Anticracking waterproof agent

A technology of anti-cracking waterproofing agent and water-reducing agent, which is applied in the field of anti-cracking waterproofing agent, which can solve the problems of poor anti-cracking and anti-seepage effect, concrete cracks, and single function, so as to improve the anti-leakage function and compactness, and prevent cracks , The effect of improving durability

Inactive Publication Date: 2009-09-16
SHANDONG DAYUAN IND
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of these additives not only have a single function, but also have poor anti-crack and anti-seepage effects, and their slump is small, which makes it difficult to pump and construct, which easily causes cracks and leakage in the concrete.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anticracking waterproof agent
  • Anticracking waterproof agent
  • Anticracking waterproof agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The percentage by weight is 39% of anhydrous gypsum, 37% of aluminum ore powder, 7% of lime, 10% of FDN-A, 3% of magnesium stearate, 1.4% of calcium gluconate, 2.0% of sodium tripolyphosphate, migration type rust inhibitor 0.4% of cellulose, 0.03% of methyl cellulose, and 0.1% of triterpene saponin powder are mixed evenly in the sample mixing machine, and then transported to a ball mill by a belt conveyor to be ground into a powder of specified fineness, and then transported to a homogenization warehouse for homogenization. After melting, it is made into powdery anti-cracking and waterproofing agent.

Embodiment 2

[0026] The percentage by weight is 36% of anhydrite, 33% of aluminum ore powder, 10% of lime, 13% of FDN-A, 2% of magnesium stearate, 1.5% of calcium gluconate, 1.6% of sodium tripolyphosphate, migratory rust inhibitor 0.7%, 0.05% methyl cellulose, 0.2% triterpenoid saponin powder are mixed evenly in the mixing machine, and then transported to the ball mill through the belt conveyor to grind into a powder of specified fineness, and then transported to the homogenization warehouse for homogenization Finally, it is made into a powdered anti-cracking waterproofing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
slumpaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-cracking waterproofing agent, which is made of anhydrous gypsum, aluminum ore powder, lime, naphthalene-based water reducer, magnesium stearate, calcium gluconate, sodium tripolyphosphate, migratory rust inhibitor, formazan Prepared from base cellulose and triterpene saponin powder. The anti-cracking and waterproofing agent can greatly improve the workability and compactness of concrete, prevent concrete from cracking, greatly improve the anti-leakage and anti-rust functions of concrete, and meanwhile greatly improve the durability of concrete.

Description

technical field [0001] The invention relates to auxiliary materials for building materials, in particular to an anti-cracking and water-repellent agent used in concrete materials. Background technique [0002] With the development of the construction industry, the use of concrete, the main material in the construction industry, is gradually increasing, and people's requirements for concrete are getting higher and higher. Concrete is developing in the direction of high performance and high strength. Concrete water glue The ratio is getting smaller and smaller, while the amount of cementitious material and sand ratio are getting bigger and bigger. As a heterogeneous brittle material, concrete will expand with heat and contract with cold and shrink with moisture, especially when the water-cement ratio is low. This phenomenon is more obvious, and the factors that lead to concrete shrinkage increase. After the concrete is solidified, cracks are prone to occur, resulting in leakag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B22/14C04B22/06C04B22/04C04B24/20C04B24/04C04B22/16C04B103/65C04B103/30
Inventor 季元升亓良树毕春楷王立明冯乃谦刘立欣黄翠季永亮刘建辉季冠祥于钊勋季文忠杨升余
Owner SHANDONG DAYUAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products