Production of composite rubber track

A technology of compound rubber and manufacturing method, applied in household components, applications, household appliances, etc., can solve the problems of high tensile strength, poor sunlight crack resistance, environmental pollution, etc., and achieve good impact absorption performance and product return Good elasticity, the effect of non-toxic volatiles

Inactive Publication Date: 2007-06-20
浙江绿环工程机械有限公司
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional runway is made of rubber particles and polyurethane cast on site. Its flatness, compactness, wear resistance and aging resistance are not good, and it is easy to discolor, degranulate, and accumulate dust. The polyurethane component is polluting to the environment. and toxic volatilization
At present, there are also composite r...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0014] Example 1, (1) First take by weight 20 parts of neoprene, 30 parts of natural rubber, 50 parts of EPDM, 20 parts of white carbon black, 40 parts of clay, 5 parts of zinc oxide, stearin 2 parts of acid, 8 parts of naphthenic oil, 8 parts of dizinc ester, 2 parts of antioxidant, 0.5 part of ultraviolet absorber, 2 parts of accelerator NS, 1.5 parts of accelerator ETU, 1.5 parts of sulfur, flame retardant chlorinated paraffin 15 parts, flame retardant decabromodiphenyl ether 30 parts, vulcanized rubber powder 50 parts.

[0015] (2) cutting raw rubber into small pieces;

[0016] (3) All materials are mixed in an internal mixer, the mixing temperature is 80-120°C, the mixing time is 10min, and the glue is removed at 120°C;

[0017] (4) Press the mixed rubber into tablets, apply a release agent and park for 12 hours;

[0018] (5) Put the parked rubber into the 18-inch open mill to add vulcanization and produce sheets for later use;

[0019] (6) Lay the fabric and the recla...

example 2

[0022] Example 2, (1) First take by weight 30 parts of neoprene, 25 parts of natural rubber, 45 parts of EPDM, 25 parts of white carbon black, 35 parts of clay, 5 parts of zinc oxide, stearin 1.5 parts of acid, 10 parts of naphthenic oil, 6 parts of dizinc ester, 2.5 parts of antioxidant, 0.8 part of ultraviolet absorber, 2.5 parts of accelerator NS, 2 parts of accelerator ETU, 1.6 parts of sulfur, flame retardant chlorinated paraffin 18 parts, flame retardant decabromodiphenyl ether 35 parts, vulcanized rubber powder 40 parts.

[0023] (2) cutting raw rubber into small pieces;

[0024] (3) All materials are mixed in an internal mixer, the mixing temperature is 80-120°C, the mixing time is 10min, and the glue is removed at 120°C;

[0025] (4) Press the mixed rubber into tablets, apply a release agent and park for 12 hours;

[0026] (5) Put the parked rubber into the 18-inch open mill to add vulcanization and produce sheets for later use;

[0027] (6) Lay the fabric and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A composite rubber racetrack is prepared from baypren, natural rubber, ethylene propylene rubber, the rubber powder made of used tyre, white carbon black, pottery clay, zinc oxide, stearic acid, naphthenic oil, dioctylester, flame retardant, ultraviolet absorbent and sulfurizing promoter through proportional mixing, adding sulfur, forming sheet, sticking the rubber liner made of regenerated rubber, sulfurizing, cutting for removing edges, grinding, examining and packing.

Description

1. Technical field [0001] The invention relates to a sports facility, in particular to a method for manufacturing a composite rubber track. 2. Technical Background [0002] The traditional runway is made of rubber particles and polyurethane cast on site. Its flatness, compactness, wear resistance and aging resistance are not good, and it is easy to discolor, degranulate, and accumulate dust. The polyurethane component is polluting to the environment. And toxic volatilization. At present, there are also composite runways, but the products are mainly made of natural rubber, supplemented by reinforcing fillers and other additives, the process is complicated, the cost is high, the product has high tensile strength, aging resistance, and poor resistance to sunlight cracking , easy to fade, shock absorption, wear resistance, impact absorption effects need to be improved. 3. Contents of the invention [0003] The purpose of the present invention is exactly to overcome the short...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29D31/00B29C35/02B29B7/00B29K19/00B29K7/00B29K21/00B29K507/04B29K509/02B29K505/00B29D99/00
Inventor 余绍火傅祥正
Owner 浙江绿环工程机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap