects. It is used in large amounts in daily life. At present, shoe polish mainly includes hard paste body, ointment body and liquid type, and the active ingredients thereof are all waxes. At present, most of the colorants used in the dark shoe polishes on the market are chemically synthesized dyes, which are easy to cause harm to the environment and the human body. Therefore, it is of great significance to develop a shoe polish containing natural colorants under this background. [0003] Lanolin is a natural product, and its composition belongs to the category of wax, which is a complex mixture o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09G1/12
CPCC09G1/12
Inventor 吴江浩钱国平王子强邵振宝陆裕厚
Owner 浙江花园营养科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com