Aqueous dispersion, method for producing same, and method for bonding shaped article made of ethylene-alpha-olefin copolymer

A water-based dispersant and bonding method technology, which is applied in the direction of monocarboxylate copolymer adhesives, adhesive types, surface pretreatment bonding methods, etc., can solve problems such as difficult to achieve adhesion, Achieve the effect of improving mechanical stability and storage stability, good stability and high adhesion

Active Publication Date: 2007-01-10
MITSUI CHEM INC
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] However, although the adhesive composition described in Patent Document 2 or the aqueous emulsion composition described in Patent Document 3 exhibits high adhesive strength to molded articles composed of highly polar copolymers such as ethylene / vinyl acetate copolymers, for example, , it is difficult to achieve sufficient adhesion to low-polarity moldings such as ethylene / α-olefin copolymers described in Patent Document 1

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous dispersion, method for producing same, and method for bonding shaped article made of ethylene-alpha-olefin copolymer
  • Aqueous dispersion, method for producing same, and method for bonding shaped article made of ethylene-alpha-olefin copolymer
  • Aqueous dispersion, method for producing same, and method for bonding shaped article made of ethylene-alpha-olefin copolymer

Examples

Experimental program
Comparison scheme
Effect test

manufacture example

[0214] 100 parts by weight of the ethylene / 1-butene copolymer obtained in Preparation Example (2) above, 0.5 parts by weight of dicumyl peroxide (DCP), and 0.35 parts by weight (TAIC conversion value) of tripropenyl isocyanide Ornithyl ester (TAIC) (trade name: M-60 (TAIC content: 60% by weight) (manufactured by Nippon Chemicals Co., Ltd.)), 7 parts by weight of dicarboxylamine nitride and 10 parts by weight of talc powder The mixture was kneaded on a roll having a roll surface temperature of 100° C. for 10 minutes to form a thin plate.

[0215] Then the thin plate obtained is placed on the stamping die, at 150kg / cm 2 , 160° C., and pressure heating for 12 minutes to obtain a foamed molded product (thickness 24.5 mm, length 1500 mm, width 200 mm).

[0216] Example 1

[0217] Preparation of aqueous dispersant (aqueous emulsion composition)

[0218] With 5 parts by weight of ethylene / α-olefin copolymer (density: 862kg / m 3 , MFR: 1.2g / 10 minutes, trade name: TAFMER-DF610 (man...

Embodiment 2

[0235] In addition to replacing 5 parts by weight of ethylene / α-olefin copolymer (density: 862kg / m 3 , MFR: 1.2g / 10 minutes, trade name: TAFMER-DF610 (manufactured by Mitsui Chemicals)), using 5 parts by weight of ethylene / α-olefin copolymer (density: 885kg / m 3 , MFR: 1.2 g / 10 minutes, brand name: TAFMER-DF810 (manufactured by Mitsui Chemicals, Inc.)), the same operation as in Example 1 was performed to obtain an aqueous emulsion composition.

[0236]Using this aqueous emulsion composition, the cleaned foam molded article and the rubber sheet were adhered in the same manner as in Example 1, and the adhesive strength was measured. The results are shown in Table 1.

Embodiment 3

[0238] In addition to replacing 5 parts by weight of ethylene / α-olefin copolymer (density: 862kg / m 3 , MFR: 1.2g / 10 minutes, trade name: TAFMER-DF610 (manufactured by Mitsui Chemicals)), using 5 parts by weight of ethylene / α-olefin copolymer (density: 870kg / m 3 , MFR: 35g / 10 minutes, trade name: TAFMER-DF7350 (manufactured by Mitsui Chemicals Co., Ltd.), replace 40 parts by weight of turpentine (trade name: gumterebinthN (manufactured by YATUHARA Chemical Co., Ltd.)) and 20 parts by weight of turpentine An aqueous emulsion composition was obtained in the same manner as in Example 1 except for limonene (trade name: D limonene (manufactured by Yatuhara Chemical Co., Ltd.).

[0239] Using this aqueous emulsion composition, the cleaned foam molded article and the rubber sheet were adhered in the same manner as in Example 1, and the adhesive strength was measured. The results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

Disclosed is an aqueous dispersion containing (A) an ethylene-alpha-olefin copolymer, (B) a modified ethylene-vinyl acetate copolymer, (C) a photopolymerization initiator and (D) an ethylenically unsaturated monomer, and if necessary (E) an ethylene-vinyl acetate copolymer and (F) a nonaqueous organic solvent.

Description

technical field [0001] The present invention relates to an aqueous dispersant, an adhesive composition containing the same, or an adhesive composition such as a primer, and a method for adhering molded articles made of ethylene / α-olefin copolymers using the same. Background technique [0002] In many fields such as building interior and exterior decoration materials, automobile interior decoration materials or glass frames, packaging materials, daily necessities, etc., in order to obtain products with low specific gravity, light weight, softness and high mechanical strength, the technology of bridging foam is used . In order to reduce weight, only foaming the resin will cause a decrease in mechanical strength, but this bridging foam combines molecular chains through the bridging reaction of the resin, suppressing the decrease in mechanical strength, and achieving weight reduction through foaming. [0003] Shoes or clothing, such as the soles of sports shoes (mainly density ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F255/00C09J4/00C09J5/02C08F2/44B05D7/24B29C65/48B29K23/00C08F255/02C08L23/08C08L51/06C09J4/06C09J11/06C09J123/00C09J123/08C09J131/04
CPCC08F255/026C09J4/06B29C66/71C08L23/0853C09J123/0815C08L51/06C08F255/00C08L2666/06C08L2666/02C08F255/02C08J3/02
Inventor 松坂康弘白木宽之
Owner MITSUI CHEM INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com