Radiation proof composite metallic yarn and weaving method thereof

A composite metal and anti-radiation technology, which is applied in the direction of yarn, textiles and paper making, can solve the problems of large wool fiber shrinkage, reduced radiation shielding effect, and uneven surface of fabrics, achieving strong cohesion and improving wide applicability , Good anti-static and anti-radiation effect

Inactive Publication Date: 2007-08-08
CHANGZHOU POLYACE TEXTILE & YARN
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anti-radiation composite wool is actually a kind of core-spun yarn. The fabric or clothing woven with the wool, because the wool completely covers the metal wires, the metal wires cannot be effectively contacted to form a current loop, thereby reducing the radiation protection. Shielding effect; In addition, during the dyeing and finishing process of this radiation-proof composite wool or the fabric or clothing woven with it, due to the large shrinkage rate of the wool fiber covered on the surface of the metal wire, the metal wire does not shrink, so that the metal wire The arch causes many knots and breaks, and the surface of the woven fabric is not smooth; moreover, this radiation-proof composite wool is a thick yarn, and fine-count yarns cannot be produced using this technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Select one spindle of stainless steel filament with a diameter of 15 μm, select one spindle with a specification of 120s single yarn, and twist the stainless steel filament and single yarn on a compound twisting machine, and control the twist tension at 15g±8g, and the twisting twist is s To 2200TPM, it is spun into antistatic composite metal yarn.

Embodiment 2

[0024] Select one spindle of stainless steel filament with a diameter of 80 μm, select one spindle with a specification of 7s single yarn, and twist the stainless steel filament and single yarn on a compound twisting machine, and control the twisting tension at 50g±8g, and the twisting degree is s To 100TPM, it is spun into antistatic composite metal yarn.

Embodiment 3

[0026] Select one spindle of stainless steel filament with a diameter of 50 μm, select one spindle with a specification of 80s single yarn, and twist the stainless steel filament and single yarn on a composite twisting machine, and control the twist tension at 35g±8g, and the twisting twist is s To 1000TPM, it is spun into antistatic composite metal yarn.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-radiation composite metal yarn comprising textile fiber bundle and metal filament. The diameter of metal filament is 15-80mum. The metal filament and the textile fiber bundle are doubled and twisted. The range of twist is 100-2200TPM. The textile fiber bundle is single yarn, plied yarn or long yarn. The invention also discloses the spinning process for anti-radiation composite metal yarn. At first, metal filaments with the diameter of 20-80mum and textile fiber bundle according with demands are selected and then selected metal filaments and textile fiber bundle are doubled and twisted on doubling and twisting machine. The tension of doubling and twisting is controlled in 15-80g and the twist of doubling and twisting is controlled in 100-2200TPM. Because metal filaments are used, the yarn and fabrics spun with the yarn are smooth. In fabric, longitude and latitude metal filaments are connected with each other in effect to form current loop. It can play a very good anti-radiation effect and improve the wide application of anti-radiation composite metal yarn.

Description

technical field [0001] The invention relates to a yarn and its spinning process, in particular to a metal yarn with radiation protection and its spinning process. technical background [0002] Various new industries characterized by automation and electronic control developed with the continuous updating of new electronic technologies have played a huge role in promoting my country's economic construction and technological progress. Electromagnetic radiation products are closely related to people's lives, such as ultra-high voltage power transmission and distribution and transmission and transformation of power systems; wireless broadcasting, mobile phones, microwave ovens, copiers, TVs, computers, wireless communications in signal transmission systems; high-frequency radiation in industrial applications Quenching, high-frequency smelting, plastic heat sealing, etc.; medical radio frequency equipment, ultrasonic medical equipment, and various household appliances, etc., all ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/12D02G3/28
Inventor 罗坚平
Owner CHANGZHOU POLYACE TEXTILE & YARN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com