Integral forming process of foamed aluminum and fiber reinforced resin-based composite sandwich panel

A technology of fiber-reinforced resin and foamed aluminum plate, applied in lamination auxiliary operations, chemical instruments and methods, lamination, etc., can solve problems such as high production difficulty, material damage, and insufficient bonding strength, so as to speed up production tempo and improve Strength and the effect of improving productivity

Active Publication Date: 2021-08-06
中机精密成形产业技术研究院(安徽)股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide an integral molding process of aluminum foam and fiber-reinforced resin-based composite sandwich panels to solve the technical problems in the prior art of insufficient bonding strength, damage to materials by bolt connections, and high production difficulty

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Integral forming process of foamed aluminum and fiber reinforced resin-based composite sandwich panel
  • Integral forming process of foamed aluminum and fiber reinforced resin-based composite sandwich panel
  • Integral forming process of foamed aluminum and fiber reinforced resin-based composite sandwich panel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0048] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0049] Such as figure 1 , figure 2 , image 3 and Figure 4 As shown, the present invention provides an integral molding process of aluminum foam and fiber-reinforced resin-based composite sandwich panels, comprising the following steps:

[0050] Step 100: Carrying out chemical film treatment on the surface of the foamed aluminum plate to obtain the once-treated foamed aluminum plate;

[0051] Step 200: using a dielectric material to fill pores on the sur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an integral forming process of a foamed aluminum and fiber reinforced resin-based composite sandwich panel, which comprises the following steps: step 100, carrying out chemical coating treatment on the surface of a foamed aluminum plate to obtain a primarily treated foamed aluminum plate; 200, performing pore filling treatment on the surface of the foamed aluminum plate subjected to primary treatment by using a dielectric material to obtain a foamed aluminum plate subjected to secondary treatment; 300, laying two fiber-reinforced resin-based composite boards symmetrically on the two sides of a mold, and placing the foamed aluminum board subjected to secondary treatment between the two fiber-reinforced resin-based composite boards; and 400, heating the sandwich type pressing equipment to the preset temperature, and enabling a combined structure formed by the two fiber-reinforced resin-based composite boards and the foamed aluminum board subjected to secondary treatment to be pressed and formed under the preset pressure through the sandwich type pressing equipment. According to the invention, the coupling property between the foamed aluminum sandwich layer and the composite material laminated plate is improved.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to an integral molding process of aluminum foam and fiber-reinforced resin-based composite sandwich panels. Background technique [0002] Foamed aluminum is made by adding additives to pure aluminum or aluminum alloy and undergoes a foaming process. It has the characteristics of metal and air bubbles at the same time. Surface coating, with excellent physical and chemical properties and recyclability. [0003] However, the existing aluminum foam has a single structure, so its mechanical properties and flame-retardant and heat-insulating properties are poor, and it is difficult to be used in occasions that require high mechanical properties and flame-retardant and heat-insulating properties. The current solution to these problems is to combine the mechanical properties of foamed aluminum and play a barrier role by using foamed aluminum as a sandwich material and connectin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B37/06B32B37/10B32B38/00
CPCB32B37/06B32B37/10B32B38/00
Inventor 孙奋丽郭平安边翊金康王小刚黎诚殷剑
Owner 中机精密成形产业技术研究院(安徽)股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap