Preparation method and application of low-grade tobacco leaf solid-phase extraction adsorbent
An adsorbent and tobacco leaf technology, applied in the field of extraction and analysis, can solve the problems of poor stability of adsorption effect, large recovery pollution, low adsorption efficiency, etc., and achieve the effect of rich pore structure, simple method and strong adsorption capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0035] Example 1
[0036] A low-Ci tobacco solids phase extraction sorbent preparation method, comprising the steps of:
[0037] . S1 was weighed Dayefukao certain amount, the low-order tobacco warehouse, was cut into 0.5 cm length pieces to obtain pieces of cut tobacco;
[0038] . S2 The pieces of cut tobacco was added 5 times the mass ratio, 0.5mol / L NaOH solution at 50 deg.] C water bath for 3h, then filtered off with suction, the filtrate was removed, to obtain pieces of cut tobacco residue;
[0039] S3. The residue was neutralized with pieces of cut tobacco wrapped in three layers of filter paper speed, is placed in a Soxhlet extractor, 10 times the mass of distilled water was added, heated to boiling, condensed reflux 3h, to give a crude product TOBACCO LEAF adsorbent solid phase extraction ;
[0040] S4. TOBACCO LEAF The solid phase extraction sorbent crude product was cooled to room temperature, the low-speed time from tobacco solid phase extraction sorbent crude product ...
Example Embodiment
[0041] Example 2
[0042] A low-Ci tobacco solids phase extraction sorbent preparation method, comprising the steps of:
[0043] . S1 was weighed Dayefukao certain amount, the low-order tobacco warehouse, was cut into 1.2 cm length pieces to obtain pieces of cut tobacco;
[0044] . S2 The pieces of cut tobacco was added 10 times the mass ratio, 2 mol / L NaOH solution at 60 ℃ at 5 h, and then filtered off with suction, the filtrate was removed, to obtain pieces of cut tobacco residue;
[0045] S3. The residue was neutralized with pieces of cut tobacco wrapping paper speed layer 4, solid phase extraction sorbent crude product was placed in a Soxhlet extractor, 20 times the mass of distilled water was added, heated to boiling, condensed reflux 5h, to obtain TOBACCO LEAF ;
[0046] S4. TOBACCO LEAF The solid phase extraction sorbent crude product was cooled to room temperature, the low-speed time from tobacco solid phase extraction sorbent crude product was taken out of the filter pa...
Example Embodiment
[0047] Example 3
[0048] A low-Ci tobacco solids phase extraction sorbent preparation method, comprising the steps of:
[0049] . S1 was weighed Dayefukao certain amount, the low-order tobacco warehouse, it was cut into pieces 1 cm length, to obtain pieces of cut tobacco;
[0050] . S2 was added to the shredded tobacco 8 times the mass ratio, 1 mol / L NaOH solution at 55 ℃ water bath for 4 h, then filtered off with suction, the filtrate was removed, to obtain pieces of cut tobacco residue;
[0051] S3. The crude product was shredded tobacco residue adsorbent solid phase extraction medium speed filter paper wrap layer 3 placed in a Soxhlet extractor, 15 times the mass of distilled water, heated to boiling, condensed reflux 4h, to give TOBACCO LEAF ;
[0052] S4. TOBACCO LEAF The solid phase extraction sorbent crude product was cooled to room temperature, the low-speed time from tobacco solid phase extraction sorbent crude product was taken out of the filter paper, 55 deg.] C and ...
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap