Antibacterial formaldehyde-removing composite inorganic artificial stone and preparation method thereof

A compound and inorganic technology, applied in the field of decorative materials, can solve the problems of human health or environmental damage, long-term effect is difficult to guarantee, and it is not easy to disperse evenly, so as to improve the effect, decompose harmful gases well, and reduce environmental pollution.

Pending Publication Date: 2021-11-12
广州戈兰迪新材料股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main shortcomings of metal ion antibacterial agents are: 1. Metal ions themselves may cause harm to human health or the environment; 2. Must be in direct contact to have antibacterial or antibacterial effects; Ions are used to destroy bacterial proteins, thereby inhibiting bacterial growth. The release may be large in the early stage and have a good effect, but as time goes on, after a period of metal ion release, the later concentration gradually decreases, and the long-term effect is difficult to guarantee; 4 , metal ion antibacterial agent powder is easy to cohere, not easy to disperse evenly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial formaldehyde-removing composite inorganic artificial stone and preparation method thereof
  • Antibacterial formaldehyde-removing composite inorganic artificial stone and preparation method thereof
  • Antibacterial formaldehyde-removing composite inorganic artificial stone and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An antibacterial and formaldehyde-removing composite inorganic artificial stone, comprising the following components in parts by mass:

[0033]

[0034] The aggregate is quartz sand and ceramic particles. The particle size of 0-15% aggregate is 2-15mm, the particle size of 50-90% aggregate is 20-120 mesh, and the particle size of 10-30% aggregate is less than or equal to 400 mesh.

[0035] The cement is Portland white cement code-named P.W.

[0036] The composite modifier is a VEA composite modifier and a PVA composite modifier.

[0037] The water reducer is polycarboxylate water reducer and alcohol amine water reducer.

[0038] The retarder is gypsum.

[0039] The modified antibacterial powder is the antibacterial powder purchased by Tangse New Material Co., Ltd.

[0040] The preparation method of the described a kind of antibacterial and formaldehyde-removing composite inorganic artificial stone comprises the following steps:

[0041] S1, weigh the aggregate, ...

Embodiment 2

[0047] An antibacterial and formaldehyde-removing composite inorganic artificial stone, comprising the following components in parts by mass:

[0048]

[0049] The aggregates are granite and cullet. Further, in the aggregate, by weight percentage, the particle diameter of 0-15% aggregate is 2-15mm, the particle diameter of 50-90% aggregate is 20-120 mesh, and the particle diameter of 10-30% aggregate is The particle size is less than or equal to 400 mesh.

[0050] The cement is Portland cement code-named P.O.

[0051] The composite modifier is a water-based epoxy resin modifier and a pozzolan active filler.

[0052] The water reducer is a naphthalene-based water reducer.

[0053] The retarder is citric acid.

[0054] The modified antibacterial powder is the antibacterial powder purchased by Tangse New Material Co., Ltd.

[0055] The preparation method of the described a kind of antibacterial and formaldehyde-removing composite inorganic artificial stone comprises the f...

Embodiment 3

[0062] An antibacterial and formaldehyde-removing composite inorganic artificial stone, comprising the following components in parts by mass:

[0063]

[0064]

[0065] The aggregate is quartz sand. Further, in the aggregate, by weight percentage, the particle diameter of 0-15% aggregate is 2-15mm, the particle diameter of 50-90% aggregate is 20-120 mesh, and the particle diameter of 10-30% aggregate is The particle size is less than or equal to 400 mesh.

[0066] The cement is aluminate cement.

[0067] The composite modifier is a VEA composite modifier.

[0068] The water reducer is a polycarboxylate water reducer.

[0069] The retarder is glucose.

[0070] The modified antibacterial powder is the antibacterial powder purchased by Tangse New Material Co., Ltd.

[0071] The preparation method of the described a kind of antibacterial and formaldehyde-removing composite inorganic artificial stone comprises the following steps:

[0072] S1, weigh the aggregate, cemen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an antibacterial formaldehyde-removing composite inorganic artificial stone material and a preparation method thereof. The material comprises the following components in parts by mass: 40 to 65 parts of aggregate; 25 to 40 parts of cement; 1 to 10 parts of a composite modifier; 0.001 to 0.008 part of a water reducing agent; 0.0002 to 0.002 part of a retarder; 6.5 to 15 parts of water; and 0.0008 to 0.005 part of modified antibacterial powder. According to the antibacterial formaldehyde-removing composite inorganic artificial stone, the modified antibacterial powder capable of continuously radiating terahertz waves is used for replacing a metal ion antibacterial agent to prepare the artificial stone, direct contact is not needed, good harmful gas decomposition and sterilization effects are achieved, environmental pollution is reduced, and human health is facilitated.

Description

technical field [0001] The invention belongs to the field of decorative materials, and in particular relates to an antibacterial and formaldehyde-removing composite inorganic artificial stone and a preparation method thereof. Background technique [0002] Artificial stone is a new type of decorative material. It has a hard texture and a compact structure. It has the characteristics of wear resistance, pressure resistance, high temperature resistance, corrosion resistance, and impermeability. It is a reusable environmentally friendly and green new building interior decoration material. . [0003] Indoor furniture usually contains formaldehyde, and indoor dark corners are prone to breed bacteria, which affects human health. At present, most of the existing inorganic artificial stones in the market do not have antibacterial and formaldehyde removal effects, and very few have antibacterial effects, and the antibacterial effect is mainly achieved by adding metal ion antibacteria...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B28/06C04B22/06C04B24/26C04B24/28C04B7/12C04B24/24C04B24/12C04B24/00C04B22/14C04B24/06C04B111/20C04B103/69C04B103/30C04B103/22
CPCC04B28/04C04B28/06C04B22/06C04B24/2623C04B24/281C04B7/12C04B24/24C04B24/122C04B24/00C04B22/143C04B24/06C04B2111/00017C04B2111/2092C04B2103/69C04B2103/22C04B2103/302C04B14/06C04B18/023C04B14/048C04B14/22
Inventor 田雨庄峰姜浩
Owner 广州戈兰迪新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com