Water-soluble acroleic-acid modified epoxy ester anti-rast paint

A water-soluble acrylic and epoxy ester technology, applied in the field of paints, can solve the problems of poor storage stability, unsatisfactory anti-rust performance, general anti-rust performance, etc., and achieve excellent anti-corrosion performance, excellent protective performance and decorative effect. Effect

Inactive Publication Date: 2005-07-20
重庆亿隆涂料股份有限公司
View PDF0 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The former has poor storage stability and unsatisfactory anti-rust performance; the latter is a drying-type anti-rust paint, and its drying conditions are generally above 140 ° C for 30 minutes, and the energy consumption is high; its anti-rust performance is very general, and salt spray There are few varieties that have been tested for 300 hours

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A color paste part (black anti-rust paste): (%)

[0035] Soft Carbon Black 2.0

[0036] Iron Oxide Black 12.0

[0037] Complex zinc phosphate 7.6

[0038] Kaolin 10.0

[0039] Water-soluble acrylic modified epoxy ester resin (50%) 54.0

[0040] Dispersant 0.4

[0041] Defoamer 0.3

[0042] Corrosion inhibitor 0.4

[0043] Drier 0.3

[0044]Cosolvent 4.0

[0045] Neutralizer 5.0

[0046] Deionized water 4.0

[0047] Total: 100.0

[0048] B paint part (black anti-rust paint): (%)

[0049] Black antirust paste 76.4

[0050] Water-soluble acrylic modified epoxy ester resin (50%) 19.0

[0051] 717 amino resin 4.0

[0052] Thickener 0.3

[0053] Antifoam 0,3

[0054] Total 100.0

[0055] C preparation method: use a vertical ball mill or a sand mill to grind the color paste to a fineness below 35um. When mixing the paint, you can use a paint mixing machine...

Embodiment 2

[0057] A color paste part (iron red anti-rust paste): (%)

[0058] Iron Oxide Red 15.0

[0059] Zinc phosphate 7.0

[0060] Talc 5.0

[0061] Kaolin 5.0

[0062] Water-soluble acrylic modified epoxy ester resin (50%) 50.0

[0063] Dispersant 0.3

[0064] Defoamer 0.4

[0065] Corrosion inhibitor 0.3

[0066] Drier 0.2

[0067] Co-solvent 6.5

[0068] Neutralizer 5.0

[0069] Deionized water 5.3

[0070] Total: 100.0

[0071] B paint part (iron red anti-rust paint): (%)

[0072] Iron red antirust paste 76.0

[0073] Water-soluble acrylic modified epoxy ester resin (50%) 20.0

[0074] Cymel325 amino resin 3.5

[0075] Thickener 0.2

[0076] Antifoam 0,3

[0077] Total 100.0

[0078] C preparation method: same as Example 1.

Embodiment 3

[0080] A color paste part (light gray anti-rust paste): (%)

[0081] Titanium dioxide 14.8

[0082] Soft carbon black 0.2

[0083] Aluminum tripolyphosphate 7.7

[0084] Kaolin 9.5

[0085] Water-soluble acrylic modified epoxy ester resin (50%) 51.0

[0086] Dispersant 0.3

[0087] Defoamer 0.2

[0088] Corrosion inhibitor 0.3

[0089] Drier 0.1

[0090] Cosolvent 5.0

[0091] Neutralizer 5.5

[0092] Deionized water 5.4

[0093] Total: 100.0

[0094] B paint part (light gray anti-rust paint): (%)

[0095] Light gray antirust paste 74.0

[0096] Water-soluble acrylic modified epoxy ester resin (50%) 21.0

[0097] MR-625 amino resin 4.5

[0098] Thickener 0.3

[0099] Antifoam 0,2

[0100] Total 100.0

[0101] C preparation method is the same as example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to one kind of water soluble acrylic acid modified antirust epoxy resin paint. The modified antirust epoxy resin paint includes water soluble acrylic acid modified epoxy resin 45.0-62.0 wt%, water soluble amino resin 3.0-6.0 wt%, coloring pigment 5.0-15.0 wt%, antirust pigment 6.0-10.0 wt% and stuffing 5.0-10.0 wt%, and it contains also neutralizing agent, co-solvent, dispersant, defoaming agent, thickener, corrosion inhibitor, drying promoter and deionized water. The modified antirust epoxy resin paint contains no organic solvent and harmful lead and chromium compound, has no hazard of burning, explosion, poisoning and polluting environment, and has excellent protecting performance and decoration effect.

Description

technical field [0001] The invention belongs to the technical field of paints, and in particular relates to a water-soluble anti-corrosion coating mainly used for iron and steel products, especially suitable for the protective and decorative coating of traffic vehicles, engineering machinery, household appliances and steel furniture manufacturing industries, etc. Acrylic modified epoxy ester antirust paint. Background technique [0002] Traditional antirust paints are mostly solvent-based paints, which contain harmful organic solvents such as benzene, pollute the air and damage human health. At the same time, most of these paint products contain lead and chromium pigments, which will also cause environmental pollution and endanger human health. In recent years, some varieties of water-based anti-rust paints have also appeared. There are mainly two types, namely latex type and water-soluble type. The former has poor storage stability and unsatisfactory anti-rust performance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/08C09D163/10
Inventor 刘恩林孟建军
Owner 重庆亿隆涂料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com