Reduction-reducing crack-resisting concrete superplasticizer of graft copolymer and method for preparing the same

A technology of graft copolymer and superplasticizer, which is applied in the field of concrete structure and concrete engineering, and concrete admixture, and can solve problems such as high price, poor cement dispersion performance, and insufficient water reducing rate.

Active Publication Date: 2006-10-11
JIANGSU SOBUTE NEW MATERIALS
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] To sum up, there are still obvious deficiencies in multifunctional admixtures. These products basically use α-allyl alcohol ω-methyl polyether as the main raw material, and the price is relatively high. At the same time, α-allyl alcohol Alcohol omega-methyl polyether-maleic anhydride copolymer has poor dispersibility to cement and insufficient water reducing rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reduction-reducing crack-resisting concrete superplasticizer of graft copolymer and method for preparing the same
  • Reduction-reducing crack-resisting concrete superplasticizer of graft copolymer and method for preparing the same
  • Reduction-reducing crack-resisting concrete superplasticizer of graft copolymer and method for preparing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] In the 2000ml glass reactor equipped with thermometer, stirrer, dropping funnel, nitrogen inlet tube and reflux condenser, add 600ml ethyl acetate, purging reaction vessel with nitrogen while stirring, and be warming up to 75 ℃. Then 1.0mol monomer a-1, 0.35mol monomer b-1 (n=9) and 0.2mol monomer c-1 (p=2, q=2, M 2 =H), 0.15mol monomer d-1 (m=12) and 0.05mol styrene, 0.027mol azobisisobutyronitrile (AIBN), 8.5g mercaptopropionic acid, also add 200ml ethyl acetate simultaneously, and stir Prepare a uniform monomer aqueous solution, add it dropwise to the reactor, the dropping time is 3h, keep warm for 4h after the dropwise addition, and then heat up to recover the ethyl acetate organic solution, which can be used multiple times, add water to dilute and cool, and add alkali Neutralize to pH 7.5 to obtain a brown transparent liquid with a solid content of 30.7% and a molecular weight of 42,000.

Embodiment 2

[0081] In the 2000ml glass reactor equipped with thermometer, stirrer, dropping funnel, nitrogen inlet tube and reflux condenser, add 600ml ethyl acetate, purging reaction vessel with nitrogen while stirring, and be warming up to 75 ℃. Then 1.0 mol of monomer a-1, 0.20 mol of monomer b-2 (n=17) and 0.15 mol of monomer c-3 (p=4, q=0, M 2 =H) and 0.15mol monomer d-1 (m=12), 0.040mol azobisisobutyronitrile (AIBN), 10.2g mercaptopropionic acid, also add 200ml ethyl acetate simultaneously, and stir to make uniform mono Aqueous aqueous solution, drop it into the reactor, dropwise time is 5h, heat preservation reaction for 3h after dropwise addition, then heat up to recover ethyl acetate organic solution, can be used multiple times, add water to dilute and cool, and add alkali to neutralize to pH value 7.5, the solid content is 30.2% brown transparent liquid, the molecular weight is 29,000.

Embodiment 3

[0083] In the 2000ml glass reactor equipped with thermometer, stirrer, dropping funnel, nitrogen inlet tube and reflux condenser, add 800ml ethyl acetate, purging reaction vessel with nitrogen while stirring, and be warming up to 75 ℃. Then 1.0 mol of monomer a-1, 0.45 mol of monomer b-3 (n=5) and 0.25 mol of monomer c-2 (p=0, q=2, M 2 =H) and 0.20mol of monomer d-2 (m=6), and 0.05mol of styrene, 0.05mol of azobisisobutyronitrile (AIBN), 3.0g of mercaptopropionic acid, while also adding 400ml of ethyl acetate, and Stir to make a homogeneous monomer aqueous solution, add it dropwise to the reactor, the dropwise addition time is 4h, keep warm for 4h after the dropwise addition, then heat up to recover the ethyl acetate organic solution, which can be used multiple times, add water to cool, and add alkali Neutralized to pH 7.5, solid content 30.2% brown transparent liquid, molecular weight 35,000.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is a shrinkage-reduction anti-cracking type grafted copolymer concrete superplasticiser, which is prepared from monomer a of acroleic acid or salts, monomer b of alkoxy polyether monoacrylate, monomer c of maleic anhydride hemiester or its salts, monomer d of alpha-propenol omega-methyl polyether and monomer e of phenylethene through free radical copolymerization reaction, wherein the molar ratio of the monomer a, b, c, d and e being 1 : 0.2-0.5 : 0.10-0.25 : 0.10-0.20 : 0-0.10.

Description

technical field [0001] The invention belongs to the technical field of concrete structures and concrete engineering, in particular to the technical field of concrete admixtures, in particular to a preparation method and application of a shrinkage-reducing and crack-resistant polycarboxylate concrete superplasticizer. Background technique [0002] Concrete has developed into the most important structural engineering material in the contemporary era. In 2005, my country's annual cement output exceeded 1 billion tons. The amount of cement and concrete consumed by its infrastructure construction is in the leading position in the world. The production of cement not only consumes a lot of mineral resources and energy, and produces a large amount of CO 2 , emitting a large amount of dust. The sustainable development of the building materials industry is to reduce resources and energy consumption as much as possible in the use of raw materials and the production process of materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/24C04B103/32
Inventor 缪昌文冉千平刘加平周静
Owner JIANGSU SOBUTE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap