Dust-preventing tension-increasing additive for wet part

A wet-end additive and tensile technology, which is applied in the direction of non-fiber pulp addition, textile and papermaking, fiber raw material processing, etc., can solve the problems of flying fine paper fibers, low economic benefits, and high proportion of short fibers

Inactive Publication Date: 2005-05-25
冯 世荣 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As we all know, in the papermaking process, the recovery rate of pulp is a crucial issue, especially in the recycling process of waste paper, the proportion of short fibers is relatively high, and in the process of cooking and pulping, the loss of paper...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Prepare materials according to the following components and weights:

[0019] Polyvinyl alcohol 4kg Trisodium phosphate 8kg

[0020] Sodium metasilicate 6kg Modified starch 20kg

[0021] Dextrin 6kg Yuanmingfen 22kg

[0022] Aluminum sulfate 3kg Acrylate 6kg

[0023] Sodium carboxymethyl cellulose 8kg Rosin gum 5kg

[0024] Preparation method: Grind polyvinyl alcohol to 100 mesh, mix with sodium sulfate, sodium carboxymethyl cellulose, add modified starch, dextrin, acrylate, rosin gum and mix evenly, then add sodium metasilicate After mixing evenly, pack it.

Embodiment 2

[0026] Polyvinyl alcohol 5kg Trisodium phosphate 9kg

[0027] Sodium metasilicate 4kg Modified starch 23kg

[0028] Dextrin 7kg Yuanmingfen 16kg

[0029] Aluminum sulfate 3.5kg Acrylate 7kg

[0030] Sodium Carboxymethyl Cellulose 6kg Rosin Gum 4kg

[0031] Preparation method: Grind polyvinyl alcohol to 120 mesh, mix with sodium sulfate, sodium carboxymethyl cellulose, add modified starch, dextrin, acrylate, rosin gum and mix evenly, then add sodium metasilicate After mixing evenly, pack it.

Embodiment 3

[0033] Polyvinyl alcohol 6kg Trisodium phosphate 6kg

[0034] Sodium metasilicate 5kg Modified starch 25kg

[0035] Dextrin 5kg Yuanmingfen 20kg

[0036] Aluminum sulfate 4kg Acrylate 5kg

[0037] Sodium Carboxymethyl Cellulose 7kg Rosin Gum 6kg

[0038] Preparation method: Grind polyvinyl alcohol to 80 mesh, mix with sodium sulfate, sodium carboxymethyl cellulose, add modified starch, dextrin, acrylate, rosin gum and mix evenly, then add sodium metasilicate After mixing evenly, pack it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a dust-proof tensile wet end additive, which contains the following components: polyvinyl alcohol 4-6, trisodium phosphate 6-9, sodium metasilicate 4-6, modified starch 20-25, dextrin 5- 7. Yuanming powder 16-22, aluminum sulfate 3-4, acrylate 5-7, carboxymethyl cellulose sodium 6-8, rosin gum 4-6, this additive can increase the fiber recovery rate by 20-36%, improve Paper tension 16-25%, reduce cost 22-32%.

Description

technical field [0001] The invention relates to an additive for papermaking, in particular to a dustproof tensile wet end additive. technical background [0002] As we all know, in the papermaking process, the recovery rate of pulp is a crucial issue, especially in the recycling process of waste paper, the proportion of short fibers is relatively high, and in the process of cooking and pulping, the loss of paper fibers is large, which is harmful to the environment. Large, low paper output, and high proportion of short fibers will easily reduce the quality of paper, flying fine paper fibers, low tensile strength, low economic benefits, so far, there is no good solution. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, to provide a paper-making dust-proof tensile strength that can improve the recovery rate of paper fibers, increase the tensile strength, smoothness and softness of paper, reduce the flyin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H21/14
Inventor 冯世荣刘永焰
Owner 冯 世荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap