Single-component polyurethane waterproof coating and preparation method thereof

A polyurethane waterproof, single-component technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of poor concrete bonding strength, low bonding strength retention rate, and affecting project quality, etc., to achieve improved bonding The effect of weakening the strength

Inactive Publication Date: 2021-11-12
KESHUN WATERPROOF TECH CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of use, the paint sometimes has to be soaked in water for a long time, which leads to the deterioration of its bonding strength with concrete, and the low retention rate of bonding strength, which greatly affects the quality of the project

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-component polyurethane waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The second aspect of the embodiment of the present application provides a method for preparing a one-component polyurethane waterproof coating, comprising steps:

[0040] S01. Under vacuum conditions, mix and stir polyether polyol, telechelic polymer, plasticizer and pigments and fillers evenly to obtain the first slurry;

[0041] S02. Add diisocyanate, latent curing agent and catalyst to the first slurry and react for a preset time to obtain a one-component polyurethane waterproof coating.

[0042] In step S01, the polyether polyol, telechelic polymer, plasticizer and pigment can be stirred and heated to 100°C-120°C under the condition of vacuum degree of -0.09MPa~-0.1MPa, dehydrated for 2h-3h, A first slurry is obtained.

[0043] In some embodiments, the reaction in step S01 can be performed in a reaction vessel.

[0044] In step S02, the temperature of the first slurry can be lowered to 70°C-80°C and diisocyanate can be added, then the temperature can be raised to ...

Embodiment 1

[0049] A kind of one-component polyurethane waterproof coating, raw materials include by weight: polyoxypropylene glycol, 15 parts; hydroxyl-terminated polybutadiene, 15 parts; diphenylmethane diisocyanate, 6.9 parts; chlorinated paraffin, 16 parts heavy calcium powder, 42.5 parts; titanium dioxide, 2 parts; dibutyltin dilaurate, 0.1 part; modified oxazolidine latent curing agent, 2.5 parts.

Embodiment 2

[0051] A kind of single-component polyurethane waterproof coating, raw materials include by weight: polyoxypropylene glycol, 10 parts; hydroxyl-terminated polybutadiene, 20 parts; diphenylmethane diisocyanate, 6.9 parts; chlorinated paraffin, 16 parts heavy calcium powder, 42.5 parts; titanium dioxide, 2 parts; dibutyltin dilaurate, 0.1 part; modified oxazolidine latent curing agent, 2.5 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a single-component polyurethane waterproof coating and a preparation method thereof. The single-component polyurethane waterproof coating comprises the following main raw materials in parts by weight: 5-30 parts of polyether polyol, 10-30 parts of a telechelic polymer, and 5.0-7.7 parts of diisocyanate, wherein the weight ratio X: Y of the polyether polyol to the telechelic polymer is 1: (1-6). The telechelic polymer is used for modifying the single-component polyurethane waterproof coating, the bonding performance of the polyurethane coating is greatly improved, the retention rate of the bonding strength of the polyurethane coating and concrete after long-term water soaking is still high, and the problem that the retention rate of the bonding strength of an existing coating and concrete after long-term water soaking is low is solved.

Description

technical field [0001] The present application relates to the technical field of waterproof coatings, in particular to a one-component polyurethane waterproof coating and a preparation method thereof. Background technique [0002] One-component polyurethane waterproof coatings are widely used as a new type of waterproof coatings in the field of building waterproofing because of their excellent overall waterproof effect, excellent mechanical properties, good low-temperature flexibility, and easy use. However, during use, the coating sometimes has to be soaked in water for a long time, which leads to the deterioration of its bonding strength with concrete, and the low retention rate of bonding strength, which greatly affects the quality of the project. Contents of the invention [0003] In view of this, the present application provides a one-component polyurethane waterproof coating and a preparation method thereof, which can keep the adhesion strength retention rate between...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/61C08G18/69C08G18/48C08G18/44
CPCC09D175/14C09D7/61C08G18/698C08G18/4825C08G18/4854C08G18/44C08K2003/2241C08K2003/265C08K3/22C08K3/26
Inventor 吴海洋何进
Owner KESHUN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com