Artificial quartz stone plate for decorating wall surface as well as preparation method and application of artificial quartz stone plate

A technology of artificial quartz stone and plate, which is applied in the field of artificial quartz stone plate for decorative wall and its preparation, can solve the problems that the quartz stone plate has no pattern and cannot be directly applied to decorative wall construction, etc., so as to improve hardness and increase insulation thermal effect

Inactive Publication Date: 2022-04-15
GUANGDONG BANNER NEW MATERIAL TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the surface of the existing quartz stone plate has no pattern, and the change is mainly concentrated on the color, so it cannot be directly applied to the construction of the decorative wall.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Artificial quartz stone plate for decorating wall surface as well as preparation method and application of artificial quartz stone plate
  • Artificial quartz stone plate for decorating wall surface as well as preparation method and application of artificial quartz stone plate
  • Artificial quartz stone plate for decorating wall surface as well as preparation method and application of artificial quartz stone plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] Composition of raw materials: 207.98 kg of quartz sand with a maximum particle size of less than 1000 microns, 18.06 kg of organic fluorine water-based leveling agent, 1.17 kg of hollow glass beads, antioxidant tetrakis [β-(3,5-di-tert-butyl-4-hydroxy 0.87 kg of phenyl) propionic acid] pentaerythritol ester, 0.36 kg of plasticizer triacetin, 0.05 kg of naphthalenesulfonate water reducer FDN, 0.54 kg of nano silicon dioxide; these raw materials are prepared by the following preparation process of quartz stone slab.

[0083] Put the above-mentioned organic fluorine water-based leveling agent, filler, antioxidant and nano-silica into the container, disperse evenly under ultrasonic vibration, and finally add the additive 2-5 minutes before putting the leveling agent mixture into the quartz sand. The plasticizer and the water reducer are stirred and mixed evenly to obtain a resin mixture. Put the above-mentioned quartz sand into the closed mixer and stir and mix evenly, the...

Embodiment 2

[0086] Composition of raw materials: 220.94 kg of quartz sand with a maximum particle size of less than 400 microns, 24.00 kg of organic fluorine water-based leveling agent, 1.28 kg of hollow glass beads, 0.88 kg of antioxidant 2,6-di-tert-butyl-4-methylphenol, 0.19 kg of plasticizer tert-butyl peroxy-2-ethylhexanoate, 0.06 kg of lignin-based water reducer MG, and 2.52 kg of nano silicon dioxide. These raw materials are prepared quartz stone plate according to the preparation process of Example 1, but there are the following differences: 0.72 kg of modified nano silicon dioxide is mixed with leveling agent, and the remaining 1.8 kg is mixed with quartz sand, and the closed mixer is stirred When the quartz sand is used, the stirring speed is increased by about 20%, the vacuum vibration is pressed for 240 seconds, and the temperature of the curing furnace is 85-90°C. According to the quartz stone plate prepared in this way, after testing, the water absorption rate is 0.01%, and ...

Embodiment 3

[0088] Composition of raw materials: 243.11 kg of quartz sand with a maximum particle size of less than 4500 microns, 24.72 kg of polyether modified polyorganosiloxane water-based leveling agent, 1.43 kg of hollow glass beads, antioxidant β-(3,5-di-tert-butyl 1.28 kg of octadecyl-4-hydroxyphenyl) propionate, 0.62 kg of epoxy tetrahydrophthalate dioctyl plasticizer, 0.1 kg of naphthalenesulfonate water reducer FDN, nano silicon dioxide 8.54 kg. Prepare these raw materials according to the preparation process of Example 1 to prepare quartz stone plates, but there are the following differences: 0.49 kg of nano silicon dioxide is mixed with leveling agent, and the remaining 8.05 kg is mixed with quartz sand, and the closed mixer is used to stir the quartz sand When the stirring speed is increased by about 40%, the vacuum vibration is pressed for 150 seconds. The quartz stone plate prepared in this way has a water absorption rate of 0.01% and a density of 2.48g / cm after testing. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an artificial quartz stone plate for decorating a wall surface as well as a preparation method and application of the artificial quartz stone plate. The artificial quartz stone plate comprises a plate layer and a pattern layer which are laminated together, wherein the plate layer comprises the following components in parts by weight: 100 parts of quartz sand, 0.01-25 parts of nano silicon dioxide and 3-25 parts of a flatting agent; 0.003 to 1.25 parts of a plasticizer and 0.01 to 3 parts of an antioxidant; the flatting agent is an organic fluorine water-based flatting agent or a polyether modified polysiloxane water-based flatting agent; and the antioxidant is tetrakis (beta-(3, 5-di-tert-butyl-4-hydroxyphenyl) propionic acid) pentaerythritol ester, 2, 6-di-tert-butyl-4-methylphenol, and beta-(3, 5-di-tert-butyl-4-hydroxyphenyl) octadecyl propionate. In this way, the hardness, strength, compactness, smoothness, impermeability and toughness of the quartzite plate can be improved.

Description

technical field [0001] The invention belongs to the technical field of artificial panels, in particular to an artificial quartz stone panel for decorative walls and a preparation method and application thereof. Background technique [0002] Artificial quartz stone is composed of more than 90% of natural quartz and about 10% of colorants, resins and other additives for adjusting bonding and curing. It is a plate processed by negative pressure vacuum, high-frequency vibration molding, and heating and curing (the temperature is determined by the production method according to the type of curing agent. Artificial quartz stones are suitable for places with high material requirements in the field of building materials such as floors and walls. [0003] However, the surface of the existing quartz stone plates has no patterns, and the changes mainly focus on the color, so it cannot be directly applied to the building construction of the decorative wall. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/02C04B111/20C04B111/27C04B111/54C04B111/80C04B111/82
Inventor 戴新张进罗刚陈振业
Owner GUANGDONG BANNER NEW MATERIAL TECH