A kind of aluminum veneer decorative material for curtain wall and its manufacturing process

A decorative material and manufacturing process technology, applied in the field of aluminum veneer decorative material for curtain wall and its manufacturing process, can solve the problems of large odor, insufficient corrosion resistance of the surface of aluminum plate, affecting the working environment, etc. The effect of improving environmental health and protecting personal safety

Active Publication Date: 2022-08-02
湖北欣洁顺幕墙材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, when the common aluminum veneer is produced, it will produce a large odor when it is electrolytically oxidized, which will affect the working environment. At the same time, the aluminum plate is not sealed when it leaves the factory, which makes subsequent use During the process, the surface corrosion resistance of the aluminum plate is not high enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An aluminum veneer decorative material for a curtain wall and a manufacturing process thereof, comprising the following steps:

[0029] S1: First take the heating and melting machine and the aluminum ingots needed for casting, and start aluminum veneer casting: heat and melt the aluminum ingots, add 0.01% titanium and 0.005% zirconium according to the mass of the aluminum ingots, get the initial raw material;

[0030] S2: Put the ingot processed in step S1 into the homogenization furnace, and start to homogenize the ingot,

[0031] S3: During the homogenization process in step S2, if there are defects such as segregation, slag, scarring and cracks on the surface of the ingot, milling should be carried out; the cutting amount depends on the depth of the defect, generally 4-10mm

[0032] S4: The initial raw material obtained in step S3 is first heated to a certain temperature to reach the critical point of aluminum liquefaction, then cut and sent to an extruder to be ext...

Embodiment 2

[0040] An aluminum veneer decorative material for a curtain wall and a manufacturing process thereof, the aluminum veneer decorative material for a curtain wall and a manufacturing process thereof comprising the following steps:

[0041]S1: First take the heating and melting machine and the aluminum ingots needed for casting, and start aluminum veneer casting: heat and melt the aluminum ingots, add 0.01% titanium and 0.005% zirconium according to the mass of the aluminum ingots, get the initial raw material;

[0042] S2: Put the ingot processed in step S1 into the homogenization furnace, and start to homogenize the ingot,

[0043] S3: During the homogenization process in step S2, if there are defects such as segregation, slag, scarring and cracks on the surface of the ingot, milling should be carried out; the cutting amount depends on the depth of the defect, generally 4-10mm

[0044] S4: The initial raw material obtained in step S3 is first heated to a certain temperature to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminum veneer decorative material for a curtain wall and a manufacturing process thereof. In the present invention, the aluminum plate is then subjected to anodizing treatment, 3 / 4 of the total volume of deionized water is added to the tank, the air mixer is started, the calculated amount of sulfuric acid is slowly added to the tank, and 100-150 of dibasic acid is added according to the formula requirements. parts, 50-100 parts of polyol, 150-200 parts of activated carbon particles, mix and stir until completely dissolved, add water to the total volume, add aluminum scraps or old oxidizing liquid; take 15% nickel acetate cobalt acetate boric acid solution, mix The aluminum material is placed into the solution for sealing, and then it is packaged to complete the entire preparation process. When the aluminum plate is anodized, 150-200 copies of activated carbon particles are added to the tank. The toxic and harmful gases produced are adsorbed for purification and odor to prevent them from being directly inhaled by the human body, thereby causing irreversible damage, protecting the personal safety of operators, and improving the environmental health of the process.

Description

technical field [0001] The invention belongs to the technical field of aluminum production, in particular to an aluminum veneer decorative material for curtain walls and a manufacturing process thereof. Background technique [0002] Metal curtain wall is a new type of building curtain wall used for decoration. It is a form of curtain wall that replaces the glass in the glass curtain wall with a metal sheet, but due to the different surface materials, there is a big difference between the two, so they should be considered separately in the design and construction process. Due to the excellent processing performance, variety of colors and good safety of sheet metal, it can fully adapt to the design of various complex shapes, can add concave and convex lines arbitrarily, and can process various types of curved lines, giving Architects are favored by architects because of their huge play space, so they have achieved rapid development; the surface materials used in metal curtain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/00E04C2/08B22C9/22C25D11/08C25D11/22C25D11/24
CPCB23P15/00E04C2/08B22C9/22C25D11/08C25D11/22C25D11/246
Inventor 陈顺南
Owner 湖北欣洁顺幕墙材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com