Method for preparing Ni3Al-based single-crystal refractory alloy by employing combination of seed crystal method and screw selecting method

A high-temperature alloy and spiral crystal selector technology, which is applied in the direction of single crystal growth, single crystal growth, chemical instruments and methods, etc., can solve the problem of low success rate of single crystal

Inactive Publication Date: 2010-02-03
BEIHANG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the seed crystal method can effectively control the crystal orientation and solidification structure of single crystals, the success rate of single crystals is extremely low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing Ni3Al-based single-crystal refractory alloy by employing combination of seed crystal method and screw selecting method
  • Method for preparing Ni3Al-based single-crystal refractory alloy by employing combination of seed crystal method and screw selecting method
  • Method for preparing Ni3Al-based single-crystal refractory alloy by employing combination of seed crystal method and screw selecting method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0083] The steps to prepare Ni-14Mo-7.8Al single crystal superalloy material with orientation and excellent solidification structure are:

[0084] The first step is to prepare the seed crystal of Ni-14Mo-7.8Al single crystal superalloy;

[0085] see figure 1 As shown, a test block with orientation was oriented cut on the Ni-14Mo-7.8Al single crystal superalloy body, and the (001) surface of the test block was polished and surface-etched to obtain Ni-14Mo- 7.8Al single crystal superalloy seed crystal;

[0086] The (001) plane is the plane formed by four points A, B, C and D;

[0087] Polishing treatment conditions: Use 150#, 360#, 500#, 1000#, 2000# water-grinding sandpaper to polish the (001) surface of the test block, and then polish it on a polishing machine (Shanghai Precision Instrument Co., Ltd., PG-1A) deal with;

[0088] Surface corrosion treatment conditions: the polished test block is treated with an etchant for 5 minutes and then taken out to obtain the Ni-14Mo...

Embodiment 2

[0104] The steps to prepare Ni-13.5Mo-7.6Al-0.04B single crystal superalloy material with orientation and excellent solidification structure are:

[0105] The first step is to prepare the seed crystal of Ni-13.5Mo-7.6Al-0.04B single crystal superalloy;

[0106] see figure 2 As shown, a test block with orientation was directional cut on the Ni-13.5Mo-7.6Al-0.04B single crystal superalloy body, and the (011) surface of the test block was polished and surface-etched to obtain Ni-13.5Mo-7.6Al-0.04B single crystal superalloy seed crystal;

[0107] The (011) plane is the plane formed by four points A, B, C and D;

[0108] Polishing treatment conditions: Use 150#, 360#, 500#, 1000#, 2000# water-grinding sandpaper to polish the (011) surface of the test block, and then polish it on a polishing machine (Shanghai Precision Instrument Co., Ltd., PG-1A) deal with;

[0109] Surface corrosion treatment conditions: the polished test block is treated with an etchant for 2 minutes and t...

Embodiment 3

[0125] The steps to prepare Ni-14Mo-7.8Al-0.02B single crystal superalloy material with orientation and excellent solidification structure are:

[0126] The first step is to prepare the seed crystal of Ni-14Mo-7.8Al-0.02B single crystal superalloy;

[0127] see image 3 As shown, a test block with orientation was oriented cut on the Ni-14Mo-7.8Al-0.02B single crystal superalloy body, and the (111) surface of the test block was polished and surface-etched to obtain Ni -14Mo-7.8Al-0.02B single crystal superalloy seed crystal;

[0128] The (111) plane is the plane formed by four points A, B, C and D;

[0129] Polishing treatment conditions: Use 150#, 360#, 500#, 1000#, 2000# water abrasive paper to polish the (111) surface of the test block, and then polish it on a polishing machine (Shanghai Precision Instrument Co., Ltd., PG-1A) deal with;

[0130] Surface corrosion treatment conditions: the polished test block is treated with an etchant for 10 minutes and then taken out ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method of preparing a Ni<3>Al-based monocrystal high-temperature alloy through the crystallon method and the spiral crystal selection method, comprising: firstly a crystallonwhich is provided with a certain crystal orientation is cut directionally on the Ni<3>Al-based monocrystal high-temperature alloy; the crystallon is extended into one side of a wax pattern of a spiral crystal selector; the other side of the wax pattern of the spiral crystal selector is connected with a parts wax pattern; and ceramics castable refractory is smeared on the outside of the crystallon, the wax pattern of the spiral crystal selector and the parts wax pattern; then a ceramics shuttering provided with the crystallon is manufactured via dewaxing and burning; and the Ni<3>Al-based monocrystal high-temperature alloy material is teemed, shaped and manufactured by making use of the ceramics shuttering in a monocrystal furnace. The invention relates to a monocrystal preparation technology which can accurately control crystal orientation of the monocrystal and fine texture to manufacture the high quality Ni<3>Al-based monocrystal high-temperature alloy material.

Description

technical field [0001] The present invention relates to a kind of Ni 3 The preparation method of Al-based single crystal superalloy material, more specifically, refers to a method of preparing Ni by using a combination of seed crystal method and spiral crystal selection method 3 Al-based single crystal superalloy method. Background technique [0002] The high development of aerospace technology requires the engine to have a higher thrust-to-weight ratio and work efficiency, which requires the engine to have a higher operating temperature. At present, single crystal superalloys are the key materials for manufacturing advanced aeroengine turbine blades and guide vanes due to their high melting point, high temperature strength and excellent creep resistance. During the directional solidification process of single crystal superalloys, the growth direction shows an obvious preferred orientation, which often has a certain off-angle with the axial direction, which significantly r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B29/52C30B11/14C22C19/03B22C9/04B22D27/20
Inventor 李树索蒋立武韩雅芳武美伶
Owner BEIHANG UNIV