A kind of molybdenum disulfide nano lubricating oil that can exist stably and preparation method thereof

A technology of molybdenum disulfide and lubricating oil, which is applied in the direction of lubricating composition and petroleum industry, which can solve the problems of poor suspension stability, complicated preparation process, aggregation, etc., and achieve the effects of low cost, simple preparation process and simple formula

Active Publication Date: 2022-08-09
DALIAN UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, the technical problem to be solved by the present invention is to provide a kind of stable molybdenum disulfide nano lubricating oil and its preparation method to solve the problem of existing MoS 2 Molybdenum disulfide in nano lubricating oil is prone to mutual adsorption and aggregation, poor suspension stability and complex preparation process, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of molybdenum disulfide nano lubricating oil that can exist stably and preparation method thereof
  • A kind of molybdenum disulfide nano lubricating oil that can exist stably and preparation method thereof
  • A kind of molybdenum disulfide nano lubricating oil that can exist stably and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] In this embodiment, the molybdenum disulfide nano lubricating oil that can exist stably is composed of molybdenum disulfide powder, a dispersant mixture and a base oil; in the molybdenum disulfide nano lubricating oil, the mass fraction of the dispersant mixture is 12wt%, The mass fraction of molybdenum disulfide powder is 0.5 wt%; the dispersant mixture is composed of oleic acid (Oleic acid, chemical formula C 18 H 34 O 2 ), oleylamine (Oleylamine, chemical formula C 18 H 37 N) and n-dodecanethiol (1-Dodecanethiol, chemical formula C 12 H 26 S) composition, the mass ratio of oleic acid, oleylamine and n-dodecanethiol is 1:2:1; the particle size of molybdenum disulfide powder is 50-200nm; the base oil is 32# base oil, which is industrial grade White oil.

[0039] The preparation method of the above-mentioned molybdenum disulfide nano lubricating oil that can exist stably comprises the steps:

[0040] Step A: 9g of oleic acid, 18g of oleylamine and 9g of n-dodecan...

Embodiment 2

[0049] In this embodiment, the molybdenum disulfide nano lubricating oil that can exist stably is composed of molybdenum disulfide powder, a dispersant mixture and a base oil; in the molybdenum disulfide nano lubricating oil, the mass fraction of the dispersant mixture is 12wt%, The mass fraction of molybdenum disulfide powder is 0.3wt%; the dispersant mixture is composed of oleic acid, (Oleic acid, chemical formula C 18 H 34 O 2 ), oleylamine (Oleylamine, chemical formula C 18 H 37 N) and n-dodecanethiol (1-Dodecanethiol, chemical formula C 12 H 26 S) composition, the mass ratio of oleic acid, oleylamine and n-dodecanethiol is 1:2:1; the particle size of molybdenum disulfide powder is 50-200nm; the base oil is 150# base oil, which is also industrial grade white oil.

[0050] The preparation method of the above-mentioned molybdenum disulfide nano lubricating oil that can exist stably comprises the steps:

[0051] Step A: 9g of oleic acid, 18g of oleylamine and 9g of n-d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a molybdenum disulfide nano lubricating oil that can exist stably and a preparation method thereof, wherein the molybdenum disulfide nano lubricating oil is composed of molybdenum disulfide powder, a dispersant mixture and a base oil; , the mass fraction of the dispersant mixed solution is 8-15 wt%, and the mass fraction of the molybdenum disulfide powder is 0.1-1.0 wt%; the preparation method comprises: adding the molybdenum disulfide powder into the dispersant mixed solution to obtain a mixed reaction system The mixed reaction system is heated and magnetically stirred, and after the reaction is finished, it is naturally cooled to obtain a dispersant modified molybdenum disulfide mixed solution; the dispersant modified modified molybdenum disulfide mixed solution is mixed with the base oil, and Perform ultrasonic dispersion treatment to obtain molybdenum disulfide nano lubricating oil. MoS of the present invention 2 Nano-lubricating oil can exist stably, and can significantly reduce the wear scar diameter under extreme pressure conditions, significantly improving the lubricating properties of the base oil.

Description

technical field [0001] The present invention relates to the technical field of nano lubricating oil. Specifically, a molybdenum disulfide nano lubricating oil that can exist stably and a preparation method thereof are provided. Background technique [0002] Existing research shows that nano-lubricating oil has excellent extreme pressure performance and anti-wear and anti-friction performance compared with base oil, and has higher bearing capacity and lubricating performance under high temperature, heavy load and other conditions, and nanoparticles can repair factors. The local peaks contact the furrows created, thereby improving the flatness of the surface. Molybdenum disulfide (MoS 2 ) is similar to graphene, both have obvious layered structure, and the lubricating properties of molybdenum disulfide depend on its own special crystal structure, and its layers are only connected by weak van der Waals force, showing the characteristics of easy shearing . The layer of molyb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/04C10N30/04C10N30/06
CPCC10M169/04C10M2201/066C10M2201/14C10M2207/126C10M2215/04C10M2219/082C10M2203/1006C10N2030/04C10N2030/06C10N2020/06C10N2020/02
Inventor 胡成志易昌利白敏丽李晓杰唐大伟
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com