Prepn process of RE nano oxide

A nano-oxide and rare-earth oxide technology, which is applied in the field of preparation of rare-earth nano-oxides, can solve problems such as being unsuitable for the preparation of high-purity rare-earth oxide nano-powders, and achieve fine particle size, uniform particle size, and simple operation. Effect

Inactive Publication Date: 2003-05-14
CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method is not suitable for the preparation of high-purity rare earth oxide ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Embodiment 1: get 1mol / L Y 3+ 300ml of nitric acid solution, diluted with water to 1000ml, heated to 60°C, added 0.1% sodium dodecylbenzenesulfonate (DBS), stirred and mixed, weighed 118.5g of sodium bicarbonate, dissolved in 3000ml of water, the concentration of the solution was 0.5mol, add dropwise to Y at a speed of 40ml / min under constant stirring 3+ in the nitric acid solution until the addition is complete. Filter quickly, wash with water at 30°C until neutral, dry the precipitate at 100-110°C, raise the temperature to 800°C for 3 hours, and generate nano-Y 2 o 3 , the particle size is less than 40nm, and the specific surface area is 20-40m 2 / g.

Embodiment 2

[0009] Embodiment 2: get 1mol / L La 3+ 200ml of hydrochloric acid solution, diluted with water to 1000ml, heated to 30°C, added 0.1% sodium dodecylbenzenesulfonate (DBS), stirred and mixed, prepared ammonium bicarbonate aqueous solution, the solution concentration was 0.5mol, and was stirred continuously Add dropwise to La at a speed of 10ml / min 3+ hydrochloric acid solution until the addition is complete. Filter quickly, wash with water at 30°C until neutral, dry the precipitate at 100-110°C, raise the temperature to 900°C for 2 hours, and generate nano-La 2 o 3 , the particle size is less than 40nm, and the specific surface area is 20-40m 2 / g.

Embodiment 3

[0010] Embodiment 3: get 1mol / L Ce 3+ 100ml of nitric acid solution, diluted with water to 1000ml, heated to 40°C, added 0.1% fatty alcohol polyoxyethylene ether (AE), stirred and mixed, prepared ammonium bicarbonate aqueous solution, the solution concentration was 0.5mol, and mixed with 20ml / min speed drops to Ce 3+ in the nitric acid solution until the addition is complete. Filter quickly, wash with water at 30°C until neutral, dry the precipitate at 100-110°C, raise the temperature to 800°C for 2 hours, and generate nano-CeO 2 , the particle size is less than 40nm, and the specific surface area is 20-40m 2 / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Nano RE oxide is prepared through the process of: selecting single RE oxide R2O3, where R is La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Y and Sc, or their mixture as raw material; dissolving in water solution of nitric acid or hydrochloric acid to reach a RE ion density of 0.1-0.4 mol/L; heating to 30-80 deg.c; adding dispersant sodium dodecyl benzenesulfonate, polyoxyethylenated alcohol, SPAN-80 or Tween-80 and precipitant to form RE carbonate precipitate; filtering, drying, and heating to 700-900 deg.c to obtain single or mixed nano RE oxide. The nano RE oxide has grain size smaller than 40 nm and specific surface area of 20-40 sq m/g.

Description

technical field [0001] The invention relates to a preparation method of rare earth nano oxides. Background technique [0002] The nanometerization of materials will endow materials with many characteristics different from macroscopic substances, which has important application value and will cause a new technological revolution. There are many reports on the preparation methods of rare earth nano-oxides, such as hydrolysis method, alkoxide method, thermal decomposition method, explosion method, homogeneous precipitation method, complex precipitation method, and sol-gel method. Most of the methods are feasible for the preparation and characterization of rare earth nanoparticles, but the industrial production is not yet mature. The present invention will provide a preparation method of rare earth nano oxides that can be industrialized. [0003] Japanese patent JP-6464-4H (1985) and Wang Zenglin et al. used rare earth oxalate as the substrate, and decomposed the oxalate into r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01F17/00C04B35/50C04B35/624
Inventor 洪广言于德才郭宝金
Owner CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap