A kind of preparation method of highly active nanocrystalline NiO thin film

A nanocrystalline, high-activity technology, applied in the direction of nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., can solve the problems of NiO electrochromic performance attenuation, and achieve the improvement of NiO electrochromic performance and low cost. Inexpensive, good electrochromic performance

Active Publication Date: 2022-04-22
NANJING UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Finally, NiOOH will produce self-discharge and partial dissolution during the process of fading and reduction, which will attenuate the electrochromic performance of NiO

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of highly active nanocrystalline NiO thin film
  • A kind of preparation method of highly active nanocrystalline NiO thin film
  • A kind of preparation method of highly active nanocrystalline NiO thin film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] As shown in Figure 1, the preparation method of a 20-layer NiO film with an electrochromic effect of 67% at a wavelength of 500nm, the specific operations are as follows:

[0021] (1) Clean the conductive glass with common detergent, rinse with deionized water, and then use acetone, ethanol, and deionized water to sonicate for 20 minutes to obtain a conductive glass substrate with a clean surface.

[0022] (2) The PEI aqueous solution that monomer concentration is 0.2M and the nickel nitrate aqueous solution of 0.1M are mixed in equal volumes, and the PEI-Ni complex aqueous solution of 0.1M is obtained, wherein PEI monomer concentration: the concentration of nickel nitrate is 2:1.

[0023] (3) Soak the cleaned conductive glass in the PAA aqueous solution with a monomer concentration of 0.1M for 5 minutes, clean it with deionized water to obtain a negatively charged film on the surface, and then soak it in a 0.1M PEI-Ni complex. After rinsing with deionized water for 5 ...

Embodiment 2

[0027] Such as figure 2 As shown, the preparation method of a 10-layer NiO thin film with electrochromic efficiency reaching 50% at a wavelength of 500nm, the specific operations are as follows:

[0028] (1) Clean the conductive glass with common detergent, rinse with deionized water, and then use acetone, ethanol, and deionized water to sonicate for 20 minutes to obtain a conductive glass substrate with a clean surface.

[0029] (2) The PEI aqueous solution that monomer concentration is 0.2M and the nickel nitrate aqueous solution of 0.1M are mixed in equal volumes, and the PEI-Ni complex aqueous solution of 0.1M is obtained, wherein PEI monomer concentration: the concentration of nickel nitrate is 2:1.

[0030] (3) Soak the cleaned conductive glass in the PAA aqueous solution with a monomer concentration of 0.1M for 5 minutes, clean it with deionized water to obtain a negatively charged film on the surface, and then soak it in a 0.1M PEI-Ni complex. After rinsing with dei...

Embodiment 3

[0034] A method for preparing a NiO thin film with an electrochromic effect of 10% at a wavelength of 500nm, the specific operations are as follows:

[0035] (1) Clean the conductive glass with common detergent, rinse with deionized water, and then use acetone, ethanol, and deionized water to sonicate for 20 minutes to obtain a conductive glass substrate with a clean surface.

[0036] (2) The PEI aqueous solution that monomer concentration is 0.02M and the nickel nitrate aqueous solution of 0.01M are mixed in equal volumes, and the PEI-Ni complex aqueous solution of 0.01M is obtained, wherein PEI monomer concentration: the concentration of nickel nitrate is 2:1.

[0037] (3) Soak the cleaned conductive glass in the PAA aqueous solution with a monomer concentration of 0.01M for 5 minutes, then wash it with deionized water to obtain a negatively charged film on the surface, and then soak it in 0.01M PEI-Ni network 5 minutes in the aqueous solution of NiO, and after cleaning wit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a highly active nanocrystalline NiO film, which comprises the following steps: (1) preparing a NiO precursor film on a substrate by a layer-by-layer self-assembly method; (2) placing the NiO precursor film on an ultraviolet ray Under light irradiation, the organic matter in the NiO precursor film is decomposed by ultraviolet light and the NiO is crystallized into nanoparticles to prepare a highly active nanocrystalline NiO film. The invention utilizes a method combining ultraviolet light irradiation and layer-by-layer self-assembly to prepare a highly active NiO nano-film, the method is simple, cheap, and does not require complicated equipment. The prepared NiO film is highly active, and the electrochromic performance is at 500nm wavelength up to 67%.

Description

technical field [0001] The invention relates to a method for preparing a NiO thin film, in particular to a method for preparing a highly active nanocrystalline NiO thin film. Background technique [0002] NiO thin films have broad application prospects in many fields such as supercapacitors, electrochromic materials, sensors, solar cells, and photodiodes. NiO is an anodic color-changing material with good electrochromic properties. It can undergo reversible redox reactions in water-soluble or organic-soluble electrolytes, and can produce reversible switching between transparent reduced states and brown-black oxidized states. It has the function of causing color change, and has the advantages of fast electrochromic response speed and large color changing range. However, the stability and cycleability of NiO are poor, and its performance will decline after long-term operation. For example, in alkaline electrolyte, NiO will become NiOOH through oxidation and coloring reaction,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/27C01G53/04B82Y30/00
CPCC03C17/27C01G53/04B82Y30/00C03C2217/217C01P2002/82C01P2004/04
Inventor 章建辉施泽宇顾明
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com