Honeycomb ceramic preparing process

A technology of honeycomb ceramics and a manufacturing method, which is applied in the field of ceramic processing, can solve the problems of polluting the environment, loss of water and fertilizer, affecting plant growth, etc., and achieves the effects of improving the ecological environment, not easy to reverse moisture, and light in weight and heat insulation performance.

Inactive Publication Date: 2007-08-22
王汉明
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And this hole causes a large loss of water and fertilizer, which not only affects the growth of plants but also pollutes the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment one: make common pottery basin

[0020] Take pottery and sawdust according to the volume percentage of 50%:50%, put them in a mixer and stir, add water while stirring, the amount of water added is 100% of the total volume of pottery and sawdust, stir and mix, and then extrude from the extruder , to become a mixed pottery with good plasticity. Put the pottery in the pot mold to get the semi-finished product, and then dry it naturally into a white billet (about 22% water content) and put it into the dragon kiln for calcination. Calcined at 1200 ℃ for 50 Hours, out of the kiln to get finished products.

Embodiment 2

[0021] Embodiment 2: making garden rocks

[0022] Get the following raw materials according to their volume percentages: pottery 40%, 1-2cm foam plastic 10%, sawdust 10%, 30 mesh oil shale powder 40%, and mix them evenly with water while stirring in a mixer. The amount of water added is the total volume of raw materials 100%, and then extruded by an extruder to become a mixed pottery with good plasticity. The pottery is placed in a mold or shaped by hand, dried to a white billet (about 22% water content), and calcined in a dragon kiln. Calcined at a temperature of 1200°C for 50 hours, and the finished product was obtained from the kiln.

Embodiment 3

[0023] Example 3: Making Ceramic Heat Insulation Layer and Floor Tiles

[0024] Making ceramic heat-insulating layer bricks: take the following raw materials according to their volume percentages: 40% of pottery, 10% of sawdust, 40% of 50 mesh oil shale, 10% of 5000 cal coal powder, and the amount of water added is 70% of the total volume of raw materials;

[0025] Making floor tiles: take the following raw materials according to their volume percentages: 70% of pottery, 10% of coal powder, 20% of 60 mesh oil shale, and the amount of water added is 70% of the total volume of raw materials;

[0026] The production process of the above two products is the same as that of traditional ceramic tiles. That is the finished product.

[0027] Combustible particles of the present invention include any combustible particulate matter, such as charcoal, bamboo charcoal, coal, rice husk, bagasse, etc., and are not limited to the materials listed in the above examples. The volume percentag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to ceramic producing technology, is especially honeycomb ceramic preparing process, and aims at providing one kind of honeycomb ceramic with high air permeability and high water absorption. The honeycomb ceramic is prepared with ceramic mud 40-80 wt% and flammable grain 20-60 wt%, and through mixing while adding water in 50-150 wt%, forming, naturally to water content lower than 30 %, and calcining at 950-1800 deg.c for 2 hr to 5 days.

Description

technical field [0001] The invention relates to the technical field of ceramic processing, in particular to a method for manufacturing honeycomb ceramics. Background technique [0002] The processing and application of ceramics has a long history. Common ceramic products such as ceramic tiles and flower pots have a high density, so the ceramic tiles will appear damp. The flower pot should have a hole at the bottom for ventilation, otherwise the Plants will be starved of oxygen and will not grow well. And this hole causes a large loss of water and fertilizer, which not only affects plant growth but also pollutes the environment. Contents of the invention [0003] The object of the present invention is to provide a method for making honeycomb ceramics in order to make up for the shortcomings of the above-mentioned prior art, and the ceramics have good air permeability. [0004] In order to achieve the above object, the technical solution adopted by the present invention is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06C04B35/622
Inventor 王汉明
Owner 王汉明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com