Manufacturing method of large-diameter Gr12 titanium-molybdenum-nickel alloy seamless pipe

A technology for seamless pipes and manufacturing methods, which is applied in the field of manufacturing large-diameter Gr12 titanium-molybdenum-nickel alloy seamless pipes, can solve the problems of unguaranteed dimensional accuracy, poor product quality stability, and low production efficiency, and achieve production costs Low cost, stable product quality and high production efficiency

Pending Publication Date: 2022-04-05
安徽宝泰特种材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the processing of titanium-molybdenum-nickel alloy seamless pipes mainly adopts plate molding welding technology or extrusion forming technology, and the production method of large-diameter Gr12 titanium-molybdenum-nickel all

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] In order to facilitate the understanding of those skilled in the art, the present invention will be further described below with reference to specific embodiments.

[0022] A method for manufacturing a large-diameter Gr12 titanium-molybdenum-nickel alloy seamless pipe, comprising the following steps:

[0023] S1. Select high-quality sponge titanium and nickel-molybdenum alloy bags as raw materials, and mix the sponge titanium and nickel-molybdenum alloy bags according to the requirements, and produce ingots through secondary vacuum melting.

[0024] S2. The ingot in step S1 is forged into a square billet, and then subjected to blanking and surface grinding treatment in turn, and finally three upsetting and three drawing processes are performed, and die forging is made into a Gr.12 titanium-molybdenum-nickel alloy bar of φ114-φ720.

[0025] S3. Put the Gr.12 titanium-molybdenum-nickel alloy bar obtained in step S2 into an electric furnace for heating, keep the temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a manufacturing method of a large-diameter Gr12 titanium-molybdenum-nickel alloy seamless pipe, which adopts the steps of vacuum melting, three-time upsetting and three-time drawing, heating and perforating, reducing treatment, necking and drawing and the like, and the manufactured large-diameter Gr12 titanium-molybdenum-nickel alloy seamless pipe is better in inner and outer surface quality, excellent in mechanical property, favorable for ensuring the comprehensive performance of the product, high in product precision, high in yield, high in product quality and high in product quality. The product quality is stable, the production cost is low, and the production efficiency is high.

Description

technical field [0001] The invention relates to the technical field of metal products, in particular to a method for manufacturing large-diameter Gr12 titanium-molybdenum-nickel alloy seamless pipes. Background technique [0002] As a high-strength metal material, titanium-molybdenum-nickel alloy is widely used in petroleum pipelines, submarine pipelines, petrochemical, automobile industry, electronics industry and other industries. At present, the processing of titanium-molybdenum-nickel alloy seamless pipes mainly adopts plate molding welding technology or extrusion forming technology, and the production method of large-diameter Gr12 titanium-molybdenum-nickel alloy seamless pipes with cross-rolling and perforation technology is not yet mature. , the production cost is high, the dimensional accuracy cannot be guaranteed, the product quality stability is poor, and the production efficiency is low. Contents of the invention [0003] The object of the present invention is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21C37/06C21D8/10C21D9/08C21D1/26C22F1/18
Inventor 李贤泉孙建芮天安杨根荣翟皓周雄杰王超张贝
Owner 安徽宝泰特种材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap