High decorative texture antibacterial powdered paint and its manufacturing method

An antibacterial powder and texture technology, which is applied in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problem that high decorative texture agents and antibacterial agents have not been found, and antibacterial agents are difficult to integrate, and the surface of decorative texture powder coatings is uneven. equality issue

Inactive Publication Date: 2004-05-05
SHANGHAI CHANGJIANG CHEM
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the surface of the decorative textured powder coating is uneven, especially the high decorative textured powder coating, which is easy to breed bacteria and difficult to integrate with antibacterial agents
Therefore, no powder coating literature reports containing high decorative texture agent and antibacterial agent have been found so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Prepare raw materials according to the following ingredients and proportions:

[0023] Epoxy 70%

[0024] Substitute dicyandiamide 3.5%

[0025] Leveling agent (polyacrylic acid) 1%

[0026] Texturizer 1%

[0027] Barium Sulfate 15%

[0028] Calcium Carbonate 7%

[0029] Benzoin 0.5%

[0030] Brightening agent 0.5%

[0031] Nano antibacterial agent 0.5%

[0032] Metallic pigment (copper gold powder) 1%

[0033] Mix and disperse the above raw materials at room temperature at high speed for 5 minutes. The mixed materials are melted and extruded through a high-temperature extruder (the temperature in the first zone is 70°C, and the temperature in the second zone is 100°C). After cooling, tableting and primary crushing, the primary crushing The materials are finely pulverized at room temperature < 25°C, and sieved through a 140-mesh sieve.

[0034] The finished powder coating is sprayed with a high-voltage electrostatic spray gun, coated on the treated metal sample...

Embodiment 2

[0036] Prepare raw materials according to the following ingredients and proportions:

[0037] Epoxy 37%

[0038] Polyester resin 37%

[0039] Texturizer 3%

[0040] Barium Sulfate 13%

[0041] Calcium Carbonate 7%

[0042] Benzoin 0.5%

[0043] Brightening agent 0.5%

[0044] Nano antibacterial agent 1%

[0045] Metal pigment (aluminum powder) 0.5%

[0046] Mix and disperse the above raw materials at room temperature for 3 minutes at high speed. The mixed materials are melted and extruded through a high-temperature extruder (the temperature in the first zone is 80°C, and the temperature in the second zone is 110°C). After cooling, tableting and primary crushing, the primary crushing The materials are finely pulverized at room temperature < 25°C, and sieved through a 140-mesh sieve.

[0047] The finished powder coating is sprayed with a high-voltage electrostatic spray gun, coated on the treated metal sample, and after being baked at 180-200°C / 10-20min to form a film, t...

Embodiment 3

[0049] Prepare raw materials according to the following ingredients and proportions:

[0050] Polyester resin 76%

[0051] TGIC 5.7%

[0052] Texturizer 0.8%

[0053] Barium Sulfate 12%

[0054] Benzoin 0.5%

[0055] Nano antibacterial agent 2%

[0056] Metal pigment (aluminum powder) 3%

[0057]Mix and disperse the above raw materials at room temperature at high speed for 5 minutes, melt and extrude the mixed materials through a high-temperature extruder (the temperature in the first zone is 75°C, and the temperature in the second zone is 120°C), after cooling, tableting and primary crushing, the primary The pulverized material is finely pulverized at room temperature < 25°C, and sieved through a 140-mesh sieve.

[0058] The finished powder coating is sprayed with a high-voltage electrostatic spray gun, coated on the treated metal sample, and after being baked at 180-200°C / 10-20min to form a film, the antibacterial test of the coating film is carried out, and its antiba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

An antibacterial powder paint able to generate decorative vein is prepared from thermosetting resin, nano-class antibacterial 0.1-3 wt.% agent, vein generating agent 0.5-5 wt.% and metallic pigment through proportionally high-speed mixing for 3-5 min, high-temp extruding out, cooling, pressing, breaking, pulverizing and sieving by 140 meshes. Its advantages are high antibacterial power and high decorative effect.

Description

technical field [0001] The invention relates to an antibacterial powder coating and a manufacturing method thereof, in particular to a powder coating with high decorative texture and antibacterial performance and a manufacturing method thereof. Background technique [0002] Electrostatic spraying and other processes are used to spray thermosetting powder coatings such as polyester on the metal surface, which not only makes the surface of the workpiece smooth and beautiful, but also a coating process with less pollution. Compared with ordinary coatings, it has more development prospects. However, the metal surface coated with powder coating is still unavoidably affected by harmful microorganisms such as bacteria and molds. For example, refrigerators, freezers, dishwashers, shells of washing machines, kitchen cabinets, food racks in stores and other places that are often in contact with water will multiply bacteria and mold when the temperature is suitable; food processing wor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/03C09D133/02C09D163/00C09D167/00C09D175/04
Inventor 陆耀祥顾若楠
Owner SHANGHAI CHANGJIANG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com