Special tool fabric capable of resisting static aggregation

An antistatic, special-purpose technology, applied in the field of tooling fabrics, can solve problems such as poor antistatic effect and affecting the use of fabrics

Active Publication Date: 2021-09-07
YI HE STOCK
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing tooling fabrics have poor antistatic effect, which is easy to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A special-purpose tooling fabric for antistatic aggregation of the present embodiment comprises the following raw materials in parts by weight:

[0026] 40 parts of flax fiber, 15 parts of bamboo fiber, 5 parts of antistatic modifier, 3 parts of modified talcum powder, 1 part of bentonite powder;

[0027] The preparation method of described antistatic modifier is:

[0028] S1, the graphene is sent into the ethanol solvent and stirred at a low speed, the stirring time is 10min, and the stirring speed is 500r / min. For 300r / min, stirring finishes, obtains graphene agent;

[0029] S2, mixing copper powder and nickel powder according to a weight ratio of 4:1, and then sending them into a calciner for calcining at a calcining temperature of 300°C for 10 minutes to obtain a composite powder;

[0030] S3, sending the composite powder of S2 into the graphene agent, then stirring at a low speed at a stirring speed of 100r / min, stirring for 20min, and then performing proton irra...

Embodiment 2

[0038] A special-purpose tooling fabric for antistatic aggregation of the present embodiment comprises the following raw materials in parts by weight:

[0039] 50 parts of flax fiber, 25 parts of bamboo fiber, 10 parts of antistatic modifier, 6 parts of modified talcum powder, 5 parts of bentonite powder;

[0040] The preparation method of described antistatic modifier is:

[0041] S1, the graphene is sent into the ethanol solvent and stirred at a low speed, the stirring time is 20min, and the stirring speed is 1000r / min. For 500r / min, stirring finishes, obtains graphene agent;

[0042] S2, mixing copper powder and nickel powder according to the weight ratio of 4:1, and then sending them into a calcination furnace for calcination at a calcination temperature of 500°C for 20 minutes to obtain a composite powder;

[0043] S3, sending the composite powder of S2 into the graphene agent, then stirring at a low speed, the stirring speed is 500r / min, stirring for 30min, and then ca...

Embodiment 3

[0051] A special-purpose tooling fabric for antistatic aggregation of the present embodiment comprises the following raw materials in parts by weight:

[0052] 45 parts of flax fiber, 20 parts of bamboo fiber, 7.5 parts of antistatic modifier, 4.5 parts of modified talcum powder, 3 parts of bentonite powder;

[0053] The preparation method of described antistatic modifier is:

[0054] S1, the graphene is sent into the ethanol solvent and stirred at a low speed, the stirring time is 15min, and the stirring speed is 750r / min. For 400r / min, stirring finishes, obtains graphene agent;

[0055] S2, mixing copper powder and nickel powder according to a weight ratio of 4:1, and then sending them into a calciner for calcining at a calcining temperature of 400°C for 15 minutes to obtain a composite powder;

[0056] S3, sending the composite powder of S2 into the graphene agent, then stirring at a low speed at a stirring speed of 300r / min for 25min, then performing proton irradiation, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a special tool fabric capable of resisting static aggregation. The special tool fabric is characterized by comprising the following raw materials in parts by weight of 40-50 parts of linen fibers, 15-25 parts of bamboo fibers, 5-10 parts of an antistatic modifier, 3-6 parts of modified talcum powder and 1-5 parts of bentonite powder. The preparation method of the antistatic modifier is shown in the specification. The tool fabric is prepared from the linen fibers, the bamboo fibers and other raw materials, and the anti-static performance of the fabric is improved by adding the anti-static modifier, the modified talcum powder and the bentonite powder; and the antistatic modifier is modified by graphene and then is mixed with composite powder, and the antistatic performance of the antistatic modifier is improved through the assistance of nano zeolite powder.

Description

technical field [0001] The invention relates to the technical field of tooling fabrics, in particular to a special tooling fabric antistatic accumulation. Background technique [0002] Fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing; woven fabrics are also called woven fabrics, which are formed by interweaving warp and weft yarns vertically fabric. There are three basic weaves: plain weave, twill weave and satin weave. Different woven fabrics are also composed of these three basic structures and their varied structures. Mainly chiffon, oxford, denim, twill, flannel, damask and so on. [0003] The existing tooling fabrics have poor antistatic effect, which easily affects the use effect of the fabrics. Based on this, further improvement is needed. Contents of the invention [0004] Aiming at the defect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/47D03D15/217D03D15/533A41D31/26D06M11/74D06M11/79D06M11/83D06M101/04D06M101/06
CPCD03D15/47D03D15/217D03D15/533A41D31/26D06M11/74D06M11/79D06M11/83D06M2101/06D06M2101/04D10B2201/04D10B2201/10A41D2500/20
Inventor 李超
Owner YI HE STOCK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap