A copper-clad aluminum complex cable copper strip composition and machining process

A processing technology and cable technology, applied in the direction of cable/conductor manufacturing, circuits, electrical components, etc., can solve the problems of high price and high cost of copper materials, and achieve saving copper resource consumption, low cost, and convenient transportation. Effect

Inactive Publication Date: 2007-10-24
LUOYANG COPPER PROCESSING GROUP
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the price of copper materials is still high, and it is still skyrocketing, resulting in unbearable high costs, causing many manufacturers to look for alternative products, so that low-cost copper-clad aluminum wires emerge as the times require

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The technical requirements for cable copper tape used for cable TV signal transmission and large-capacity communication network signal transmission are:

[0042] Copper strip specification: 0.36×305mm

[0043] State: soft state (M)

[0044] Performance requirements: 245MPa≤Rm≤265MPa, Rp0.2<100MPa, Al1.3≥40%

[0045] Tolerance requirements: thickness tolerance -0.010~+0.005mm, width tolerance ±0.20mm

[0046] Grain size: 0.010mm

[0047] Conductivity: ≥95%IACS

[0048] The processing technology is as follows:

[0049] Ingredients: 60.5% cathode copper and 39.5% red copper old materials are weighed and put into the smelting furnace for ingredients.

[0050] Melting: Melting is carried out in a cored power frequency induction furnace with a melting temperature of 1180°C.

[0051] Covering: After the ingredients are completely melted, charcoal is used to cover the liquid surface of the solution in the furnace, and the covering thickness is 100mm.

[0052] D...

Embodiment 2

[0071] The technical requirements for copper strips used for light vehicle cables, welding cables, and emergency mobile cables are:

[0072] Copper strip specification: 0.38×287mm

[0073] State: soft state (M)

[0074] Performance requirements: 245MPa≤Rm≤265MPa, Rp0.2<100MPa, Al1.3≥40%

[0075] Tolerance requirements: thickness tolerance -0.010~+0.005mm, width tolerance ±0.20mm

[0076] Grain size: 0.010mm

[0077] Conductivity: ≥95%IACS

[0078] The processing technology is as follows:

[0079] Ingredients: The ingredients are made of pure cathode copper and weighed separately and put into the smelting furnace.

[0080] Melting: use a cored power frequency induction furnace for melting, and the melting temperature is 1120°C.

[0081] Covering: After the ingredients are completely melted, graphite is used to cover the liquid surface of the solution in the furnace, and the covering thickness is 200mm.

[0082] Deoxidation: When preparing to transfer to the hol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The disclosed copper strip for Cu-covered-Al composite cable comprises: 59. 9705-99. 9805% cathode copper, <40% waste red copper, 0. 002-0. 012% P, <0. 002% O, and <0. 0155% other impurity. The preparation method comprises: mixing, smelting, covering, deoxidizing, revolving furnace, covering, holding, detecting, casting, sawing, ingotting and heating, hot-rolling, milling surface, coarse rolling, end shearing, intermediate annealing, fine rolling, product annealing, surface passivating, and packaging. This product has high conductivity, strength, extensibility, and welding feature. The tension processing ratio can come up to 99. 99%.

Description

technical field [0001] The invention belongs to the technical field of non-ferrous metal processing, and in particular relates to a copper strip component and a processing technology for copper-clad aluminum-clad cables. Background technique [0002] Cable TV signal transmission, large-capacity communication network signal transmission, control signal cables, light vehicle cables, welding cables, emergency mobile cables, TV excitation coils, ballast coils and deflection coils are all made of pure copper cores Cable. At present, the price of copper materials remains high and is still skyrocketing, resulting in unbearable high costs, causing many manufacturers to look for alternative products, so that low-cost copper-clad aluminum wires emerge as the times require. However, the outer layer of copper must ensure high conductivity, high strength, high elongation and good welding performance. At the same time, it is also required that when the subsequent wire drawing processing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/02H01B13/00C22C9/00B23P23/04
Inventor 秦光文娄花芬余学涛高双玲刘富良游金阁曹秀兰朱景明韩卫光李建涛王刚彦
Owner LUOYANG COPPER PROCESSING GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com