Solid solution aging technique for modifying Cu-Ag alloy rigidity and electric conductivity

A technology of solid solution aging and electrical conductivity, applied in the field of heat treatment of copper-based alloys, to achieve the effect of simple process and easy implementation

Active Publication Date: 2010-03-24
ZHEJIANG UNIV
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these heat treatment techniques are limited to homogenization annealing, intermediate heat treatment and final heat treatment, and their good effects must be reflected in the processing and deformation process, requiring the structure to be a complex multi-phase fiber composite form, which does not involve optimizing the original cast state. performance improvement techniques

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid solution aging technique for modifying Cu-Ag alloy rigidity and electric conductivity
  • Solid solution aging technique for modifying Cu-Ag alloy rigidity and electric conductivity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The metal Ag and electrolytic Cu are mixed according to the mass percentage, among which the metal Ag is 5%, and the rest is electrolytic Cu. First, Cu is placed in a vacuum induction furnace, melted at an atmospheric pressure lower than 0.1Pa, and left standing at 1150°C for degassing Then fill the furnace with Ar to 450kPa, then add Ag and melt it, electromagnetically stir it evenly and let it stand for 2-3 minutes, then cast it into a plate-shaped ingot of 16×42×170mm.

[0025] The ingot is solid solution treated by isothermal water cooling at 730°C / 8h+760°C / 4h.

[0026] The solution-treated ingots were aged at 350°C for 2 hours and subjected to isothermal air-cooling treatment.

[0027] After the above processing and heat treatment of the alloy, its Vickers hardness reaches 111, and the relative conductivity reaches 85% IACS change (see figure 1 and figure 2 ).

Embodiment 2

[0029] Metal Ag and electrolytic Cu are mixed according to mass percentage, wherein the metal Ag is 6%, and the rest is electrolytic Cu. The ingot smelting and casting process are the same as in Example 1.

[0030] The ingot is solution treated by isothermal water cooling at 730°C / 8h+760°C / 8h.

[0031] The solution-treated ingots were aged at 350°C for 24 hours and subjected to isothermal air-cooling treatment.

[0032] After the above processing and heat treatment, the Vickers hardness reaches 116, and the relative conductivity reaches 96% IACS (see figure 1 and figure 2 ).

Embodiment 3

[0034] Metal Ag and electrolytic Cu are mixed according to mass percentage, wherein the metal Ag is 6.5%, and the rest is electrolytic Cu. The ingot smelting and casting process are the same as in Example 1.

[0035] The ingot is solid solution treated by isothermal water cooling at 730°C / 8h+780°C / 4h.

[0036] The solution-treated ingots were aged at 450°C for 2 hours and subjected to isothermal air-cooling treatment.

[0037] After the above processing and heat treatment, the Vickers hardness reaches 130, and the relative conductivity reaches 90% (see figure 1 and figure 2 ).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a solid solution aging process whose cuprum-argent alloy hardness and conductivity are improved. Metal argent whose mass percentage is 5-7 percent and other burden which is electrolytic cuprum are melted in a vacuum induction furnace and are poured into ingots under the protection of argon gas, through the solid solution in 730 DEG C / 8 hours and in 760-780 DEG C / 4-8 hours and the aging of 350-450 DEG C / 2-24 hours, the Vickers hardness of cast alloy is capable of being reached to 110-130 DEG C, and the relative conductivity is reached to 85-96 percent of International Annealed Copper Standard. The invention increases the alloy hardness and relative conductivity of casting cuprum-5-7 percent of argent through the solid solution aging, the process is simple, the performance level is higher than cuprum-24 percent of argent, and the cost of raw materials is reduced.

Description

technical field [0001] The invention relates to a heat treatment technology of a copper-based alloy. In particular, it relates to a solid solution aging process for improving the performance of Cu-Ag alloy. Background technique [0002] Conductor alloys used in high-tech fields have extremely high requirements on strength, hardness and conductivity, but the hardness and conductivity of conductor alloys generally have an inverse function relationship, that is, if specific technologies are used to increase hardness, the conductivity is often sacrificed. The price, or the hardness is often lost in order to improve the conductivity. Therefore, it is very necessary to adopt a specific technology to obtain good hardness and electrical conductivity at the same time, so as to meet the performance of use. The fiber phase composite reinforced Cu-Ag alloy currently being developed shows excellent hardness and electrical conductivity, and is expected to become a preferred conductor ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/08
Inventor 孟亮姚大伟
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap