Processing technology of low-energy-consumption environment-friendly carbon black

A processing technology and low energy consumption technology, which is applied in the processing technology field of low energy consumption and environmental protection carbon black, and can solve the problems of insignificant improvement of rubber mechanical properties.

Active Publication Date: 2022-01-07
新疆德欣新材料有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a low-energy-consumption and environmentally friendly carbon black processing technology. Through modified carbon black and reinforcing agent, it is solved that the mechanical properties of rubber are not significantly improved after carbon black is reinforced at the present stage, and agglomeration phenomenon will occur. problems, and enhance the anti-aging effect of rubber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technology of low-energy-consumption environment-friendly carbon black
  • Processing technology of low-energy-consumption environment-friendly carbon black
  • Processing technology of low-energy-consumption environment-friendly carbon black

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of processing technology of low energy consumption environment-friendly carbon black, specifically comprises the following steps:

[0037] Step S1: Dissolve the enhancer in tetrahydrofuran to prepare the enhancer solution, disperse the modified carbon black in deionized water, add triethylamine, and stir at a speed of 150r / min and a temperature of 20°C. Add the enhancement solution dropwise, react for 4 hours, and then centrifuge and dry to obtain pretreated carbon black;

[0038] Step S2: Mix the pretreated carbon black, graphene, and polyvinyl alcohol 600 evenly, ultrasonically treat for 2 hours at a frequency of 60 kHz, and then calcinate for 3 hours at a temperature of 400° C. to obtain environmentally friendly carbon black.

[0039] Modified carbon black is made by the following steps:

[0040]Disperse carbon black in deionized water, stir and pass ozone under the condition of rotating speed of 200r / min, after reacting for 1h, adjust the pH value of the rea...

Embodiment 2

[0046] A kind of processing technology of low energy consumption environment-friendly carbon black, specifically comprises the following steps:

[0047] Step S1: Dissolve the enhancer in tetrahydrofuran to prepare the enhancer solution, disperse the modified carbon black in deionized water, add triethylamine, and stir at a speed of 180r / min and a temperature of 23°C. Add the enhancement solution dropwise, react for 4.5 hours, and then dry by centrifugation to obtain pretreated carbon black;

[0048] Step S2: Mix the pretreated carbon black, graphene, and polyvinyl alcohol 600 evenly, and after ultrasonic treatment for 2.5 hours at a frequency of 70 kHz, roast for 3.5 hours at a temperature of 410°C to obtain environmentally friendly carbon black.

[0049] Modified carbon black is made by the following steps:

[0050] Disperse carbon black in deionized water, stir and pass ozone under the condition of rotating speed of 300r / min, after reacting for 1.3h, adjust the pH value of...

Embodiment 3

[0056] A kind of processing technology of low energy consumption environment-friendly carbon black, specifically comprises the following steps:

[0057] Step S1: Dissolve the enhancer in tetrahydrofuran to prepare the enhancer solution, disperse the modified carbon black in deionized water, add triethylamine, and stir at a speed of 200r / min and a temperature of 25°C. Add the enhancement solution dropwise, react for 5 hours, and then centrifuge and dry to obtain pretreated carbon black;

[0058] Step S2: Mix the pretreated carbon black, graphene, and polyvinyl alcohol 600 evenly, ultrasonicate for 3 hours at a frequency of 80 kHz, and then calcinate for 4 hours at a temperature of 420° C. to obtain environmentally friendly carbon black.

[0059] Modified carbon black is made by the following steps:

[0060] Disperse carbon black in deionized water, stir and pass ozone under the condition of rotating speed of 300r / min, after reacting for 1.5h, adjust the pH value of the reactio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a processing technology of low-energy-consumption environment-friendly carbon black. Pre-treated carbon black and graphene are compounded by taking polyvinyl alcohol 600 as a binder to prepare environment-friendly carbon black, in this way, other toxic binders are avoided, greenness and environmental protection of the carbon black preparation technology are ensured, and meanwhile, no high-power equipment is used for treatment, so that the energy consumption of the carbon black preparation is reduced, the modified carbon black and the reinforcing agent are prepared during the preparation process, the reinforcing agent molecule contains a large amount of hindered amine and hindered phenol structure, the generated free radical or hydroperoxide decomposition can be promoted, the chain reaction can be prevented and the free radical reaction can be eliminated when the reinforcing agent is blended with the rubber, free radicals can generate stable substances to achieve an anti-aging effect, and meanwhile, a mercaptobenzothiazole structure on a molecule can participate in a vulcanization cross-linking reaction of rubber, so that the interaction between the environment-friendly carbon black and rubber quality inspection is enhanced, the reinforcing effect is improved, and the dispersity of filler is promoted.

Description

technical field [0001] The invention relates to the technical field of carbon black preparation, in particular to a processing technology of low energy consumption and environment-friendly carbon black. Background technique [0002] Carbon black is widely used in plastic products due to its good light resistance, heat resistance and antistatic properties. In the application of plastic products, compared with adding carbon black directly, carbon black masterbatch with plastic as the carrier is used It can be better dispersed in plastics, and the blackness of carbon black masterbatch is directly related to the particle size of carbon black. The smaller the particle size, the larger the specific surface area, and the higher the blackness of carbon black. This is because although the primary particles It has been fused into a primary aggregate, but its specific surface can still function. The finer the primary carbon black particles, the larger the specific surface area of ​​the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09C1/56C07D417/14C08K3/04C08K9/02C08K9/04C08K9/08
CPCC09C1/56C09C1/565C07D417/14C08K9/04C08K3/04C08K9/08C08K9/02C08K3/042
Inventor 卢建平顾娇
Owner 新疆德欣新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products