Toner with good fixing effect in low-temperature environment and preparation process thereof

A technology of low temperature environment and preparation process, applied in the direction of developer, instrument, optics, etc., can solve the problems of fixing effect influence and influence, achieve the effect of lowering melting point and improving low temperature fixing effect

Pending Publication Date: 2022-08-05
福建美宏科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ceramic heater is a technological product in recent years, and some models are not equipped with a ceramic heater, so the models without a ceramic heater still cannot solve the problem that the low temperature has a great influence on the fixing effect
The melting temperature of most toners is around 100°C. In order to ensure a good fixing effect, the copier needs to be preheated for 1-2 minutes to make the heating roller reach 185°C, which will obviously affect some urgent printing. users who need

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further illustrated by specific embodiments below.

[0024] A toner with good low-temperature environment fixing effect, the toner is composed of the following components: polyester resin, low-temperature polyester resin, pigment, surface modifier, charge regulator and wax, wherein the components of the toner are The parts by weight are: 80 parts of polyester resin, 1 part of low temperature polyester resin, 3 parts of pigment, 1 part of surface modifier, 1 part of charge regulator, and 8 parts of wax.

[0025] Further, the polyester resin is a copolymer of styrene monomer and acrylate, a copolymer of styrene monomer and methacrylate, vinyl polymer and its copolymer, styrene copolymer, Polyvinyl ether, polyvinyl ketone, polyetheramine, polyurethane, rubber, epoxy resin, polyvinyl butyral rosin, denatured rosin, phenolic resin, polyester (saturated polyester resin, unsaturated polyester resin, benzene One or more of propylene-polyester copo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses powdered ink with a good fixing effect in a low-temperature environment, and the powdered ink is prepared from the following components in parts by weight: 70 to 95 parts of polyester resin, 1 to 2 parts of low-temperature polyester resin, 1 to 10 parts of pigment, 0.1 to 5 parts of surface modifier, 0.1 to 5 parts of charge control agent and 0.1 to 5 parts of wax. 0.5-5 parts of a charge control agent and 1-10 parts of wax. The invention also discloses a preparation process of the powdered ink with the good fixing effect in the low-temperature environment. Through a surface modification mode, the surface characteristics of the toner are changed, so that the toner can be smoothly fused and fixed in a low-temperature state, and the technical effect of stable handwriting is realized, thereby improving the fixing effect of the existing toner in the low-temperature state.

Description

technical field [0001] The invention relates to the field of preparation and production of toner, more specifically to a toner with good fixing effect in a low temperature environment and a preparation process thereof. Background technique [0002] In the existing laser color copiers, the melted toner is immersed into the printing paper by means of pressurized hot-melt to complete the final fixing. The low temperature environment will make the printer's fusing components unable to reach the working temperature, which will result in poor fusing, prolong the paper output time on the first page, and in severe cases, the toner cartridge sealing material may collapse and leak powder. At present, the mainstream solutions on the market are fixing by using more advanced ceramic heaters (PCT). However, ceramic heaters are a technological product in recent years. Some models are not equipped with ceramic heaters. Therefore, models without ceramic heaters still cannot solve the proble...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03G9/08G03G9/087G03G9/097G03G9/09
CPCG03G9/08G03G9/08755G03G9/09733G03G9/08782G03G9/09G03G9/0808
Inventor 汤若狮黄晓玲
Owner 福建美宏科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products