Preparation method of special blade for cigar scissors or cigar knife and blade

A technology for cigar cutters and cigar cutters, applied in applications, tobacco, pipes, etc., can solve the problems of user experience affecting the overall quality of cigar cutters, high blade replacement frequency, and high use costs, and achieve overall quality improvement, low affinity, and high cost. Infrequent replacement effect

Active Publication Date: 2022-03-25
CHENGDU MET CERAMIC ADVANCED MATERIALS
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The object of the present invention is to provide a preparation method and blade for cigar scissors or cigar cutter special blades, so as to solve the problem that the hardness of the material used for preparing cigar cutters in the prior art is low, the blade is easily blunted or the edge is curled, and the replacement frequency of the blade is high. , which affects the overall quality of the cigar cutter and the user experience, and is a technical problem with high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of special blade for cigar scissors or cigar knife and blade
  • Preparation method of special blade for cigar scissors or cigar knife and blade
  • Preparation method of special blade for cigar scissors or cigar knife and blade

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] 1.1 Preparation of cemented carbide materials

[0080] 1.1.1 Raw materials

[0081] The ratio of raw materials is shown in Table 1.

[0082] 1.1.2 Preparation method

[0083] Include the following steps:

[0084] (1) mixing: mixing each raw material according to the proportioning ratio to obtain a homogeneous mixture;

[0085] Adopt ball mill to carry out wet ball milling, ball milling time is 90 hours, add molding agent during ball milling, molding agent adopts paraffin, the adding amount of molding agent is 1.5% of raw material gross weight; Ball milling medium is hexane, and the addition amount of ball milling medium is raw material 30% of the weight; the grinding ball used is a grinding rod, and its consumption is 3 times of the total weight of the raw material;

[0086] (2) dry granulation: dry and granulate the mixture obtained in step (1) to obtain powder;

[0087] Granulation by spray drying: the drying medium is high-temperature nitrogen, the oxygen conten...

Embodiment 2

[0103] 2.1 Preparation of cemented carbide materials

[0104] 2.1.1 Raw materials

[0105] The ratio of raw materials is shown in Table 1.

[0106] 2.1.2 Preparation method

[0107] Include the following steps:

[0108] (1) mixing: mixing each raw material according to the proportioning ratio to obtain a homogeneous mixture;

[0109] Use a ball mill to carry out wet ball milling, the ball milling time is 60 hours, add a molding agent during the ball milling, the molding agent is PEG, and the amount of molding agent added is 2% of the total weight of the raw materials; the ball milling medium is ethanol, and the amount of the ball milling medium is the weight of the raw material 40% of that; the grinding balls used are cemented carbide balls, the amount of which is 4 times the total weight of raw materials;

[0110] (2) dry granulation: dry and granulate the mixture obtained in step (1) to obtain powder;

[0111] Spray drying granulation: the drying medium is high-temperat...

Embodiment 3

[0127] 3.1 Preparation of cemented carbide materials

[0128] 3.1.1 Raw materials

[0129] The ratio of raw materials is shown in Table 1.

[0130] 3.1.2 Preparation method

[0131] Include the following steps:

[0132] (1) mixing: mixing each raw material according to the proportioning ratio to obtain a homogeneous mixture;

[0133] Adopt ball mill to carry out wet ball milling, ball milling time is 30 hours, add molding agent during ball milling, molding agent adopts paraffin, the adding amount of molding agent is 3% of raw material gross weight; Ball milling medium is ethanol, and the addition amount of ball milling medium is raw material weight 30% of that; the grinding balls used are cemented carbide balls, and the amount used is 3 times the total weight of raw materials;

[0134] (2) dry granulation: dry and granulate the mixture obtained in step (1) to obtain powder;

[0135] Spray drying granulation: the drying medium is high-temperature nitrogen to ensure that th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a blade special for cigar scissors or cigar knives and the blade. The blade is made of hard alloy or metal ceramic; when the blade is made of hard alloy, the thickness of the blade is larger than or equal to 0.5 mm and smaller than or equal to 0.8 mm or larger than 0.8 mm and smaller than or equal to 1.5 mm. When the blade is made of metal ceramic, the thickness of the blade is larger than or equal to 0.5 mm and smaller than or equal to 1 mm or larger than 1 mm and smaller than or equal to 1.5 mm. The special blade for the cigar scissors or the cigar knife has the advantages that the surface smoothness of a grinding surface is high, the strength, the hardness, the wear resistance and the toughness are excellent, and enough cutting edge sharpness can be kept while high-fiber tobacco shreds are cut; the surface of the notch is smooth, so that the service life, the attractiveness and the use satisfaction degree of a user of the cigar knife or the cigar scissors can be remarkably improved.

Description

technical field [0001] The invention relates to the field of knife preparation, in particular to a method for preparing a special blade for cigar scissors or cigar cutters and the blade. Background technique [0002] As an important part of the current tobacco consumption, cigars are made of dried and fermented tobacco. They have the characteristics of high price, large diameter and long length of a single cigar, and high plant fiber content in tobacco leaf veins. Users It is often not possible to smoke the whole stick in a single puff, so after each puff, it is often necessary to use a professional cigar cutter or cigar to cut off the cigar head. Its appearance design, materials and accessories have been paid attention to, making it more beautiful and tasteful, and can better demonstrate the taste of cigars. Similarly, the price of cigar knives or cigar cutters is also expensive. [0003] At present, most of the common cigar cutters or cigar scissors on the market are made...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00A24F13/24C22C1/05C22C29/04C22C47/14C22C49/02C22C49/14
CPCB23P15/00A24F13/24C22C49/02C22C49/14C22C47/14C22C29/04C22C1/051
Inventor 杨成亮鲁攀单成潘辉刘毅邱嵩颜焰刘强
Owner CHENGDU MET CERAMIC ADVANCED MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap