Mobile charge induced periodic poling and device

Abstract

Devices and methods are disclosed for realizing a high quality bulk domain grating structure utilizing mobile charges that are generated by means of photo-excitation in a substrate. An effect of light exposure (UV, visible, or a combination of wavelengths) is to generate photo-induced charges. The application of a voltage across the substrate combined with the application of light exposure causes a photo-induced current to flow through the substrate. The photo-induced charges (behaving like virtual electrode inside the material) and the photo-induced current result in both reduction of the coercive field required for domain inversion in the material and improve realization of the domain inversion pattern, which previously has not been possible at room temperature.

Description

BACKGROUND OF THE INVENTION[0001]1. Field of the Invention[0002]This invention relates generally to high quality short period bulk domain inversion structures (gratings), and more particularly to high quality short period bulk domain inversion structures (gratings) that are fabricated in substrate materials such as MgO doped congruent lithium niobate using electric field poling.[0003]2. Description of the Related Art[0004]Quasi phase matching (QPM) is an efficient way to achieve nonlinear optical interactions. The approach was first proposed by Bloembergen et al, U.S. Pat. No. 3,384,433, using a domain inversion grating structure to achieve QPM. Such a domain grating structure can be usefully realized in an optically transparent ferroelectric material, such as LiNbO3, LiTaO3, and KTP. There are many different ways to achieve inverted domain structures in these materials.[0005]A periodic poled material structure can be grown directly within the material by modifying a parameter durin...

AI Technical Summary

Benefits of technology

[0016]Accordingly, an object of the present invention is to provide a domain grating device, and its associated fabrication methods, that has controlled domain growth through the bulk of the crystal for uniform short period domain inversion gratings.

[0017]Another object of the present invention is to provide a domain grating device fabrication method, using the generation of mobile charges in a substrate to improve the seeding of inverted domains and to guide the growth of the domains through the bulk of the substrate for improved poling quality.

[0018]Another object of the present invention is to provide an improved domain grating device that results in high efficiency bulk domain grating devices for applications in generating high power visible laser light. This is achieved in a domain grating device that has a substrate with first and second opposing surfaces. The substrate has an inverted domain grating structure that extends through the entire substrate. An inverted domain duty cycle at the first surface is greater than 50% and less than 100%, and an inverted domain duty cycle at the second surface is less than 50% and greater than 0% ensuring a region of 50% duty cycle within the substrate.

Problems solved by technology

This method can produce gratings with periods as short as 6 μm and 4 μm, but it is difficult grow long lengths and curvature of the domains limits the lateral dimensions and efficiency.

Impurity doping or material removal in some ferroelectric materials (such as lithium niobate and KTP) can result in domain inversion.

Papuchon (U.S. Pat. No. 4,236,785) demonstrated patterned electric field inplane poling on lithium niobate to achieve waveguide quasi-phasematched nonlinear interactions Short period domain inversion in Z-cut congruent lithium niobate was first demonstrated by Yamada at Sony in 1992, U.S. Pat. No. 5,193,023 but the described process suffered from limitations in the material thickness and high instances of destructive electrical breakdown.

These localized trapped electrons in the material result in localized high electric field that causes domain inversion.

However the MgO dopant in MgO:CLN brings an even bigger challenge in realizing periodic domain structures.

However short-period-domain-grating structures have not been achieved at room temperature in a reliable and repeatable manner.

This current flow results in preferential growth of domains which are formed early in the poling process and disrupts the domain seeding uniformity and therefore the uniformity of the final grating pattern.

Since the inverted domain structure does not strictly follow the crystal structure, it is fundamentally challenging for the inverted domain to propagate through the entire thickness of the substrate while maintaining the lateral dimensions of the masking pattern applied on one surface of the substrate.