Hot-rolled fine-grained steel for electrostatic enamel and manufacturing method thereof

A technology of fine-grained steel and manufacturing methods, applied in metal rolling, manufacturing tools, metal rolling, etc., can solve the problems of scale explosion, poor adhesion, poor adhesion, scrapped enamel products, etc., and achieve enamel adhesion And the effect of good scale explosion resistance, easy process control and low production cost

Active Publication Date: 2007-10-31
BAOSHAN IRON & STEEL CO LTD
View PDF2 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is a method of dry powder enamel and then sintering, and its main defects are scale explosion and poor adhesion
But generally speaking, the bonding force between the porcelain powder and the steel plate, that is, the adhesion, is not as good as that of the wet enamel. In this way, the enamel peels off due to poor adhesion, resulting in the scrapping of the enamel products, and the loss will be very serious.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0044] See Tables 3 and 4 for examples of the invention.

[0045] Example

C

Si

mn

P

S

Al

Ti

N

1

0.055

0.100

0.70

0.011

0.02

0.039

0.06

0.010

2

0.100

0.030

1.00

0.020

0.03

0.010

0.07

0.005

3

0.045

0.017

0.40

0.011

0.04

0.042

0.08

0.003

4

0.041

0.017

0.45

0.015

0.05

0.04

0.10

0.005

5

0.040

0.016

0.48

0.009

0.02

0.034

0.03

0.003

6

0.050

0.023

0.60

0.012

0.03

0.049

0.07

0.005

7

0.053

0.030

0.50

0.050

0.04

0.100

0.08

0.005

8

0.035

0.100

0.40

0.011

0.030

0.039

0.10

0.010

9

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparing method of electrostatic enamel hot-roller fine-grained steel, which is characterized by the following: allocating mass percent as 0. 02-0. 10 carbon, not more than 0. 10 silicon, 0. 4-1. 0 manganese, not more than 0. 05 phosphor, 0. 02-0. 05 sulfur, 0. 01-0. 10 aluminum, 0. 003-0. 010 nitrogen, 0. 03-0. 10 titanium, surplus ferric and unavoidable impurity; setting the content of TiN at 0. 013-0. 044; setting ferrite tissue grain fineness number not less than 10 grade. This invention possesses good enamel adherence property and against squama knock property.

Description

technical field [0001] The present invention relates to hot-rolled fine grain steel for electrostatic enamel and its manufacturing method. Background technique [0002] When producing pressure-resistant containers such as water heater inner tanks, they were mainly manufactured by wet enamel processes in the past. In wet enamel, the adhesion between the enamel and the steel plate is relatively good, so the key point is to solve the scale resistance of the steel plate, because the enamel of wet enamel contains high crystal water, which is easy to generate hydrogen during the enamel process. Scales burst. There are many related patents for wet enamelled steel plates (see Table 1 and Table 2 for details). [0003] In these patents, in order to improve the scale explosion resistance of the steel plate, very high alloying elements (such as titanium and boron, etc.) are usually added to the steel to form sufficient compounds in the steel, which can effectively absorb the corrosio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/14B22D11/00B21B37/16B21B37/58B21B37/74C21D8/00C21D11/00
Inventor 孙全社
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products