Composite wear-resistant fabric
A kind of wear-resistant fabric and composite technology, which is applied in the direction of wear-resistant fiber, textile and papermaking, fiber treatment, etc., can solve the problems of unfavorable environmental protection, base fabric layer damage, affecting fabric performance, etc., achieve good windproof effect, improve durability Grinding performance, good anti-mildew protection effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] (1) Add 50g of water-based urethane acrylate, 5g of hydroxyethyl methacrylate, 5g of trimethylolpropane triacrylate, 10g of deionized water and 0.2g of SN-5040 into the stirring tank, stir evenly, and then add 20g of A -171 modified nano-silica, stirred at 1200r / min for 30min, so that A-171 modified nano-silica was evenly dispersed, and finally added 0.5g of methyl benzoylformate, stirred evenly to obtain wear-resistant material;
[0039] (2) Apply the wear-resistant material evenly on the surface of the base fabric layer by roller coating, and the coating amount is 10g / m 2 , the composite wear-resistant fabric is obtained after UV curing, wherein the curing energy of UV curing is 600mJ / cm 2 , The curing speed is 8mm / s.
Embodiment 2
[0041](1) Add 55g of water-based polyurethane acrylate, 10g of tripropylene glycol diacrylate, 3g of pentaerythritol triacrylate, 15g of deionized water and 0.7g of OROTAN731A into the stirring tank, stir evenly, and then add 22g of KH-570 modified nano-dioxide For silicon, stir at 1200r / min for 30min to disperse the KH-570 modified nano-silica evenly, and finally add 1.2g of 1-hydroxycyclohexyl phenyl ketone and stir evenly to obtain a wear-resistant material;
[0042] (2) Apply the wear-resistant material evenly on the surface of the base fabric layer by roller coating, and the coating amount is 10g / m 2 , the composite wear-resistant fabric is obtained after UV curing, wherein the curing energy of UV curing is 600mJ / cm 2 , The curing speed is 8mm / s.
Embodiment 3
[0044] (1) Add 65g of water-based polyurethane acrylate, 10g of dipropylene glycol diacrylate, 8g of trimethylolpropane triacrylate, 25g of deionized water and 1.6g of SN-5040 into the stirring tank, stir evenly, and then add 28g of A- 151 modified nano-silica, stirred at 1200r / min for 30min to disperse A-151 modified nano-silica evenly, and finally added 2.3g of isopropylthioxanthone, stirred evenly to obtain wear-resistant material;
[0045] (2) Apply the wear-resistant material evenly on the surface of the base fabric layer by roller coating, and the coating amount is 10g / m 2 , the composite wear-resistant fabric is obtained after UV curing, wherein the curing energy of UV curing is 600mJ / cm 2 , The curing speed is 8mm / s.
PUM
Property | Measurement | Unit |
---|---|---|
antibacterial rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com