Magneto-optical recording target material and its preparing process

A magneto-optical recording and production process technology, which is applied in magnetic recording, data recording, recording information storage, etc., can solve the problems of non-centralized research and variable alloy composition

Inactive Publication Date: 2004-09-01
SOUTHWEST JIAOTONG UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are few studies on this aspect, and most of the doping is to improve the oxidation resistance and corrosion resistance of materials. There are many studies on diversified alloys, but the alloy composition changes, and there is no centralized research.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magneto-optical recording target material and its preparing process
  • Magneto-optical recording target material and its preparing process
  • Magneto-optical recording target material and its preparing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] specific implementation plan

[0013] The process of preparing the magneto-optical target is as follows:

[0014] Process 1 Raw material treatment and batching: chemically treat the surface of industrial pure iron, then refine terbium, light rare earth, and iron in a magnetic suspension furnace; at the same time, carry out appropriate surface treatment on cobalt; finally, batching under the protection of inert gas ; The ingredient elements and components of various targets are consistent with the above-mentioned composite targets. The base target alloy is smelted by magnetic levitation technology, and the alloy composition of the base target 1 is iron-cobalt (FeCo) alloy. Cut pure terbium 2 (Tb) and light rare earth 3 (LRE) wires into segments or disks, and symmetrically inlay them in the circular area with the largest etching of the iron-cobalt alloy-based target 1 to make a composite target, such as figure 1 with figure 2 As shown, the composition of the target ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A target material for magneto-optical record (optical disk or magneto-optical disk) is based on the principle that the light- or medium-weight rare-earth elements have high saturation magnetization intensity, magnetocrystalline anisotropy and magneto-optical effect. It is prepared through magnetic suspension smelting of FeCo alloy as basic target alloy, linearly cutting the pure terbium and light-weight rare-earth element to obtain sectorial or circular sheets, symmetrically inlaying them on said basic target. Its advantages are high uniformity, low cost and high efficiency.

Description

[0001] Field [0002] The invention belongs to the technical field of manufacturing optical discs and magneto-optical discs. Background technique [0003] Information storage technology is the backbone of all high-tech fields. With the astonishing increase in the amount of information, it is imperative to research and develop large-capacity storage and retrieval systems. Due to the advantages of high storage density, fast data transmission, and long storage life, optical discs have been rapidly developed as external storage devices for computers. However, optical discs can only be burned once, and cannot be rewritten and reused like magnetic storage. It is suitable for for long-term data storage. The disk can be erased and written repeatedly, but the storage capacity is small. It is in this situation that magneto-optical disks become a new generation of optical disks. Compared with optical disks and magnetic disks, they not only have the advantages of high density and large ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G11B5/62G11B5/84
Inventor 张喜燕周世杰刘志农
Owner SOUTHWEST JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com